Influence of the use of acids and films in post-harvest lychee conservation

Lychee (Litchi chinensis Sonn.) has a high commercial value; however, it has a short shelf-life because of its rapid pericarp browning. The objective of this study was to evaluate the shelf-life of 'Bengal' lychee fruits stored after treatment with hydrochloric acid and citric acid, associated with cassava starch and plastic packaging. Uniformly red pericarp fruits were submitted to treatments: 1-(immersion in citric acid 100 mM for 5 minutes + cassava starch 30 g L-1 for 5 minutes), 2-(immersion in hydrochloric acid 1 M for 2 minutes + starch cassava 30 g L-1 for 5 minutes), 3-(immersion in citric acid 100 mM for 5 minutes + polyvinyl chloride film (PVC, 14 µm thick)) and 4-(immersion in hydrochloric acid 1 M for 2 minutes + PVC film). During 20 days, the fruits were evaluated for mass loss, pericarp color, pH, soluble solids and titratable acidity, vitamin C of the pulp and pericarp and activities of polyphenol oxidase and peroxidase of the pericarp. The treatment with hydrochloric acid associated with PVC was the most effective in maintaining the red color of the pericarp for a period of 20 days and best preservation of the fruit. The cassava starch associated with citric acid, and hydrochloric acid did not reduce the mass loss and did not prevent the browning of lychee fruit pericarp.

Replacement of HIV p24 Ag test by a multiplex RT-PCR method for primary screening of blood donors

Nucleic Acid Testing (NAT) as a tool for primary screening of blood donors became a reality in the end of the 1990 decade. We report here the development of an "in-house" RT-PCR method that allows the simultaneous (multiplex) detection of HCV and HIV-RNA in addition to an artificial RNA employed as an external control. This method detects all HIV group M subtypes, plus group N and O, with a detection threshold of 500 IU/mL. After validation, the method replaced p24 Ag testing, in use for blood donation screening since 1996 at our services. From July 2001 to February 2006, 102,469 donations were tested and 41 (0.04%) were found HIV-RNA reactive. One NAT-only reactive donation (antibody non-reactive) was observed, with subsequent seroconversion of the implied donor, giving a yield of 1:102,469. This rate is in contrast to the international experience that reports a detection of approximately 1:600,000 - 1:3,100,000 of isolated HIV-RNA donations.

FALSE-NEGATIVE DENGUE CASES IN RORAIMA, BRAZIL: AN APPROACH REGARDING THE HIGH NUMBER OF NEGATIVE RESULTS BY NS1 AG KITS

Serum samples from 150 NS1-negative (Platelia ELISA) patients presumptively diagnosed with dengue were analyzed by the TaqMan probed real-time reverse transcription PCR (TaqMan qRT-PCR) method. The qRT-PCR positive samples were tested for serotype by semi-nested RT-PCR and a qualitative immunochromatographic assay for IgG and IgM. Molecular detection methods showed 33 (22%) positive samples out of 150 NS1-antigen negative samples. Of these, 72% were collected up to day 2 after the onset of symptoms, when diagnostic sensitivity of NS1-antigen test assays is significantly enhanced. Most of the cases were not characterized as secondary infection. Twenty-eight samples were successfully serotyped, 75% of which for DENV-4, 14% for DENV-2, 7% for DENV-3 and 4% for DENV-1. These findings reaffirm the hyperendemic situation of the state of Roraima and suggest a lower sensitivity of the NS1 test, mainly when DENV-4 is the predominant serotype. Health care providers should therefore be aware of samples tested negative by NS1 antigen assays, especially when clinical symptoms and other laboratory data results show evidence of dengue infection.

Nota sobre antígeno relacionado à hepatite (HB Ag) e anticorpo (HB Ab) em população do território Federal do Amapá

53 amostras de soro, provenientes de Ferreira Gomes, no Amapá, foram testados para antígeno HB Ag e anticorpo HB Ab, com uma positividade de 3,7% para HB Ag, sub-tipo D. Os autores acentuam a necessidade de inquéritos em populações brasileiras a fim de estabelecer os sub-tipos associados à hepatite.

Procedimentos para recuperação de Ag de resíduos líquidos e sólidos

A simple procedure for recovering Ag, generated as residual solutions, from three different analytical methods, is presented. Based on the rate of the total Ag mass recovered, to the initial one in the initial residual solutions, efficiency as high as 97,9 ± 2,9% was obtained in the process. The purity of Ag, as Ag2O, was verified by employing this reagent in the determination of S in plant tissue. This leads to the generation of a solid metallic Ag as waste. In this situation, an 88,7 ± 0,6% Ag recovery was acquired, when a HNO3 solution was employed as solvent.

Use of thin films obtained by plasma polymerization for grain protection and germination enhancement

In this work, preliminary results of the use of hydrophobic thin films obtained by plasma deposition to protect grains and seeds are presented: grains coated by the films did not present biological degradation when stored in a saturated water vapor environment, but had their germination accelerated in the presence of water. A model that explains the difference of behavior of the films when exposed to water in vapor form or in liquid form, based on the formation of microchannels within the film that lead to water uptake in seeds, is presented. The model was successfully tested using quartz crystal measurements, which showed that the microchannels within the films can favor the adsorption and permeation of water when the films are immersed in water.

Plasma polymerized acetaldehyde thin films for retention of volatile organic compounds

The aim of this work is the production and characterization of plasma polymerized acetaldehyde thin films. These films show highly polar species, are hydrophilic, organophilic and easily adsorb organic reactants with CO radicals but only allow permeation of reactants with OH radicals. The good step coverage of films deposited on aluminum trenches is useful for sensor development. Films deposited on hydrophobic substrates may result in a discontinued layer, which allows the use of preconcentration in sample pretreatment. Deposition on microchannels showed the possibility of chromatographic columns and/or retention system production to selectively detect or remove organic compounds from gas flows.

Planejamento fatorial e superfície de resposta: otimização de um método voltamétrico para a determinação de ag(i) empregando um eletrodo de pasta de nanotubos de carbono

A factorial design applied in a voltammetric stripping method for the measurement of Ag(I) in natural water is described. The procedure is based on the effective pre-concentration of silver ions on electrode surface. The calibration graph was linear in the silver concentration range from 7.92 x 10"7 to 1.07 x 10"5 mol L"1 with a detection limit of 3.81 x 10-7 mol L-1. The determination of Ag(I) in natural water samples was carried out satisfactory with the proposed electrode.

Citric acid as multifunctional agent in blowing films of starch/PBAT

Citric acid was used as a compatibilizer in the production of starch and PBAT films plasticized with glycerol and processed by blow extrusion. Films produced were characterized by WVP, mechanical properties, FT-IR-ATR and SEM. WPV ranged from 3.71 to 12.73×10-11 g m-1 s-1 Pa-1, while tensile strength and elongation at break ranged from 1.81 to 7.15 MPa and from 8.61 to 23.63%, respectively. Increasing the citric acid concentration improved WVP and slightly decreased film resistance and elongation. The films micrographs revealed a more homogeneous material with the addition of citric acid. However, the infrared spectra revealed little about cross-linking esterification reaction

Enhanced photocatalytic activity of TiO2 films by modification with polyethylene glycol

Titanium dioxide porous thin films on the Anatase phase were deposited onto glass slides by the sol-gel method assisted with polyethylene glycol (PEG). The dip-coated films were characterized using scanning electron microscopy (SEM), thermogravimetric analysis (TGA and DTG), UV-visible spectroscopy and X-ray diffraction (XRD). The photocatalytic activity of the films was determined by means of methyl-orange oxidation tests. The resultant PEG-modified films were crack-free and developed a porous structure after calcination at 500 °C. Photo-oxidation tests showed the dependency of catalytic activity of the films on the number of layers (thickness) and porosity, i.e. of the interfacial area.

Starch/poly (butylene adipate-co-terephthalate)/montmorillonite films produced by blow extrusion

This study aims to prepare biodegradable films from cassava starch, poly (butylene adipate-co-terephthalate) (PBAT), and montmorillonite (MMT) using blow-extrusion process and analyze the effects of different types and concentrations of MMT on the microstructure, physicochemical, and mechanical properties of the resulting films. The films were produced by blending 30% of PBAT with glycerol (17.5%), starch (49.0-52.5%), and four different types of montmorillonite (Cloisite® Na+, 10A, 15A, and 30B) at two different concentrations (1.75% and 3.5%). All the films prepared in this study showed an increase in the basal spacing of MMT layers. In particular, the films with 10A and 30B showed the highest increase in intercalation basal spacing, suggesting the formation of intercalated composites. The addition of nanoclays decreased the elongation of films. The addition of Cloisite® 10A resulted in films with the lowest WVP values and the highest stability to water adsorption under different RH conditions.

Is it necessary to soak rice grains to prepare Rhizoctonia solani AG-4 inoculum?

A study was conducted to evaluate the effects on the development of root rot on common bean, cv. 'Dufrix' after treatment with four volumes of water (0, 30%, 60%, and 90%, v/w) added to rice grains previously immersed in water for 24 hours before autoclaving and colonization of grains by Rhizoctoniasolani AG-4. Colonized rice grains and non-infested rice grains were mixed in pots with sterilized soil and sand (2:1), where beans were sown. Based on results of area under plant emergence curve, plant height, plant dry weight, and disease severity, we conclude that inoculum is more effective in causing disease when no water is added to the rice grains before autoclaving.

Determinação da temperatura de solubilização da prata em ligas de Cu-Al-Ag por medidas de resistência elétrica

As temperaturas onde ocorre a solubilização da fase rica em prata, em ligas de Cu-Al-Ag, foram determinadas através de medidas de variação da resistência elétrica com a temperatura. As derivadas das curvas obtidas experimentalmente permitiram determinar com precisão essas temperaturas e também que se traçasse um esboço da região onde ocorre a transição monofásica para bifásica.

Comparação do ajuste dos modelos de morgan-mercer-flodin e de johnson-mehl-avrami na reação de precipitação na liga cu-3%al-5%ag

Em geral, os modelos de crescimento empregados na descrição de processos cinéticos do estado sólido utilizam as funções de Morgan-Mercer-Flodin (MMF) e Johnson-Mehl-Avrami (JMA). Neste trabalho comparou-se o comportamento das estimativas dos parâmetros dessas funções, em duas parametrizações, quando ajustadas aos dados experimentais de variação isotérmica da microdureza da liga Cu-3%Al-5%Ag com o tempo de envelhecimento, em cinco temperaturas diferentes. Na estimativa dos parâmetros aplicou-se o método dos mínimos quadrados à função linearizada do modelo e para o refinamento da solução, os procedimentos da regressão não linear. Foram obtidas as distribuições de freqüências das estimativas dos parâmetros, por simulação, e determinados seus erros relativos. Observou-se que, em uma das parametrizações das funções, a estimativa do parâmetro cinético apresentou maior estabilidade. Apesar dessas funções serem anteriormente consideradas distintas, verificou-se que a função de MMF é uma aproximação da função de JMA, sendo que esta, com a parametrização adequada, é a mais indicada para descrever o processo cinético considerado.

Influence of the Al content on the phase transformations in Cu-Al-Ag alloys

The influence of the Al content on the phase transformations in Cu-Al-Ag alloys was studied by classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The results indicated that the increase in the Al content and the presence of Ag decrease the rate of the b1 phase decomposition reaction and contribute for the raise of this transition temperature, thus decreasing the stability range of the perlitic phase resulted from the b1 decomposition reaction.