Influence of shade, curing mode, and aging on the color stability of resin cements

The color stability of resin cements is essential for aesthetic restorations. Aim: To evaluate the influence of shade and aging time on the color stability of two light-cured and two dual-cured resin cements. Methods: The CIE-Lab color parameters (n=6) were measured immediately after sample preparation and at 7, 30 and 90 days of aging in distilled water. The color difference (ΔE) was calculated and then analyzed by three-way ANOVA for repeated measures and Tukey’s HSD test (α=0.05). Results: ΔE was higher for transparent resin colors, followed by dark and light colors. The mean values of ΔE were lower for both light-cured resin cements compared to the dual-cured cements. As the aging time increased, ΔE values increased. Conclusions: The light-cured resin cements showed greater color stability. The lighter shades of luting were more likely to display a greater color change.

In vitro effects of erosive challenge on the surface properties of sealants

Aim: To assess in vitro the surface roughness (Ra), Vickers hardness (VHN) and surface morphology of resin and glass ionomer materials used for sealants after dynamic erosive challenge. Methods: Twenty specimens of each material were prepared and divided into experimental (erosive challenge) and control groups (n=10): Protect Riva (SDI), Opallis Flow (3M ESPE), Fluroshield (Dentsply), Filtek Z350 XT Flow (3M ESPE). The erosive challenge was performed 4 times per day (90 s) in cola drink and for 2 h in artificial saliva for 7 days. The control specimens were maintained in artificial saliva. Ra and VHN readings were performed before and after erosion. The percentage of hardness loss (%VHN) was obtained after erosion. The surface morphology was evaluated by scanning electron microscopy (SEM). The data were analyzed by ANOVA, Tukey and paired t tests (α=0.05). Results: After erosion and saliva immersion, there was an increase in Ra values for all groups and Riva group showed the highest Ra values. After erosive challenge, Riva and Filtek groups showed significant decrease in VHN values, but Filtek group showed the greatest %VHN. For all groups there was inorganic particle protrusion and matrix degradation after erosion visualized by SEM images. Conclusions: Erosive challenge affected the surface properties of all materials used as sealants, particularly in the Riva and Filtek groups.

Clinical evaluation of two materials in the restoration of abfraction lesions

Aim: To evaluate the clinical performance of a composite resin (CR) and a resin-modified glassionomer cement (RMGIC) for the treatment of abfraction lesions. Methods: Thirty patients with abfraction lesions in at least two premolar teeth were selected and invited to participate in this study. All restorations were made within the same clinical time frame. One tooth was restored with CR Z100TM (3M, St. Paul, MN, USA), and the other was restored with RMGIC VitremerTM (3M). The restorations were assessed immediately and 1, 6 and 12 months after the restoration, using modified US Public Health Service (USPHS) criteria: marginal integrity, marginal discoloration, wear, retention, secondary caries and hypersensitivity. The statistical analysis was based on Friedman ANOVA test and Mann-Whitney test, considering p<0.05 for statistical significance. Results: Both materials demonstrated satisfactory clinical performance after one year. In the individual analysis of each material, there was a significant difference (p<0.05) in the criteria marginal integrity and wear, for both CR and RMGIC. RMGIC exhibited more damage one year after the restoration. Comparing both materials, it was found a significant difference only for marginal discoloration, while the RMGIC restorations showed the worst prognosis after a year of evaluation. There was no significant difference in the number of retentions, caries or hypersensitivity between CR and RMGIC. Conclusions: It was concluded that CR exhibited the best clinical performance according to the cost-effectiveness and evaluation criteria used in this study.

Influence of adhesive system on quartz fiber post dislocation resistance in endodontically treated teeth

Aim: To evaluate the dislocation resistance of the quartz fiber post/cement/dentin interface after different adhesion strategies. Methods: Forty bovine lower central incisors were selected and prepared with K-files using the step-back technique, and irrigated with 3 mL of distilled water preceding the use of each instrument. Prepared teeth were stored at 37ºC and 100% humidity for 7 days. The roots were prepared and randomized into 4 groups. The quartz fiber post was cemented with an adhesion strategy according to the following groups: GBisCem- BISCEM; GOneStep±C&B- One Step ± C&B; GAllBond±C&B- AllBond3 ± C&B; GAllBondSE±C&B- AllBondSE ±C&B with a quartz fiber post. Cross-sectional root slices of 0.7 mm were produced and stored for 24 h at 37° C before being submitted to push-out bond strength. Results: The mean and standard deviation values of dislocation resistance were GBisCem: 1.12 (± 0.23) MPa, GOneStep±C&B: 0.81 (± 0.31) MPa, GAllBond±C&B: 0.98 (± 0.14) MPa, and GAllBondSE±C&B: 1.57 (± 0.04) MPa. GAllBondSE±C&B showed significantly higher values of dislocation resistance than the other groups. Conclusions: Based on this study design, it may be concluded that adhesion strategies showed different results of quartz post dislocation resistance. Simplified adhesive system with sodium benzene sulphinate incorporation provided superior dislocation resistance.

Antimicrobial and bond strength properties of a dental adhesive containing zinc oxide nanoparticles

Aim: To assess the effect of adding zinc oxide nanoparticles to dental adhesives on their anti-microbial and bond strength properties. Methods: 45 human premolars were cut at the cement enamel junction (CEJ) and the crowns were sliced into buccal and lingual halves. The specimens were classified into three groups, etched with 37% phosphoric acid for 15 s and rinsed for 30 s. Single Bond, Single Bond+5% zinc oxide and Single Bond+10% zinc oxide were used in the first, second and third groups. A cylinder of Z250 composite was bonded and cured for 40 s. For anti-bacterial testing, 10 samples of each group were assessed by direct contact test; 10 μL of bacterial suspension was transferred into tubes containing adhesives and incubated for one hour; 300 μL of brain heart infusion (BHI) broth was added to each tube and after 12 h, 50 μL of bacteria and broth were spread on blood agar plates and incubated for 24 h. Results: The colony count decreased significantly in the second and third groups compared to the first. Conclusions: Incorporation of zinc oxide nanoparticles into dental adhesives increases their anti-microbial properties without affecting their bond strength.