Preparación y caracterización de la zeolita MCM-22 y de su precursor laminar

The layered precursor of MCM-22 was prepared with different Si/Al ratios: 15, 25, 50, 100 and ¥. Upon heat treatment these precursors form MCM-22 zeolite. Both layered precursor and MCM-22 zeolite were characterized by several techniques: Chemical Analysis by Atomic Absorption Spectroscopy (AAS), X-Ray Diffraction (XRD), Thermo-gravimetric Analysis (TGA), Pore Analysis by N2 and Ar adsorption, Scanning Electron Microscopy (SEM), Infrared Spectroscopy (IR) and Temperature Programmed Desorption of ammonium (TPD).

Efeito da adição de lantânio em catalisadores de Ni/ZrO2 aplicados na reação de reforma a vapor de etanol

The catalytic performance of Ni/ZrO2 catalysts loaded with different lanthanum content for steam reforming of ethanol was investigated. Catalysts were characterized by BET surface area, X-ray diffraction, UV-vis spectroscopy, temperature programmed reduction, and X-ray absorption fine structure techniques. Results showed that lanthanum addition led to an increase in the degree of reduction of both NiO and nickel surface species interacting with the support, due to the higher dispersion effect. The best catalytic performance at 450 ºC was found for the Ni/12LZ catalyst, which exhibited an effluent gaseous mixture with the highest H2 yield.

Caracterização de catalisadores Cu/CeO2/Al2O3 por redução a temperatura programada e atividade para oxidação de CO

The kinetic parameters for the CO oxidation reaction using copper/alumina-modified ceria as catalysts were determined. The catalysts with different concentrations of the metals were prepared using impregnation methods. In addition, the reduction-oxidation behaviour of the catalysts were investigated by temperature-programmed reduction. The activity results show that the mechanism for CO oxidation is bifunctional : oxygen is activated on the anionic vacancies of ceria surface, while carbon monoxide is adsorbed preferentially on the higher oxidation copper site. Therefore, the reaction occurs on the interfacial active centers. Temperatures-programmed Reduction patterns show a higher disperdion when cerium oxide is present.

Decomposição do NO sobre Cu suportado em zeólitas

Direct decomposition of NO on copper supported on zeolite catalysts such as MCM-22 and Beta was compared with that on the thoroughly studied Cu-ZSM-5. The catalysts were prepared by ion-exchange in basic media. They were characterized by atomic absorption, surface area, nitrogen adsorption at 77K, X-ray diffraction and temperature programmed reduction. The products of the reaction were analyzed by Fourier transform infrared spectroscopy using a gas cell. Catalytic activity tests indicated that zeolite catalysts, like Beta and MCM-22, lead to NO conversion values comparable to ZSM-5.

Efeito do teor metálico em catalisadores Co/Al2O3 aplicados à reação de reforma a vapor de etanol

The development of cobalt catalysts to produce hydrogen from ethanol is the goal of this investigation. Co/Al2O3 catalysts were prepared by impregnation and characterized by atomic absorption, nitrogen adsorption, X-ray diffraction, Raman spectroscopy, temperature programmed reduction and carbon analysis. The catalysts contained Co3O4 oxide and Co3+ and Co2+ species interacting with alumina. The cobalt load affects the crystal size and the crystalline structure and higher Co loads influence the reaction mechanism, changing the selectivity of the catalysts, decreasing the amount of CO produced and avoiding the formation of products catalyzed by the support. The ethanol conversion was 50-70% with 10-<1% of CO in the hydrogen.

Análise estatística e optimização de perfis de redução termoprogramada (TPR)

The effect of operational variables and their interaction in TPR profiles was studied using a fractional factorial experimental design. The heating rate and the reducing agent concentration were found to be the most important variables determining the resolution and sensitivity of the technique. They showed opposite effects. Therefore, they should be manipulated preferentially in order to obtain optimized TPR profiles. The effect of sample particle size was also investigated. The tests were carried out within a Cu/Zn/Al2O3 catalyst used for the water-gas shift reaction that presented two distinct species of Cu2+ in TPR profiles.

Produção de hidrogênio a partir da reforma a vapor de etanol utilizando catalisadores Cu/Ni/gama-Al2o3

Cu/Ni/gamma-Al2O3 catalysts were prepared by an impregnation method with 2.5 or 5% wt of copper and 5 or 15% wt of nickel and applied in ethanol steam reforming. The catalysts were characterized by atomic absorption spectrophotometry, X-ray diffraction, temperature programmed reduction with hydrogen and nitrogen adsorption. The samples showed low crystallinity, with the presence of CuO and NiO, both as crystallites and in dispersed phase, as well as of NiO-Al2O3. The catalytic tests carried out at 400 ºC, with a 3:1 water/ethanol molar ratio, indicated the 5Cu/5Ni/Al2O3 catalyst as the most active for hydrogen production, with a hydrogen yield of 77% and ethanol conversion of 98%.

Cinética de redução do catalisador CuO/ZnO/Al2O3

The reduction kinetics of a CuO/ZnO/Al2O3 catalyst by hydrogen was investigated isothermally and by temperature programmed reduction (TPR). Two reducible Cu2+ species were detected; the first one was identified as CuO bulk and the other as Cu2+ strongly interacting with alumina, possibly in the form of copper aluminate. The activation energies for the reduction of these two species were 60 and 90 kJ mol-1, respectively, and the reaction order with respect to hydrogen was one. The isothermal reduction data showed that the isotropic growth model is the most appropriate to describe the reaction rate data for both Cu2+ species.

Óxidos do tipo perovskita para reação de redução de no com CO

In this work, the perovskite-type oxides LaNiO3, LaMnO3, La0,7Sr0,3NiO3 and La0,7Sr0,3MnO3 were prepared by co-precipitation and tested in the NO reduction with CO at 400 and 500 ºC for 10 h. The catalysts were characterized by X-ray diffraction, temperature programmed reduction with hydrogen, nitrogen adsorption and chemical analysis. The nonstoichiometric oxygen was quantified by temperature programmed reduction, and the catalytic tests showed that the La0,7Sr0,3MnO3 catalyst presented the higher performance for the reduction reaction of NO with CO. The partial substitution of lanthanum by strontium increased the NO conversion and the N2 yield.

Remoção de compostos orgânicos em água empregando carvão ativado impregnado com óxido de ferro: ação combinada de adsorção e oxidação em presença de H2O2

In this work, composites based on activated carbon/iron oxide (AC/Fe) were prepared in two different proportions (AC/Fe 5/1 and 1/1) and evaluated in the removal of the organic dye methylene blue (MB). Physical-chemical properties of the composites were determined by X-ray diffraction (XRD), adsorption/dessorption of N2 isotherm, temperature programmed reduction (TPR) and scanning electron microscopy (SEM). Results showed that goethite (α- FeOOH), with nanometer particle size, was formed over carbon surface for both composites. These materials showed high efficiency to remove MB from solution by combined adsorption and oxidation process. The AC/Fe 1/1 showed to be more active in (MB) oxidation then AC/Fe 5/1.

Síntese e caracterização de nanopartículas de óxido de ferro suportadas em matriz carbonácea: remoção do corante orgânico azul de metileno em água

In this work were prepared composites of iron oxide and carbonaceous materials in two different weight proportions (Carbon/Fe 1/1 and 1/2). The physico-chemical properties of the composites were determined by temperature programmed reduction (TPR), adsorption/dessorption of N2, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and pulse titration H2. The XRD and XPS analysis showed a cubic iron oxide phase, identified as maghemite, formed over the carbon surface. The particle size of maghemite showed to be within 10-30 nm. Carbon/Fe 1/2 was the most active in MB removal kinetics and ESI-MS studies showed that MB removal by both composites leads to oxidized intermediates.

Sistema RTP: uma técnica poderosa para o monitoramento da formação de nanotubos de carbono durante o processo por deposição de vapor químico

In this work, a TPR (Temperature Programmed Reduction) system is used as a powerful tool to monitor carbon nanotubes production during CVD (Chemical Vapour Deposition), The experiments were carried out using catalyst precursors based on Fe-Mo supported on Al2O3 and methane as carbon source. As methane reacts on the Fe metal surface, carbon is deposited and H2 is produced. TPR is very sensitive to the presence of H2 and affords information on the temperature where catalyst is active to form different forms of carbon, the reaction kinetics, the catalyst deactivation and carbon yields.

Palladium-supported catalysts in methane combustion: comparison of alumina and zirconia supports

Palladium catalysts supported on alumina and zirconia were prepared by the impregnation method and calcined at 600 and 1000 ºC. Catalysts were characterized by BET measurements, XRD, XPS, O2-TPD and tested in methane combustion through temperature programmed surface reaction. Alumina supported catalysts were slightly more active than zirconia supported catalysts, but after initial heat treatment at 1000 ºC, zirconia supported palladium catalyst showed better performance above 500 ºC A pattern between temperature interval stability of PdOx species and activity was observed, where better PdOx stability was associated with more active catalysts.

Estudo da oxidação parcial do etanol em catalisadores de Rh por DRIFTS

The partial oxidation of ethanol on γ-Al2O3, CeO2, ZrO2 and Ce xZr1-xO2 supported rhodium catalysts was investigated by Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS). The catalysts were characterized by temperature-programmed reduction (TPR) and cyclohexane dehydrogenation. DRIFTS studies on the partial oxidation of ethanol showed that ethanol is adsorbed dissociatively, through O-H bond breaking, with the formation of ethoxy species, followed by successive dehydrogenation to acetaldehyde and acetyl species. Further oxidation to acetate and carbonate species lead to the formation of CO, CH4 and H2 by decomposition. The presence of CeO2 in the catalysts favored the oxidation steps due to its oxygen storage capacity.

Estudo de catalisadores de níquel suportados em cinza de casca de arroz na reforma de metano com dióxido de carbono visando a produção de hidrogênio e gás de síntese

Rice husk ash (RHA) is used as a silica source for several purposes, among them to obtain metal catalysts, as was done in this work. The catalysts were characterized by chemisorption, physisorption, thermal analyses (TG, DSC), X-ray diffraction, X-ray fluorescence, temperature-programmed reduction and scanning electron microscopy. The catalysts synthesized with different Ni loadings supported on RHA were applied to the reaction of dry reforming of methane. The reaction was tested at three temperatures of catalytic reduction (500, 600 and 700 ºC). All synthesized catalysts were active for the studied reaction, with different H2/CO ratios achieved according to degree of metallic dispersion.