Sistema MINUS® - técnica minimamente invasiva para o tratamento das fraturas transtrocanterianas do fêmur

The MINUS system was developed as a minimally invasive procedure that uses a diaphyseal cephalic extramedullary implant for the treatment of transtrochanteral fractures of the femur in elderly patients. The implant consists of a sliding screw coupled to a plate adapted to the minimally invasive technique. The surgical access is approximately three centimeters in length located on the lateral surface of the hip, below the projection of the small trochanter. A perfectly adapted instrument was used for the procedure, which also requires the use of an image intensifier, reducing surgery time and rate of bleeding. The objective of this study is to present a new instrument and implant, developed specifically for treatment with the minimally invasive technique, reducing the length of the conventional surgical access from 10 to three centimetres. This new implant was given the commercial name of MINUS System.

Estudo inicial da degradação in vivo de poli(L-co-D,L ácido lático), sintetizado em laboratório, aplicado como prótese tibial em coelhos

The copolymer poly (L-co-D,L lactic acid), PLDLA, has gained prominence in the field of temporary prostheses due to the fact that their time of degradation is quite compatible with the requirement in the case of osseous fracture. In this work the in vivo degradation of devices from copolymer, as a system of plates and screws, used in fixation of the tibia of rabbits was studied. The devices were implanted in 15 adult rabbits, albinos, New Zealand race, and they were used as control devices of alloys of titanium (Ti-6Al-4V/ V grade). The use of copolymers, synthesized in the laboratory, was tested in the repair of fracture in rabbits'tibias, being assessed in the following times: 2 weeks, 2 months and 3 months. Morphological analysis of tissue surrounding the plate and screw system, for 2 weeks of implantation, showed the presence of osteoblasts, indicating a pre bone formation. After 2 months there was new bone formation in the region in contact with the polymer. This bone growth occurred simultaneously with the process of PLDLA degradation, invading the region where there was polymer and after 3 months there was an intense degradation of the copolymer and hence greater tissue invasion compared to 2 months which characterized bone formation in a region where the polymer degraded. The in vivo degradation study of the devices for PLDLA by means of histological evaluations during the period of consolidation of the fracture showed the efficiency of plate and screw system, and it was possible to check formation of bone tissue at the implantation site, without the presence of inflammatory reaction

Indicações para ceratoplastia penetrante no Hospital das Clínicas-UNICAMP

PURPOSE: To determine the main causes of penetrating keratoplasty indications at Hospital das Clínicas-UNICAMP (January, 1999 to December, 2003). METHODS: A non-comparative, retrospective series of case studies. The authors reviewed the files of 857 patients who underwent penetrating keratoplasty at Hospital das Clínicas-UNICAMP between 1999-2003 and classified them into different categories according to diagnostic indication for surgery. RESULTS: The age range was between 0-88 years (average 44 years ±1.2). The main causes of penetrating keratoplasty were: keratoconus in 427 cases (49.82%); 152 cases (17.74%) of corneal ulceration (perforated or not); corneal graft failure in 87 cases (10.15%); bullous keratopathy, 72 cases (8.40%); Fuchs dystrophy in 59 cases (6.88%); trachoma complications in 28 cases (3.27%); other causes, 32 (3.74%). In children under 10 years of age, the main cause of penetrating keratoplasty indications was infectious ulcer (77.78%) and between 11-50 years of age, keratoconus was the main cause (71.65%). CONCLUSION: This study was composed of a young population, and the main causes of penetrating keratoplasty were keratoconus and therapeutic keratoplasty.