Inertization of small-scale chemical wastes using iron phosphate glass

The viability of small-scale heavy-metal waste immobilization into iron phosphate glasses was investigated. Several waste forms containing different amounts of heavy-ion wastes were evaluated (5%, 10%, 15%, 20%, 26%, 33%, 40% and 50% by mass) and their X-ray diffraction patterns revealed that no crystallization occurred in glasses with waste concentrations up to 26%. The dissolution rates for all of the reported glass compositions (ca. 10-8 g cm-2 min-1) are similar to those reported for the materials most commonly used for waste vitrification. Iron phosphate glasses thus proved to be very useful for the immobilization of heavy-metal wastes, exhibiting good contention and chemical durability comparable to that of borosilicate glasses.

Efeito da adição de serragem de couro tratada quimicamente nas propriedades do cimento Portland

The sheave leather was subjected to chemical treatment in an attempt to immobilize chromium ion in a matrix of cement. Cementitious pastes were obtained by adding different proportions of waste treated solutions (5 and 10% compared to the cement mass) and the pH and setting time (hardening) were measured. Aiming to check the leather influence in Portland cement pastes, the phases formation were observed by X-ray diffraction (XRD). The results showed that the pretreatment was effective for the waste dissolution and the pH of treated waste chemical solutions did not influence significantly the characteristics of cement paste, with a slight increase in setting time results.