Resistência química de vitro-cerâmicos pertencentes a sistemas Li2O-ZrO2-BaO-SiO2 frente ao tratamento com soluções ácidas e básicas

The chemical durability of the Li2O-ZrO2-BaO-SiO2 system was examined by determination of the Vickers hardness. The dependence of hardness and of the chemical resistance with BaO addition was investigated. The experimental results indicate that the hardness increases with the BaO content. The samples surface's morphology submitted to the chemical treatment in acidic (H2SO4) and basic (KOH) solution was accompanied by scanning electron microscopy. The chemical durability of the materials with BaO showed better than the glass ceramic without this content. These materials treated with H2SO4 solution showed a preferential attack to the silica rich sites.

Caracterização de cimento odontológico obtido a partir de um vidro preparado pelo método dos precursores poliméricos

Glass ionomer cements are glass and polymer composite materials. These materials currently find use in dentistry. The purpose of this work is to obtain glass powders based on the composition 4.5SiO2 - 3Al2O3 - 2CaO to be used in dentistry. The powders were prepared by a chemical route at 700 0C. The properties of glass ionomer cements obtained from powders prepared at 700 ºC were studied. Diametral tensile strength and microhardness were evaluated for the experimental glass ionomer cements and a commercial material. It was concluded that the properties of experimental cements were similar to those of the commercial ones.