Hydroxyapatite-nanotube composites and coatings for orthopedic applications

Hydroxyapatite (HA) has received wide attention in orthopedics, due to its biocompatibility and osseointegration ability. Despite these advantages, the brittle nature and low fracture toughness of HA often results in rapid wear and premature fracture of implant. Hence, there is a need to improve the fracture toughness and wear resistance of HA without compromising its biocompatibility. ^ The aim of the current research is to explore the potential of nanotubes as reinforcement to HA for orthopedic implants. HA- 4 wt.% carbon nanotube (CNT) composites and coatings are synthesized by spark plasma sintering and plasma spraying respectively, and investigated for their mechanical, tribological and biological behavior. CNT reinforcement improves the fracture toughness (>90%) and wear resistance (>66%) of HA for coating and free standing composites. CNTs have demonstrated a positive influence on the proliferation, differentiation and matrix mineralization activities of osteoblasts, during in-vitro biocompatibility studies. In-vivo exposure of HA-CNT coated titanium implant in animal model (rat) shows excellent histocompatibility and neobone integration on the implant surface. The improved osseointegration due to presence of CNTs in HA is quantified by the adhesion strength measurement of single osteoblast using nano-scratch technique. ^ Considering the ongoing debate about cytotoxicity of CNTs in the literature, the present study also suggests boron nitride nanotube (BNNT) as an alternative reinforcement. BNNT with the similar elastic modulus and strength as CNT, were added to HA. The resulting composite having 4 wt.% BNNTs improved the fracture toughness (∼85%) and wear resistance (∼75%) of HA in the similar range as HA-CNT composites. BNNTs were found to be non-cytotoxic for osteoblasts and macrophages. In-vitro evaluation shows positive role of BNNT in osteoblast proliferation and viability. Apatite formability of BNNT surface in ∼4 days establishes its osseointegration ability.^

Study of Ammonia Borane and its Derivatives: Influence of Nanoconfinements and Pressures

Recently, ammonia borane has increasingly attracted researchers’ attention because of its merging applications, such as organic synthesis, boron nitride compounds synthesis, and hydrogen storage. This dissertation presents the results from several studies related to ammonia borane. The pressure-induced tetragonal to orthorhombic phase transition in ammonia borane was studied in a diamond anvil cell using in situ Raman spectroscopy. We found a positive Clapeyron-slope for this phase transformation in the experiment, which implies that the phase transition from tetragonal to orthorhombic is exothermic. The result of this study indicates that the rehydrogenation of the high pressure orthorhombic phase is expected to be easier than that of the ambient pressure tetragonal phase due to its lower enthalpy. The high pressure behavior of ammonia borane after thermal decomposition was studied by in situ Raman spectroscopy at high pressures up to 10 GPa. The sample of ammonia borane was first decomposed at ~140 degree Celcius and ~0.7 GPa and then compessed step wise in an isolated sample chamber of a diamond anvil cell for Raman spectroscopy measurement. We did not observe the characteristic shift of Raman mode under high pressure due to dihydrogen bonding, indicating that the dihydrogen bonding disappears in the decomposed ammonia borane. Although no chemical rehydrogenation was detected in this study, the decomposed ammonia borane could store extra hydrogen by physical absorption. The effect of nanoconfinement on ammonia borane at high pressures and different temperatures was studied. Ammonia borane was mixed with a type of mesoporous silica, SBA-15, and restricted within a small space of nanometer scale. The nano-scale ammonia borane was decomposed at ~125 degree Celcius in a diamond anvil cell and rehydrogenated after applying high pressures up to ~13 GPa at room temperature. The successful rehydrogenation of decomposed nano-scale ammonia borane gives guidance to further investigations on hydrogen storage. In addition, the high pressure behavior of lithium amidoborane, one derivative of ammonia borane, was studied at different temperatures. Lithium amidoborane (LAB) was decomposed and recompressed in a diamond anvil cell. After applying high pressures on the decomposed lithium amidoborane, its recovery peaks were discovered by Raman spectroscopy. This result suggests that the decomposition of LAB is reversible at high pressures.

Study of ammonia borane and its derivatives: Influence of nanoconfinements and pressures

Recently, ammonia borane has increasingly attracted researchers’ attention because of its merging applications, such as organic synthesis, boron nitride compounds synthesis, and hydrogen storage. This dissertation presents the results from several studies related to ammonia borane. ^ The pressure-induced tetragonal to orthorhombic phase transition in ammonia borane was studied in a diamond anvil cell using in situ Raman spectroscopy. We found a positive Clapeyron-slope for this phase transformation in the experiment, which implies that the phase transition from tetragonal to orthorhombic is exothermic. The result of this study indicates that the rehydrogenation of the high pressure orthorhombic phase is expected to be easier than that of the ambient pressure tetragonal phase due to its lower enthalpy. ^ The high pressure behavior of ammonia borane after thermal decomposition was studied by in situ Raman spectroscopy at high pressures up to 10 GPa. The sample of ammonia borane was first decomposed at ∼140 degree Celcius and ∼0.7 GPa and then compessed step wise in an isolated sample chamber of a diamond anvil cell for Raman spectroscopy measurement. We did not observe the characteristic shift of Raman mode under high pressure due to dihydrogen bonding, indicating that the dihydrogen bonding disappears in the decomposed ammonia borane. Although no chemical rehydrogenation was detected in this study, the decomposed ammonia borane could store extra hydrogen by physical absorption. ^ The effect of nanoconfinement on ammonia borane at high pressures and different temperatures was studied. Ammonia borane was mixed with a type of mesoporous silica, SBA-15, and restricted within a small space of nanometer scale. The nano-scale ammonia borane was decomposed at ∼125 degree Celcius in a diamond anvil cell and rehydrogenated after applying high pressures up to ∼13 GPa at room temperature. The successful rehydrogenation of decomposed nano-scale ammonia borane gives guidance to further investigations on hydrogen storage. ^ In addition, the high pressure behavior of lithium amidoborane, one derivative of ammonia borane, was studied at different temperatures. Lithium amidoborane (LAB) was decomposed and recompressed in a diamond anvil cell. After applying high pressures on the decomposed lithium amidoborane, its recovery peaks were discovered by Raman spectroscopy. This result suggests that the decomposition of LAB is reversible at high pressures.^