Conversão química de no e co sobre catalisadores à base de óxidos de cobalto ou de ferro

Cobalt or iron oxides supported or not on zeolite Hbeta were prepared and evaluated in the reduction reaction of NO by CO in presence of O2, SO2 or H2O. XRD results evidenced the Hbeta structure and the formation of Co3O4 and Fe2O3. TPR-H2 analysis showed complete reduction of cobalt oxide at lower temperatures than for iron oxide. The catalysts are quite active and the activity depends on the reaction temperature. The highest conversions rates were observed for pure iron oxide, which can be a relatively low cost catalyst for reduction of NO by CO, with high selectivity towards the N2 formation.

Cristalização convencional de zeólitas e induzida por sementes

Seed-assisted synthesis of zeolites diminishes crystallization time and enables the industrial use of certain zeolites, which was conventionally unfeasible due to the complexity of synthesis and the cost of organic structure-directing agents. This study reports the primary results of zeolite crystallization in the presence of seeds, which are used as a substitute for organic compounds.

DESENVOLVIMENTO DE MATERIAIS HÍBRIDOS MICRO-MESOPOROSOS DO TIPO ZSM-12/MCM-41

Micro-mesoporous hybrid materials of ZSM-12/MCM-41 type with different micro- and mesoporosity contributions were prepared by a procedure that uses the desilication of the zeolite in an alkaline medium, followed by recrystallization onto the mesostructure, where the zeolite is used as the silica source in the formation of mesoporous phase. The materials were characterized by X-ray diffraction, nitrogen adsorption-desorption at 77 K, scanning electron microscopy and thermal analysis. The results showed that the methodology utilized is efficient for obtaining hybrid materials of ZSM-12/MCM-41 type with optimized micro-and mesoporosity.

TUNGSTOPHOSPHORIC ACID HETEROGENIZED ONTO NH4ZSM5 AS AN EFFICIENT AND RECYCLABLE CATALYST FOR THE PHOTOCATALYTIC DEGRADATION OF DYES

Materials based on tungstophosphoric acid (TPA) immobilized on NH4ZSM5 zeolite were prepared by wet impregnation of the zeolite matrix with TPA aqueous solutions. Their concentration was varied in order to obtain TPA contents of 5%, 10%, 20%, and 30% w/w in the solid. The materials were characterized by N2 adsorption-desorption isotherms, XRD, FT-IR, 31P MAS-NMR, TGA-DSC, DRS-UV-Vis, and the acidic behavior was studied by potentiometric titration with n-butylamine. The BET surface area (SBET) decreased when the TPA content was raised as a result of zeolite pore blocking. The X-ray diffraction patterns of the solids modified with TPA only presented the characteristic peaks of NH4ZSM5 zeolites, and an additional set of peaks assigned to the presence of (NH4)3PW12O40. According to the Fourier transform infrared and 31P magic angle spinning-nuclear magnetic resonance spectra, the main species present in the samples was the [PW12O40]3- anion, which was partially transformed into the [P2W21O71]6- anion during the synthesis and drying steps. The thermal stability of the NH4ZSM5TPA materials was similar to that of their parent zeolites. Moreover, the samples with the highest TPA content exhibited band gap energy values similar to those reported for TiO2. The immobilization of TPA on NH4ZSM5 zeolite allowed the obtention of catalysts with high photocatalytic activity in the degradation of methyl orange dye (MO) in water, at 25 ºC. These can be reused at least three times without any significant decrease in degree of degradation.

USE OF A LOW-COST TEMPLATE-FREE ZSM-5 FOR ATMOSPHERIC PETROLEUM RESIDUE PYROLYSIS

To understand the physicochemical properties and catalytic activity during the pyrolysis of atmospheric petroleum residue, a template-free ZSM-5 zeolite was synthesized using a direct method without additional seeds or an organic structure director and compared with conventionally synthesized ZSM-5. The crystallinities of the two zeolites were evaluated by XRD and FTIR and were quite similar; however, structural analyses using SEM and argon physisorption revealed that the zeolites diverged in particle diameter and in the external surface area of the micropores. The synthesis procedure without a template incorporated additional aluminum into the crystalline network, according to ICP-AES and TPD NH3 experiments. The catalytic pyrolysis performed over the template-free ZSM-5 generated results comparable to those for pyrolysis performed over the conventional ZSM-5 according to its hydrocarbon distribution. The selectivity to aromatics compounds was exactly the same for both ZSM-5 zeolites, and these values stand out compared to thermal pyrolysis. The template-free ZSM-5 produced 20% of light hydrocarbons (C4-C6), where such compounds are olefins and paraffins of great interest to the petrochemical industry. Therefore, template-free ZSM-5 is promising for industrial use due to its lowered synthesis time, low-cost and significant distribution to light hydrocarbons.