The control of radioactive backgrounds will be key in the search for neutrinoless double beta decay at the SNO+ experiment. Several aspects of the SNO+ back- grounds have been studied. The SNO+ tellurium purification process may require ultra low background ethanol as a reagent. A low background assay technique for ethanol was developed and used to identify a source of ethanol with measured 238U and 232Th concentrations below 2.8 10^-13 g/g and 10^-14 g/g respectively. It was also determined that at least 99:997% of the ethanol can be removed from the purified tellurium using forced air ow in order to reduce 14C contamination. In addition, a quality-control technique using an oxygen sensor was studied to monitor 222Rn contamination due to air leaking into the SNO+ scintillator during transport. The expected sensitivity of the technique is 0.1mBq/L or better depending on the oxygen sensor used. Finally, the dependence of SNO+ neutrinoless double beta decay sensitivity on internal background levels was studied using Monte Carlo simulation. The half-life limit to neutrinoless double beta decay of 130Te after 3 years of operation was found to be 4.8 1025 years under default conditions.

A Study of the Microwave Carbothermic Reduction of Chromite Ore

Microwave reduction testing using activated charcoal as a reducing agent was performed on a sample of Black Thor chromite ore from the Ring of Fire deposit in Northern Ontario. First, a thermodynamic model was constructed for the system. Activity coefficients for several species were found in the literature. The model predicted chromium grades of 61.60% and recoveries of 93.43% for a 15% carbon addition. Next, reduction testing on the chromite ore was performed. Tests were performed at increasing power levels and reduction times. Testing atmospheres used were air, argon, and vacuum. The reduced product had maximum grades of 72.89% and recoveries of 80.37%. These maximum values were obtained in the same test where an argon atmosphere was used, with a carbon addition of 15%, optimal power level of 1200 W (actual 1171 W), and a time of 400 seconds. During this test, 17.53% of the initial mass was lost as gas, a carbon grade of 1.95% was found for the sintered core product. Additional work is recommended to try and purify the sintered core product as well as reduce more of the initial sample. Changing reagent schemes or a two step reduction / separation process could be implemented.