Síntese e caracterização de beads acrílicos preparados por polimerização em suspensão visando aplicação como excipiente farmacêutico para compressão direta

One of the difficulties reported for the suspension polymerization is control the size and granulometry of beads. The purpose of this work was to evaluate the use of cellulose nanowhiskers and mesoporous silica as stabilizers to reduce the size and the particle distribution. To monitor polymerization process was used FTIR-ATR spectroscopy. The morphology was analyzed by scanning electron microscopy. The particle size distribution was characterised using a CILAS granulometer. Thermal stability was studied by thermogravimetric analysis. The results indicated that cellulose nanowhiskers may provide stabilization and increase the thermal stability of the beads in contrast to mesoporous silica.

Produção e caracterização de espumas cerâmicas obtidas a partir de lodo de anodização de alumínio

Ceramic foams were produced from a sludge generated in the aluminum anodizing process by using an industrial polyurethane foam (replication method) with open cell sizes of 10 ± 5 ppi (porosity = 97%) which were impregnated with suspensions containing 50-61 wt.% alumina, 1 wt.% citric acid, 6 wt.% bentonite and fired at 1600 ºC for 2 h. The aluminum anodizing sludge shows a high alumina content (87.5 wt.%) and a low particle size (~1.7 mm) after calcination and milling. The obtained filters show porosity of approximately 70%, filtration capability (mass water flow) of 1.7 kg/s and mechanical strength under compression of 2.40 MPa.

Avaliação do processo adsortivo utilizando mesocarpo de coco verde para remoção do corante cinza reativo BF-2R

This work used green coconut mesocarp as a bioadsorbent to remove Reactive Gray BF-2R dye. A 2³ factorial design was used to evaluate the influence of the variables adsorbent mass, particle size and stirring speed on the adsorptive process. Kinetic and adsorption equilibrium studies were performed. Results showed that the kinetic equilibrium was reached after 150 min. Using the Langmuir model, a q max of 21.9 mg g-1 and k of 0.30 L g-1 was obtained. The mesocarp of coconut, a residue of agribusiness, proved to be an effective alternative technique for the removal of dye in this study.

Desenvolvimento e caracterização de nanopartículas lipídicas destinadas à aplicação tópica de dapsona

In this work, theospheres (innovative lipid nanoparticles) were prepared by the high pressure homogenization technique using different surfactants for dapsone encapsulation. Mean particle size ranged from 105 to 153 nm and negative zeta potentials were obtained for all theosphere formulations. Atomic force microscopy images confirmed the spherical shape of theospheres. The HPLC method used to determine dapsone-loaded theospheres was selective, linear, exact and precise. The entrapment efficiency of dapsone was 91.4%. Theospheres provided controlled release of idebenone (52.7 ± 1.6%) in comparison to the free drug (103.1 ± 1.9%).

A comparative study of hydroxyapatite nanoparticles synthesized by different routes

In this study, bioactive hydroxyapatite nanoparticles were prepared by two different methods: wet chemical precipitation and biomimetic precipitation. The aim was to evaluate the morphology, particle-size, crystallinity and phases of the powders obtained by traditional wet chemical precipitation and the novel biomimetic precipitation using a supersaturated calcium solution. The nanoparticles were investigated by transmission electron microscopy, Fourier transform infrared spectroscopy and X-ray diffraction. The results revealed that the nanoparticles were formed by hydroxyapatite with a high crystallinity and controlled morphology. Additionally, it was found that the shape and size of the nanoparticles can be modified with each preparation method.

Preparação de nanopartículas de prata e ouro: um método simples para a introdução da nanociência em laboratório de ensino

A new practical experiment involving silver and gold nanoparticle syntheses was introduced in an inorganic chemistry laboratory course for undergraduate students at the Institute of Chemistry, UNICAMP. The nanoparticles were synthesized by the reduction of silver nitrate and tetrachloroauric acid with sodium borohydride and sodium citrate in an aqueous medium. Stabilities of the suspensions were tested using several different reactants including sodium chloride, polyvinylpyrrolidone, polyvinyl alcohol and cistamine. Changes in optical properties were observed by electronic spectra and also by transmission electronic microscopy, which also yielded data for estimating particle size.

Interaction of naproxen with calcium carbonate: physicochemical characterization and in vitro drug release studies

Interaction and physicochemical characterization of dispersions of naproxen in calcium carbonate after freeze-drying the wet-state equilibrated mixture have been investigated by analytical methods. The FT-IR study revealed the acid-base reaction between naproxen and calcium carbonate. The DSC study indicated physical interaction and significantly diminished crystallinity of naproxen in the formulation containing higher quantities of calcium carbonate. Furthermore, the SEM study showed the reduced particle size and loss of crystalline morphology in the same sample. Drug release increased with the increase of calcium carbonate in the formulations. Formulation of naproxen with calcium carbonate in 1:2 ratio allowed its dissolution to the greatest extent (94.96%) while other compositions, 1:0.5 and 1:1, showed 80.86% and 78.30% release, respectively.

Vanadato de bismuto sintetizado por combustão em solução na presença de diferentes combustíveis: síntese, caracterização e estudo da atividade fotocatalítica

In this manuscript, a BiVO4 semiconductor was synthesized by solution combustion synthesis using different fuels (Alanine, Glycine and Urea). Also, the Tween® 80 surfactant was added during synthesis. BiVO4 was characterized by XRD, SEM and diffuse reflectance spectroscopy. Photocatalytic activity was evaluated by the discoloration of methylene blue at 664 nm under UV-visible light irradiation. According to XRD, the monoclinic phase of BiVO4 was obtained for the samples. The smallest particle size and highest k obs value were observed for the BiVO4/alanine sample, which promoted greater demethylation of methylene blue.

SYNGAS PRODUCTION FROM CO2-REFORMING OF CH4 OVER SOL-GEL SYNTHESIZED Ni-Co/Al2O3-MgO-ZrO2 NANOCATALYST: EFFECT OF ZrO2 PRECURSOR ON CATALYST PROPERTIES AND PERFORMANCE

Ni-Co/Al2O3-MgO-ZrO2 nanocatalyst with utilization of two different zirconia precursors, namely, zirconyl nitrate hydrate (ZNH) and zirconyl nitrate solution (ZNS), was synthesized via the sol-gel method. The physiochemical properties of nanocatalysts were characterized by XRD, FESEM, EDX, BET and FTIR analyses and employed for syngas production from CO2-reforming of CH4. XRD patterns, exhibiting proper crystalline structure and homogeneous dispersion of active phase for the nanocatalyst ZNS precursor employed (NCAMZ-ZNS). FESEM and BET results of NCAMZ-ZNS presented more uniform morphology and smaller particle size and consequently higher surface areas. In addition, average particle size of NCAMZ-ZNS was 15.7 nm, which is close to the critical size for Ni-Co catalysts to avoid carbon formation. Moreover, FESEM analysis indicated both prepared samples were nanoscale. EDX analysis confirmed the existence of various elements used and also supported the statements made in the XRD and FESEM analyses regarding dispersion. Based on the excellent physiochemical properties, NCAMZ-ZNS exhibited the best reactant conversion across all of the evaluated temperatures, e.g. CH4 and CO2 conversions were 97.2 and 99% at 850 ºC, respectively. Furthermore, NCAMZ-ZNS demonstrated a stable yield with H2/CO close to unit value during the 1440 min stability test.

KINETIC STUDY OF SELECTIVE GAS-PHASE OXIDATION OF ISOPROPANOL TO ACETONE USING MONOCLINIC ZRO2 AS A CATALYST

Zirconia was prepared by a precipitation method and calcined at 723 K, 1023 K, and 1253 K in order to obtain monoclinic zirconia. The prepared zirconia was characterized by XRD, SEM, EDX, surface area and pore size analyzer, and particle size analyzer. Monoclinic ZrO2 as a catalyst was used for the gas-phase oxidation of isopropanol to acetone in a Pyrex-glass-flow-type reactor with a temperature range of 443 K - 473 K. It was found that monoclinic ZrO2 shows remarkable catalytic activity (68%) and selectivity (100%) for the oxidation of isopropanol to acetone. This kinetic study reveals that the oxidation of isopropanol to acetone follows the L-H mechanism.

Synthesis, structural and morphological characterization of CeO2-ZnO nanosized powder systems from Pechini's method

This work reports on the investigation of nanosized CeO2-ZnO systems prepared by Pechini's method. The structural and morphological characterization of CeO2-ZnO systems as well as the characterization of CeO2 and ZnO separately, showed that the employed method result in powders with spheroidal particles whose size are in the range 30 - 200 nm, which is appropriate to provide homogeneous suspensions. The ZnO present in the prepared mixed oxides seems to increase particle size distribution and to influence the arrangement of the particles after powder dispersion.

Preparation of nano-MgO using ultrasonic method and its characteristics

MgO is an important inorganic material, which can be used in many aspects, such as catalyst, toxic-waste remediation agent, adsorbent, and others. In order to make use of MgO, nano-MgO was prepared by ultrasonic method using Mg (CH3COO)2.2H2O as precursor, NaOH aqueous solution as precipitant in this paper. Effect factors on MgO nano-particle size were investigated. Characteristics of samples were measured by TGA, XRD, TEM, and others techniques. The results showed that the size of nano-MgO about 4 nm could be obtained under the following conditions (ultrasonic time 20 min, ultrasonic power 250 W, titration rate of NaOH 0.25 mL/min, NaOH concentration 0.48 mol/L, calcinations temperature 410 °C, calcination time 1.5 h, heating rate of calcination 5 °C/min). It was a very simple and effective method to prepare nano-MgO.

Adsorption isotherm studies of BOD, TSS and colour reduction from palm oil mill effluent (POME) using boiler fly ash

Palm oil is one of the two most important vegetable oils in the world's oil and fats market. The extraction and purification processes generate different kinds of waste generally known as palm oil mill effluent (POME). Earlier studies had indicated the possibility of using boiler fly ash to adsorb impurities and colour in POME treatment. The adsorption treatment of POME using boiler fly ash was further investigated in detail in this work with regards to the reduction of BOD, colour and TSS from palm oil mill effluent. The amount of BOD, colour and TSS adsorbed increased as the weight of the boiler fly ash used was increased. Also, the smaller particle size of 425µm adsorbed more than the 850µm size. Attempts were made to fit the experimental data with the Freundlich, Langmuir and Dubinin-Radushkevich isotherms. The R² values, which ranged from 0.8974-0.9898, 0.8848-0.9824 and 0.6235-0.9101 for Freundlich, Langmuir and Dubinin-Radushkevich isotherms respectively, showed that Freundlich isotherm gave a better fit followed by Langmuir and then Dubinin-Radushkevich isotherm. The sorption trend could be put as BOD > Colour > TSS. The apparent energy of adsorption was found to be 1.25, 0.58 and 0.97 (KJ/mol) for BOD, colour and TSS respectively, showing that sorption process occurs by physiosorption. Therefore, boiler fly ash is capable of reducing BOD, Colour and TSS from POME and hence could be used to develop a good adsorbent for POME treatment.

Operational characteristics of four metering systems for agricultural fertilizers and amendments

The use of fertilizers and solid amendments in agriculture generates special interest for their effect on crop productivity, as well as for their environmental impact. The efficient use of these products demands knowing their physical and mechanical properties, the storing conditions effect and the operational characteristics of the metering systems used in the fertilizing equipment. In this context, the present study was developed with the purpose of evaluating the operational characteristics of different fertilizing metering systems and to determine the adequate metering system-product operational parameters, using powder lime, powder gypsum, granular 10-30-10 (N-P-K), and granular urea. Operational differences were established among four types of commercial fertilizer metering systems, including wire auger, star-shaped feed wheel, feed screw and ridged traction wheel. The study found that the unloading rate depends directly on the fertilizer metering system's rotating speed and is affected by particle size, repose angle, bulk density and moisture content of the applied product. The wire auger and star-shaped feed wheel metering systems were adequate for the distribution of powder products and the feed screw for granulated fertilizers. Furthermore, theoretical and experimental characteristic equations were established, defining curves for calibration and handling of the products plus the rotating speed range in which a better distributing behavior was achieved.

Characterization and use of swine deep bedding ashes in cementitious composites

The deep bedding is a swine alternative production, especially in the finishing phase, whose byproduct can be recycled, reducing the environmental impact. The objectives of this study were to characterize the ash coming from the controlled burning of the swine deep bedding (SDBA) based on rice husk, and to evaluate their performance in composites as a partial substitute for Portland cement (PC). To measure the differences between SDBA and rice husk ash (RHA) as a reference, we have characterized: particle size distribution, real specific density, x-ray diffraction, electrical conductivity, scanning electron microscopy, chemical analysis and loss on ignition. Samples were prepared for two experimental series: control, and another one with the partial replacement of 30% of SDBA in relation to the mass of the Portland cement. According to the results obtained for physical and mechanical characterization, the composites with SDBA can be used as a constructive element in the rural construction.