Oxochloroalkoxide of the Cerium (IV) and Titanium (IV) as oxides precursor

The Cerium (IV) and Titanium (IV) oxides mixture (CeO2-3TiO2) was prepared by thermal treatment of the oxochloroisopropoxide of Cerium (IV) and Titanium (IV). The chemical route utilizing the Cerium (III) chloride alcoholic complex and Titanium (IV) isopropoxide is presented. The compound Ce5Ti15Cl16O30 (iOPr)4(OH-Et)15 was characterized by elemental analysis, FTIR and TG/DTG. The X-ray diffraction patterns of the oxides resulting from the thermal decomposition of the precursor at 1000 °C for 36 h indicated the formation of cubic cerianite (a = 5.417Å) and tetragonal rutile (a = 4.592Å) and (c = 2.962 Å), with apparent crystallite sizes around 38 and 55nm, respectively.

Synthesis and characterization of Fe(III)-doped ceramic membranes of titanium dioxide and its application in photoelectrocatalysis of a textile dye

Pure and Fe(III)-doped TiO2 suspensions were prepared by the sol gel method with the use of titanium isopropoxide (Ti(OPri)4) as precursor material. The properties of doped materials were compared to TiO2 properties based on the characterization by thermal analysis (TG-DTA and DSC), X-ray powder diffractometry and spectroscopy measurements (FTIR). Both undoped and doped TiO2 suspensions were used to coat metallic substrate as a mean to make thin-film electrodes. Thermal treatment of the precursors at 400ºC for 2 h in air resulted in the formation of nanocrystalline anatase TiO2. The thin-film electrodes were tested with respect to their photocatalytic performance for degradation of a textile dye in aqueous solution. The plain TiO2 remains as the best catalyst at the conditions used in this report.

Air blast freezing of fruit pulp models in commercial boxes: influence of preferential channels in the bed on freezing times estimating

The freezing times of fruit pulp models packed and conditioned in multi-layered boxes were evaluated under conditions similar to those employed commercially. Estimating the freezing time is a difficult practice due to the presence of significant voids in the boxes, whose influence may be analyzed by means of various methods. In this study, a procedure for estimating freezing time by using the models described in the literature was compared with experimental measurements by collecting time/temperature data. The following results show that the airflow through packages is a significant parameter for freezing time estimation. When the presence of preferential channels was considered, the predicted freezing time in the models could be 10% lower than the experimental values, depending on the method. The isotherms traced as a function of the location of the samples inside the boxes showed the displacement of the thermal center in relation to the geometric center of the product.

PEASANT AND SCIENTIFIC KNOWLEDGE ON PLANOSOLS AS A SOURCE OF MATERIALS IN THE MAKING OF NON-INDUSTRIAL POTTERY

Ethnopedological studies have mainly focused on agricultural land uses and associated practices. Nevertheless, peasant and indigenous populations use soil and land resources for a number of additional purposes, including pottery. In the present study, we describe and analyze folk knowledge related to the use of soils in non-industrial pottery making by peasant potters, in the municipality of Altinho, Pernambuco State, semiarid region at Brazil. Ethnoscientific techniques were used to record local knowledge, with an emphasis on describing the soil materials recognized by the potters, the properties they used to identify those soil materials, and the criteria employed by them to differentiate and relate such materials. The potters recognized three categories of soil materials: “terra” (earth), “barro” (clay) and, “piçarro” (soft rock). The multi-layered arrangement of these materials within the soil profiles was similar to the arrangement of the soil horizon described by formal pedologists. “Barro vermelho” (red clay) was considered by potters as the principal ceramic resource. The potters followed morphological and utilitarian criteria in distinguishing the different soil materials. Soils from all of these sites were sodium-affected Alfisols and correspond to Typic Albaqualf and Typic Natraqualf in the Soil Taxonomy (Soil Survey Staff, 2010).

Introdução às técnicas de reflexão especular e de reflexão-absorção no infravermelho: (2) reflexão-absorção

This paper is the second part of an article aimed to present theoretical basis as well as some applications of two infrared reflection techniques: specular reflection and reflection-absorption. It is emphasyzed how much spectral simulation can aid spectral analysis. The usefulness of reflection-absorption spectroscopy as a thin film caracterization technique is stressed. Optical effects such as LO-TO splittings and their observation as Berreman effect are also addressed.

Filmes de titânio-silício preparados por "spin" e "dip-coating"

The conditions for the preparation of luminescent materials, consisting of Eu3+ ions entrapped in a titanium matrix, in the forma of a thin film, using the sol-gel process, are described. The films were obtained from sols prepared with TEOS and TEOT, in the presence of acetylacetone as the hidrolysis-retarding agent, using the dip-coating and spin-coating techniques. The influence of these techniques on the films based on titanium and silicon are presented. The Eu3+ was used as a luminescent probe. The films have been characterized by luminescence, reflection and transmittance. The thickness of the films could be related to the preparation procedure. Transparent thin films have been prepared by dip-coating technique.

Filmes delgados luminescentes obtidos a partir de hidroxicarbonatos de ítrio ativados por európio ou térbio

These films were obtained by dip coating. Parameters like dislocation velocity; number of deposits, suspension concentration, and number of deposits followed or not by heat treatment between each deposit and calcination temperature were evaluated for establishing the best homogeneity. The obtained films were characterized in terms of their morphology, optical quality and photoluminescence by scanning electron microscopy (SEM), UV-vis absorption spectrophotometry and luminescence spectroscopy, respectively. The morphologic and luminescent characteristics showed dip coating as good laboratory technique for development of thin films for optical applications.

Estabilização de solo contaminado com zinco usando zeólitas sintetizadas a partir de cinzas de carvão

The effect of synthetic zeolites on stabilizing Zn-contaminated soil using 0.01 mol L-1 CaCl2 leaching solution in batch experiments was investigated. The zeolites were synthesized from coal ash by hydrothermal treatment with alkaline solution. The additive enhanced the sorption capacity of the soil and reduced leaching. Zinc leaching was reduced by more than 80% using a minimum of 10% additive. The higher cation exchange capacity of the zeolite/soil mixtures and higher pH were responsible for stabilizing Zn in soil. The poly(2-aminobenzenesulfonic acid)-coated mercury thin-film electrode was used for the determination of zinc.

Remoção dos hormônios 17β-estradiol e 17α-etinilestradiol de soluções aquosas empregando turfa decomposta como material adsorvente

This paper describes the adsorption of 17β-estradiol (E2) and 17α-ethinylestradiol (EE2) from aqueous solution by decomposed peat. The peat presented a good adsorption process, close to 76.2% for E2 removal and approximately 55.0% for EE2. Moreover, the results indicated a probable multi-layered process. Adsorption isotherms were well fitted by Freundlich model. The data were evaluated considering the pseudo-first-order and pseudo-second-order approaches, being the second more significant mechanism in the rate-controlling step. Thermodynamic data revealed that hormones adsorption onto peat is spontaneous under the employed experimental conditions. The results confirmed the potential of this adsorbent to be employed for effluents treatment.

Labile copper and zinc fractions under different salinity conditions in a shipyard area in the patos lagoon estuary, south of Brazil

Copper and zinc are common elements in paint residues and can be toxic to estuarine organisms. This study aims to determine the labile dissolved and labile particulate fractions (LPFs) of copper and zinc in the estuarine waters of a shipyard in southern Brazil under different salinity levels and in different seasons. The labile dissolved fraction was determined using the diffusive gradient in thin-film (DGT) technique. The variations in DGT-Cu (0.22-1.05 µg L-1), DGT-Zn (0.54-18.39 µg L-1), LPF-Cu (1.22-3.77 µg g-1), and LPF-Zn (4.29-19.12 µg g-1) concentration were related to changes in their physico-chemical parameters and as a result of boat maintenance activities.

Desenvolvimento de reator tipo "dip catalyst" para filmes poliméricos contendo nanopartículas de metais de transição

This article describes the development of a new catalytic reactor designed to operate with nanoparticle-embedded polymer thin films. Stabilization of metal nanoparticles in films that serve as catalysts in organic reactions is relatively new; therefore, the development of reactors to facilitate their use is necessary. We describe in detail the preparation of the GDCR reactor-type "dip catalyst" and its evaluation in the Suzuki - Miyaura cross-coupling reaction of phenylboronic acid and 4-bromoanisole catalyzed by palladium nanoparticle-embedded cellulose acetate thin film (CA/PD(0)). Compared with earlier prototypes, GDCR reactor showed excellent results when operating with CA/PD(0) thin films.

DISPOSITIVOS DGT MODIFICADOS COM MATERIAIS ALTERNATIVOS PARA USO NA ESPECIAÇÃO DE ELEMENTOS TRAÇO

The use of MT-K10 Montmorillonite immobilized onto agarose was investigated in this work as an alternative binding phase in Diffusive Gradient in Thin Film (DGT) devices for the determination of metallic labile species. In addition, agarose itself was also used as the diffusive phase. The percentage of sorption of Zn2+, Cu2+, Cr3+, Mn2+, Cd2+, Pb2+, and Ni2+ onto the binding phase was higher than 80% and the desorption process for all elements was also greater than 75%. Elution factors were determined experimentally, ranging from 0.74 for Zn2+ and 0.90 for Cr3+ and Pb2+. The accumulation of all species was linear with time, in agreement with the Fick's 1st law of diffusion. The deployment of the alternative devices in natural waters was compared to commercial devices. Labile concentrations determined by the alternative devices were slightly superior compared to results obtained with the deployment of original DGT devices due to the less restrictive pores of agarose.

Effects of condensation in microchannels with a porous boundary: analytical investigation on heat transfer and meniscus shape

In two-phase miniature and microchannel flows, the meniscus shape must be considered due to effects that are affected by condensation and/or evaporation and coupled with the transport phenomena in the thin film on the microchannel wall, when capillary forces drive the working fluid. This investigation presents an analytical model for microchannel condensers with a porous boundary, where capillary forces pump the fluid. Methanol was selected as the working fluid. Very low liquid Reynolds numbers were obtained (Re~6), but very high Nusselt numbers (Nu~150) could be found due to the channel size (1.5 mm) and the presence of the porous boundary. The meniscus calculation provided consistent results for the vapor interface temperature and pressure, as well as the meniscus curvature. The obtained results show that microchannel condensers with a porous boundary can be used for heat dissipation with reduced heat transfer area and very high heat dissipation capabilities.