EFFECTS OF BUBBLE-FACILITATED VOC TRANSPORT FROM LNAPL SMEAR ZONES ON VAPOR INTRUSION

Light non-aqueous phase liquid (LNAPL) sources can pose a significant threat to indoor air through vapour intrusion (VI). Most conceptual and numerical models of VI assume that the transport of volatile organic compounds (VOCs) is a diffusion-limited process. Recently, alternate conditions have been identified that could lead to faster transport, including the presence of preferential pathways and methanogenic gas production. In this study, an additional mechanism that could lead to faster transport was investigated: bubble-facilitated VOC transport from LNAPL smear zones. A laboratory investigation was preformed using pentane in one-dimensional laboratory columns and two-dimensional visualization experiments. Results of the column experiments showed that average VOC mass fluxes in the bubble-facilitated columns were over two orders of magnitude greater than in the diffusion-limited columns. In addition, the flux signal was intermittent, consistent with expectations of bubble-facilitated transport as bubbles expand, mobilize and are released to the vadose zone at various times during the test. The results from the visualization experiments showed gas fingers growing and mobilizing over time, which supports the findings of the column experiments. In conclusion, these results demonstrate the potential for bubble-facilitated VOC transport to affect mass transfer in LNAPL smear zones, and lead to increased indoor air concentrations by VI.

FABRICATION, CHARACTERIZATION, AND IRRADIATION OF AN AUSTENITIC OXIDE DISPERSION STRENGTHENED STEEL SUITED FOR NEXT GENERATION NUCLEAR APPLICATIONS

As nuclear energy systems become more advanced, the materials encompassing them need to perform at higher temperatures for longer periods of time. In this Master’s thesis we experiment with an oxide dispersion strengthened (ODS) austenitic steel that has been recently developed. ODS materials have a small concentration of nano oxide particles dispersed in their matrix, and typically have higher strength and better extreme temperature creep resistance characteristics than ordinary steels. However, no ODS materials have ever been installed in a commercial power reactor to date. Being a newer research material, there are many unanswered phenomena that need to be addressed regarding the performance under irradiation. Furthermore, due to the ODS material traditionally needing to follow a powder metallurgy fabrication route, there are many processing parameters that need to be optimized before achieving a nuclear grade material specification. In this Master’s thesis we explore the development of a novel ODS processing technology conducted in Beijing, China, to produce solutionized bulk ODS samples with ~97% theoretical density. This is done using relatively low temperatures and ultra high pressure (UHP) equipment, to compact the mechanically alloyed (MA) steel powder into bulk samples without any thermal phase change influence or oxide precipitation. By having solutionized bulk ODS samples, transmission electron microscopy (TEM) observation of nano oxide precipitation within the steel material can be studied by applying post heat treatments. These types of samples will be very useful to the science and engineering community, to answer questions regarding material powder compacting, oxide synthesis, and performance. Subsequent analysis performed at Queen’s University included X-ray diffraction (XRD) and inductively coupled plasma optical emission spectrometry (ICP-OES). Additional TEM in-situ 1MeV Kr2+ irradiation experiments coupled with energy dispersive X-ray (EDX) techniques, were also performed on large (200nm+) non-stoichiometric oxides embedded within the austenite steel grains, in an attempt to quantify the elemental compositional changes during high temperature (520oC) heavy ion irradiation.