Water absorbent polymer in sugarcane crop

The water absorbent polymer effect on vegetative growth and production of Theoretical Recovery Sugar (TRS) of sugarcane cv. RB 86 7515 was evaluated on two field tests installed in randomized blocks, with four treatments and five repetitions. The polymer doses were 0; 4; 8 and 12 g m-1 of furrow (test 1) and 0; 1.4; 2.8 and 4.2 g m-1 of furrow (test 2). Test 1 (dec/2007 to may/2009) was implanted in a Distroferric Red Argisol soil in Presidente Prudente - State of São Paulo (SP), Brazil; and the test 2 (Aug/2008 to Aug/2009) was implanted in a Red Yellow Argisol soil in Lucélia - State of São Paulo (SP), Brazil. In test 2, there were no significant differences for any evaluated parameters. In both tests the polymer doses equal to or less than 4 g m-1 of furrow showed no significant effect on the evaluated parameters. In test 1, the polymer doses of 8 and 12 g m-1 of the conditioning polymer increased the number of tillers in stage II of development and led to the largest amount of straw. The gross income per hectare has positive relation with the polymer doses. The polymer had no significant effect on the sugarcane stems productivity and technological parameters.

Arc fusion of self-fluxed nickel alloys

Self-fluxed nickel alloys are usually flame fused after thermal spraying. However, due to the practical aspects of high temperatures reached during flame fusing, large structures such as the hydraulic turbines for power generation, can not be efficiently coated. An alternative is to fuse the sprayed coating with a gas tungsten electric arc. In this case, heating is much more intensive and substrate temperature during and after the fusing operation is much lower, thus reducing the possibility that any problem will occur. In this work, coatings of self-fluxed nickel alloy fused by flame and gas tungsten arc were evaluated as protection of hydraulic turbines against cavitational damage. Several tests were performed, including the ASTM ultrasonically vibration-induced cavitation, optical and scanning electronic microscopic metallography, and hardness tests. The results showed that the arc-fused coating presented better cavitation damage resistance, probably due to its finer microstructure. A field application of this new technique is also described. A self-fluxed Ni alloy was flame sprayed in critical regions of Francis-type hydraulic turbine blades and fused by a gas tungsten arc after spraying. The blades will be inspected during the next two years.

Effect of particle morphology on the mechanical and thermo-mechanical behavior of polymer composites

Fiber reinforced polymer composites have been used in many applications, such as in automobile, aerospace and naval industries, due basically to their high strength-to-weight and modulus-to-weight, among other properties. Even though particles are usually not able to lead to the level of reinforcement of fibers, particle reinforced polymer composites have been proposed for many new applications due to their low cost, easy fabrication and isotropic properties. In this work, polymer composites were prepared by incorporating glass particles of different morphologies on poly(aryl sulfones) matrices. Particles with aspect ratios equal to 1, 2.5 and 10 were used. The prepared composites were characterized using electron microscopy and thermal analysis. Mechanical properties of the composites were evaluated using a four-point bending test. The thermo-mechanical behavior of the obtained composites was also investigated. The results showed that the morphology of the particles alter significantly the mechanical properties of composites. Particles with larger values of aspect ratio led to large elastic modulus but low levels of strain at failure. This result was explained by modeling the thermo-mechanical behavior of the composites using a viscoelastic model. Parameters of the model, obtained from a Cole-Cole type of plot, demonstrated that interactions at the polymer-reinforcing agent interface were higher for composites with large aspect ratio particles. Higher levels of interactions at interfaces can lead to higher degrees of stress transfer and, consequently, to composites with large elastic modulus, as experimentally observed.

Differences in pressure and temperature transitions of proteins and polymer gels

Pressure-driven and temperature-driven transitions of two thermoresponsive polymers, poly(N-isopropylacrylamide) (pNIPAM) and poly(N-vinylisobutyramide) (pNVIBA)), in both a soluble linear polymer form and a cross-linked hydro-gel form, were examined by a dynamic light-scattering method and direct microscopic observation, respectively. Their behavior was compared with that of protein systems. Changes in some characteristic parameters in the time-intensity correlation functions of dynamic light-scattering measurement of aqueous solutions of pNIPAM at various pressures and temperatures showed no essential differences during temperature and pressure scanning and, as a whole, the motions of polymers in aqueous solutions were similar in two types of transitions until chain shrinkage occurred. The gels (cross-linked polymer gels) prepared from the thermoresponsive polymers also showed similar volume transitions responding to the pressure and temperature increase. In temperature transitions, however, gels showed drastic volume shrinkage with loss of transparency, while pressure-induced transition showed a slow recovery of transparency while keeping the size, after first transient drastic volume shrinkage with loss of transparency. At a temperature slightly higher than the transition under atmospheric temperature, so-called reentry of the volume change and recovery of the transparency were observed during the pressure-increasing process, which implies much smaller aggregation or non-aggregated collapsed polymer chains in the gel at higher pressures, indicating a certain mechanistic difference of the dehydration processes induced by temperature and pressure.

Effects of nickel on the mineral composition of Fleischmann’s yeast (Saccharomyces cerevisiae)

Sugar cane juice containing 12% (w.w -1) of total reducing sugars and 0.0 to 5.0 mmol of nickel L-1, with pH ranging from 3.5 to 6.5, was inoculated with Fleischmann’s yeast (Saccharomyces cerevisiae) (10% w.w -1). Six hours after fermentation, the yeast’s cellular viability and trehalose content were evaluated. The resulting must was centrifuged and the raw yeast was analyzed by atomic absorption spectroscopy to evaluate the intracellular levels of calcium, copper, iron, magnesium, manganese, nickel, phosphorus, potassium, sulfur and zinc. The intracellular levels of iron, magnesium and calcium were affected and the yeast’s susceptibility to nickel was enhanced by the decrease in pH. The yeast’s growth was not affected by nickel at high pH, but the toxic effects of nickel were potentiated at low pH.