Development of surface flaw thresholds for pre-cured fiber reinforced polymer and groove size tolerance for near surface mounted fiber reinforced polymer retrofit systems

Since the introduction of fiber reinforced polymers (FRP) for the repair and retrofit of concrete structures in the 1980’s, considerable research has been devoted to the feasibility of their application and predictive modeling of their performance. However, the effects of flaws present in the constitutive components and the practices in substrate preparation and treatment have not yet been thoroughly studied. This research aims at investigating the effect of surface preparation and treatment for the pre-cured FRP systems and the groove size tolerance for near surface mounted (NSM) FRP systems; and to set thresholds for guaranteed system performance. This study was conducted as part of the National Cooperative Highway Research Program (NCHRP) Project 10-59B to develop construction specifications and process control manual for repair and retrofit of concrete structures using bonded FRP systems. The research included both analytical and experimental components. The experimental program for the pre-cured FRP systems consisted of a total of twenty-four (24) reinforced concrete (RC) T-beams with various surface preparation parameters and surface flaws, including roughness, flatness, voids and cracks (cuts). For the NSM FRP systems, a total of twelve (12) additional RC T-beams were tested with different grooves sizes for FRP bars and strips. The analytical program included developing an elaborate nonlinear finite element model using the general purpose software ANSYS. The bond interface between FRP and concrete was modeled by a series of nonlinear springs. The model was validated against test data from the present study as well as those available from the literature. The model was subsequently used to extend the experimental range of parameters for surface flatness in pre-cured FRP systems and for groove size study in the NSM FRP systems. Test results, confirmed by further analyses, indicated that contrary to the general belief in the industry, the impact of surface roughness on the global performance of pre-cured FRP systems was negligible. The study also verified that threshold limits set for wet lay-up FRP systems can be extended to pre-cured systems. The study showed that larger surface voids and cracks (cuts) can adversely impact both the strength and ductility of pre-cured FRP systems. On the other hand, frequency (or spacing) of surface cracks (cuts) may only affect system ductility rather than its strength. Finally, within the range studied, groove size tolerance of ±1/8 in. does not appear to have an adverse effect on the performance of NSM FRP systems.

Development of Surface Flaw Thresholds for Pre-Cured Fiber Reinforced Polymer and Groove Size Tolerance for Near Surface Mounted Fiber Reinforced Polymer Retrofit Systems

Since the introduction of fiber reinforced polymers (FRP) for the repair and retrofit of concrete structures in the 1980’s, considerable research has been devoted to the feasibility of their application and predictive modeling of their performance. However, the effects of flaws present in the constitutive components and the practices in substrate preparation and treatment have not yet been thoroughly studied. This research aims at investigating the effect of surface preparation and treatment for the pre-cured FRP systems and the groove size tolerance for near surface mounted (NSM) FRP systems; and to set thresholds for guaranteed system performance. The research included both analytical and experimental components. The experimental program for the pre-cured FRP systems consisted of a total of twenty-four (24) reinforced concrete (RC) T-beams with various surface preparation parameters and surface flaws, including roughness, flatness, voids and cracks (cuts). For the NSM FRP systems, a total of twelve (12) additional RC T-beams were tested with different grooves sizes for FRP bars and strips. The analytical program included developing an elaborate nonlinear finite element model using the general purpose software ANSYS. The model was subsequently used to extend the experimental range of parameters for surface flatness in pre-cured FRP systems, and for groove size study in the NSM FRP systems. Test results, confirmed by further analyses, indicated that contrary to the general belief in the industry, the impact of surface roughness on the global performance of pre-cured FRP systems was negligible. The study also verified that threshold limits set for wet lay-up FRP systems can be extended to pre-cured systems. The study showed that larger surface voids and cracks (cuts) can adversely impact both the strength and ductility of pre-cured FRP systems. On the other hand, frequency (or spacing) of surface cracks (cuts) may only affect system ductility rather than its strength. Finally, within the range studied, groove size tolerance of +1/8 in. does not appear to have an adverse effect on the performance of NSM FRP systems.

Enhanced biocompatibility of Nitinol via surface treatment and alloying

It is projected that by 2020, there will be 138 million Americans over 45, the age at which the increased incidence of heart diseases is documented. Many will require stents. This multi-billion dollar industry, with over 2 million patients worldwide, 15% of whom use Nitinol stents have experienced a decline in sales recently, due in part to thrombosis. It is a sudden blood clot that forms inside stents. As a result, the Food and Drug Administration and American Heart Association are calling for a new generation of stents, new designs and different alloys that are more adaptable to the arteries. The future of Nitinol therefore depends on a better understanding of the mechanisms by which Nitinol surfaces can be rendered stable and inert. In this investigation, binary and ternary Nitinol alloys were prepared and subjected to various surface treatments such as electropolishing (EP), magnetoelectropolishing (MEP) and water boiling & passivation (W&P). In vitro corrosion tests were conducted on Nitinol alloys in accordance with ASTM F 2129-08. The metal ions released into the electrolyte during corrosion tests were measured by Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). Biocompatibility was assessed by observing the growth of human umbilical vein endothelial cells (HUVEC) on the surface of Nitinol alloys. Static and dynamic immersion tests were performed by immersing the Nitinol alloys in cell culture media and measuring the amount of metal ions released in solution. Sulforhodamine B (SRB) assays were performed to elucidate the effect of metal ions on the growth of HUVEC cells. The surfaces of the alloys were studied using Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS) respectively. Finally, wettability and surface energy were measured by Contact Angle Meter, whereas surface roughness was measured by Atomic Force Microscopy (AFM). All the surface treated alloys exhibited high resistance to corrosion when compared with untreated alloys. SRB assays revealed that Ni and Cu ions exhibited greater toxicity than Cr, Ta and Ti ions on HUVEC cells. EP and MEP alloys possessed relatively smooth surfaces and some were composed of nickel oxides instead of elemental nickel as determined by XPS. MEP exhibited lowest surface energy and lowest surface roughness.

Assessment of biodegradable magnesium alloys for enhanced mechanical and biocompatible properties

Biomaterials have been used for more than a century in the human body to improve body functions and replace damaged tissues. Currently approved and commonly used metallic biomaterials such as, stainless steel, titanium, cobalt chromium and other alloys have been found to have adverse effects leading in some cases, to mechanical failure and rejection of the implant. The physical or chemical nature of the degradation products of some implants initiates an adverse foreign body reaction in the tissue. Some metallic implants remain as permanent fixtures, whereas others such as plates, screws and pins used to secure serious fractures are removed by a second surgical procedure after the tissue has healed sufficiently. However, repeat surgical procedures increase the cost of health care and the possibility of patient morbidity. This study focuses on the development of magnesium based biodegradable alloys/metal matrix composites (MMCs) for orthopedic and cardiovascular applications. The Mg alloys/MMCs possessed good mechanical properties and biocompatible properties. Nine different compositions of Mg alloys/MMCs were manufactured and surface treated. Their degradation behavior, ion leaching, wettability, morphology, cytotoxicity and mechanical properties were determined. Alloying with Zn, Ca, HA and Gd and surface treatment resulted in improved mechanical properties, corrosion resistance, reduced cytotoxicity, lower pH and hydrogen evolution. Anodization resulted in the formation of a distinct oxide layer (thickness 5-10 μm) as compared with that produced on mechanically polished samples (~20-50 nm) under ambient conditions. It is envisaged that the findings of this research will introduce a new class of Mg based biodegradable alloys/MMCs and the emergence of innovative cardiovascular and orthopedic implant devices.^

Treatment attrition among racial /ethnic minority adolescents participating in a brief motivational intervention for substance use problems: The influence of individual, social, cultural, and treatment factors

The present study has the primary aim of examining the predictors of treatment attrition among racial/ethnic minority adolescents with substance use problems. This study explores the potential differential influence of specific individual, social, cultural, and treatment factors on treatment attrition within three racial/ethnic subgroups of adolescents. Participants: A unique feature of the study is the use of a racial/ethnic minority sample (N=453), [U.S.-born Hispanics (n = 262), Foreign-born Hispanics (n = 117), and African-Americans (n = 74)]. Multivariate logit analyses were used to examine the influence of specific factors on treatment attrition among the full sample of adolescents, as well as within each racial/ethnic subgroup. Consistent with expectations, multivariate logit analyses reveal that, the specific factors associated with attrition varied across the three racial/ethnic subgroups. Having parents with problem substance use, being on the waitlist, and being court mandated to treatment emerged as predictors of attrition among the US-born Hispanics, while only Conduct Disorder was significantly associated with greater attrition among foreign-born Hispanics. Finally, among African-Americans, parental crack/cocaine use, parental abstinence from alcohol, and being on the waitlist were predictive of attrition. Multiple factors were associated with treatment attrition among racial/ethnic minority adolescents with specific factors differentially predicting attrition within each racial/ethnic subgroup. African-American youth were more than twice as likely as their Hispanic counterparts to leave treatment prematurely. It is critically important to understand the predictors of attrition among racial/ethnic minority youth in order to better meet the needs of youth most at risk of dropping out. ^

Treatment attrition among racial/ethnic minority adolescents participating in a brief motivational intervention for substance use problems : the influence of individual, social, cultural, and treatment factors

The present study has the primary aim of examining the predictors of treatment attrition among racial/ethnic minority adolescents with substance use problems. This study explores the potential differential influence of specific individual, social, cultural, and treatment factors on treatment attrition within three racial/ethnic subgroups of adolescents. Participants: A unique feature of the study is the use of a racial/ethnic minority sample (N=453), [U.S.-born Hispanics (n = 262), Foreign-born Hispanics (n = 117), and African- Americans (n = 74)]. Multivariate logit analyses were used to examine the influence of specific factors on treatment attrition among the full sample of adolescents, as well as within each racial/ethnic subgroup. Consistent with expectations, multivariate logit analyses reveal that, the specific factors associated with attrition varied across the three racial/ethnic subgroups. Having parents with problem substance use, being on the waitlist, and being court mandated to treatment emerged as predictors of attrition among the US-born Hispanics, while only Conduct Disorder was significantly associated with greater attrition among foreign-born Hispanics. Finally, among African-Americans, parental crack/cocaine use, parental abstinence from alcohol, and being on the waitlist were predictive of attrition. Multiple factors were associated with treatment attrition among racial/ethnic minority adolescents with specific factors differentially predicting attrition within each racial/ethnic subgroup. African-American youth were more than twice as likely as their Hispanic counterparts to leave treatment prematurely. It is critically important to understand the predictors of attrition among racial/ethnic minority youth in order to better meet the needs of youth most at risk of dropping out.

Enhanced Biocompatibility of NiTi (Nitinol) Via Surface Treatment and Alloying

It is projected that by 2020, there will be 138 million Americans over 45, the age at which the increased incidence of heart diseases is documented. Many will require stents. This multi-billion dollar industry, with over 2 million patients worldwide, 15% of whom use Nitinol stents have experienced a decline in sales recently, due in part to thrombosis. It is a sudden blood clot that forms inside stents. As a result, the Food and Drug Administration and American Heart Association are calling for a new generation of stents, new designs and different alloys that are more adaptable to the arteries. The future of Nitinol therefore depends on a better understanding of the mechanisms by which Nitinol surfaces can be rendered stable and inert. In this investigation, binary and ternary Nitinol alloys were prepared and subjected to various surface treatments such as electropolishing (EP), magnetoelectropolishing (MEP) and water boiling & passivation (W&P). In vitro corrosion tests were conducted on Nitinol alloys in accordance with ASTM F 2129-08. The metal ions released into the electrolyte during corrosion tests were measured by Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). Biocompatibility was assessed by observing the growth of human umbilical vein endothelial cells (HUVEC) on the surface of Nitinol alloys. Static and dynamic immersion tests were performed by immersing the Nitinol alloys in cell culture media and measuring the amount of metal ions released in solution. Sulforhodamine B (SRB) assays were performed to elucidate the effect of metal ions on the growth of HUVEC cells. The surfaces of the alloys were studied using Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS) respectively. Finally, wettability and surface energy were measured by Contact Angle Meter, whereas surface roughness was measured by Atomic Force Microscopy (AFM). All the surface treated alloys exhibited high resistance to corrosion when compared with untreated alloys. SRB assays revealed that Ni and Cu ions exhibited greater toxicity than Cr, Ta and Ti ions on HUVEC cells. EP and MEP alloys possessed relatively smooth surfaces and some were composed of nickel oxides instead of elemental nickel as determined by XPS. MEP exhibited lowest surface energy and lowest surface roughness.