Investigação de Er3+ nos dois sítios cristalográficos de Gd2SiO5 através da fotoluminescência resolvida no tempo

Gadolinium oxyortho-silicate, Gd2SiO5, presents a monoclinic structure with two crystallographic sites in which Gd3+ ions are equally distributed with coordination numbers CN, 7 and 9, respectively. By doping this host with Er3+ it is possible to distinguish and attribute the two sites by means of lifetime determination of the 4S3/2 state, (in this case, Er3+ substitutes Gd3+ ions). Samples doped with 0.1 and 5.0% molar Er3+ were prepared by solid state reaction and characterized by X-ray Diffractometry, Vibrational and Electronic Absorption Spectroscopies, and Time Resolved Photoluminescence. Based on the experimental results, it is possible to verify that, for the 5,0% doped sample, the lifetime value of the 4S3/2 state of the erbium ion inserted in site 1, (CN = 9), is 2.7 ± 0.1 mus, and for the one inserted in site 2, (CN = 7), it is 1.5 ± 0.1 mus.

Óxidos de ferro e monazita de areias de praias do Espírito Santo

Sand samples collected from two sampling sites on Guarapari and Iriri beaches, state of Espírito Santo, Brazil, were studied in an attempt to better describe their chemical and mineralogical compositions and radioactive behaviors. The sands were found to contain about 6 (Guarapari) and 2 dag kg-1 (Iriri) of rare earth and thorium that, if allocated to the monazite-(Ce) structure, lead to the averaged formulae Ce3+0,494Gd3+0,012La3+0,209Nd3+0,177Pr3+0,040Sm3+0,024Th4+0,033 (PO4) and Ce3+0,474La3+0,227Nd3+0,190Pr3+0,044Sm3+0,032Th4+0,024 (PO4). From Mössbauer spectroscopy data, the magnetic fractions of these sands were found to contain stoichiometric hematite (47.4 dag kg-1, from Guarapari, and 25.1 dag kg-1, from Iriri) and magnetite (44.1 and 58.8 dag kg-1). The specific alpha and beta radiation activities were also measured for both samples.

Estudo da decomposição térmica de oxalato de estrôncio dopado com cério(III) como precursor de materiais luminescentes

Este trabalho trata da obtenção de SrC2O4, Ce2(C2O4)3, e SrC2O4 dopado com diferentes porcentagens de Ce3+ como precursores do luminóforo azul Sr2CeO4. Os precursores preparados foram estudados por TG e DTA. Uma mistura contendo SrC2O4 e Ce2(C2O4)3 na relação 4:1 respectivamente e SrC2O4 dopado com diferentes porcentagens de Ce3+, foram tratadas termicamente à 1100ºC, 12 horas. Os produtos foram analisados por XRD e espectroscopia de luminescência e apresentam mistura das fases SrCeO3, Sr2CeO4 e SrCO3. Os produtos contendo a fase Sr2CeO4 apresentam luminescência azul de banda larga, com exceção daquele obtido a partir de SrC2O4 dopado com 50% de Ce3+. Neste caso a fase predominante é SrCeO3. Pela curva DTA observa-se um pico endotérmico em torno de 1000ºC para todas as amostras, com exceção da amostra dopada em 50%, evidenciando a temperatura de formação da fase Sr2CeO4. A fase luminescente Sr2CeO4 é preferencialmente obtida partindo-se de SrC2O4:Ce3+ 25% e de misturas mecânicas na proporção de 4:1 de oxalatos de estrôncio e de oxalato de cério.