Sodium hypochlorite effects on dentin bond strength and acid-base resistant zone formation by adhesive systems

Aim: To evaluate the effects of 10% NaOCl gel application on the dentin bond strengths and morphology of resin-dentin interfaces formed by three adhesives. Methods: Two etch-and-rinse adhesives (One-Step Plus, Bisco Inc. and Clearfil Photo Bond, Kuraray Noritake Dental) and one self-etch adhesive (Clearfil SE Bond, Kuraray Noritake Dental) were applied on dentin according to the manufacturers’ instructions or after the treatment with 10% NaOCl (ED-Gel, Kuraray Noritake Dental) for 60 s. For interfacial analysis, specimens were subjected to acid-base challenge and observed by SEM to identify the formation of the acid-base resistant zone (ABRZ). For microtensile bond strength, the same groups were investigated and the restored teeth were thermocycled (5,000 cycles) or not before testing. Bond strength data were subjected to two-way ANOVA and Tukey’s test (p<0.05). Results: NaOCl application affected the bond strengths for One-Step Plus and Clearfil Photo Bond. Thermocycling reduced the bond strengths for Clearfil Photo Bond and Clearfil SE Bond when used after NaOCl application and One-Step Plus when used as recommended by manufacturer. ABRZ was observed adjacent to the hybrid layer for self-etch primer. The etch-and-rinse systems showed external lesions after acid-base challenge and no ABRZ formation when applied according to manufacturer’s instructions. Conclusions: 10% NaOCl changed the morphology of the bonding interfaces and its use with etch-&-rinse adhesives reduced the dentin bond strength. Formation of ABRZ was material-dependent and the interface morphologies were different among the tested materials.

Influence of adhesive system on quartz fiber post dislocation resistance in endodontically treated teeth

Aim: To evaluate the dislocation resistance of the quartz fiber post/cement/dentin interface after different adhesion strategies. Methods: Forty bovine lower central incisors were selected and prepared with K-files using the step-back technique, and irrigated with 3 mL of distilled water preceding the use of each instrument. Prepared teeth were stored at 37ºC and 100% humidity for 7 days. The roots were prepared and randomized into 4 groups. The quartz fiber post was cemented with an adhesion strategy according to the following groups: GBisCem- BISCEM; GOneStep±C&B- One Step ± C&B; GAllBond±C&B- AllBond3 ± C&B; GAllBondSE±C&B- AllBondSE ±C&B with a quartz fiber post. Cross-sectional root slices of 0.7 mm were produced and stored for 24 h at 37° C before being submitted to push-out bond strength. Results: The mean and standard deviation values of dislocation resistance were GBisCem: 1.12 (± 0.23) MPa, GOneStep±C&B: 0.81 (± 0.31) MPa, GAllBond±C&B: 0.98 (± 0.14) MPa, and GAllBondSE±C&B: 1.57 (± 0.04) MPa. GAllBondSE±C&B showed significantly higher values of dislocation resistance than the other groups. Conclusions: Based on this study design, it may be concluded that adhesion strategies showed different results of quartz post dislocation resistance. Simplified adhesive system with sodium benzene sulphinate incorporation provided superior dislocation resistance.

Influence of shade, curing mode, and aging on the color stability of resin cements

The color stability of resin cements is essential for aesthetic restorations. Aim: To evaluate the influence of shade and aging time on the color stability of two light-cured and two dual-cured resin cements. Methods: The CIE-Lab color parameters (n=6) were measured immediately after sample preparation and at 7, 30 and 90 days of aging in distilled water. The color difference (ΔE) was calculated and then analyzed by three-way ANOVA for repeated measures and Tukey’s HSD test (α=0.05). Results: ΔE was higher for transparent resin colors, followed by dark and light colors. The mean values of ΔE were lower for both light-cured resin cements compared to the dual-cured cements. As the aging time increased, ΔE values increased. Conclusions: The light-cured resin cements showed greater color stability. The lighter shades of luting were more likely to display a greater color change.

Antimicrobial and bond strength properties of a dental adhesive containing zinc oxide nanoparticles

Aim: To assess the effect of adding zinc oxide nanoparticles to dental adhesives on their anti-microbial and bond strength properties. Methods: 45 human premolars were cut at the cement enamel junction (CEJ) and the crowns were sliced into buccal and lingual halves. The specimens were classified into three groups, etched with 37% phosphoric acid for 15 s and rinsed for 30 s. Single Bond, Single Bond+5% zinc oxide and Single Bond+10% zinc oxide were used in the first, second and third groups. A cylinder of Z250 composite was bonded and cured for 40 s. For anti-bacterial testing, 10 samples of each group were assessed by direct contact test; 10 μL of bacterial suspension was transferred into tubes containing adhesives and incubated for one hour; 300 μL of brain heart infusion (BHI) broth was added to each tube and after 12 h, 50 μL of bacteria and broth were spread on blood agar plates and incubated for 24 h. Results: The colony count decreased significantly in the second and third groups compared to the first. Conclusions: Incorporation of zinc oxide nanoparticles into dental adhesives increases their anti-microbial properties without affecting their bond strength.