Design and performance assessment of aortic heart valve for tissue engineering

Current artificial heart valves are classified as mechanical and bioprosthetic. An appealing pathway that promises to overcome the shortcomings of commercially available heart valves is offered by the interdisciplinary approach of cardiovascular tissue engineering. However, the mechanical properties of the Tissue Engineering Heart Valves (TEHV) are limited and generally fail in the long-term use. To meet this performance challenge novel biodegradable triblock copolymer poly(ethylene oxide)-polypropylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO or F108) crosslinked to Silk Fibroin (F108-SilkC) to be used as tri-leaflet heart valve material was investigated. ^ Synthesis of ten polymers with varying concentration and thickness (55 µm, 75 µm and 100 µm) was achieved via a covalent crosslinking scheme using bifunctional polyethylene glycol diglycidyl ether (PEGDE). Static and fatigue testing were used to assess mechanical properties of films, and hydrodynamic testing was performed to determine performance under a simulated left ventricular flow regime. The crosslinked copolymer (F108-Silk C) showed greater flexibility and resilience, but inferior ultimate tensile strength, by increasing concentration of PEGDE. Concentration molar ratio of 80:1 (F108: Silk) and thickness of 75 µm showed longer fatigue life for both tension-tension and bending fatigue tests. Four valves out of twelve designed satisfactorily complied with minimum performance requirement ISO 5840, 2005. ^ In conclusion, it was demonstrated that the applicability of a degradable polymer in conjugation with silk fibroin for tissue engineering cardiovascular use, specifically for aortic valve leaflet design, met the performance demands. Thinner thicknesses (t<75 µm) in conjunction with stiffness lower than 320 MPa (80:1, F108: Silk) are essential for the correct functionality of proposed heart valve biomaterial F108-SilkC. Fatigue tests were demonstrated to be a useful tool to characterize biomaterials that undergo cyclic loading. ^

Hydrogel formulation for enhanced regeneration in cell transplantation

Myocardial cell transplantation can compensate for the loss of necrotic cardiomyocytes. The objective of this research study was to reformulate the hydrogel with concentrations of growth factors, such as Leukemia Inhibitory Factor (LIF), Hepatocyte Growth Factor (HGF), and Interleukin-6 (IL-6). A controlled delivery system of PEO-PPO-PEO was formulated for release of a single growth factor and of multiple growth factors. Cytotoxicity and proliferation assay for single growth factors starting with 4000 skeletal myoblasts yielded their highest proliferation at 4 days with HGF (25,500 cells) and LIF (42,000 cells), while IL-6 (115,000 cells) generated its highest proliferation at 5 days. Combination of LIF and IL-6 resulted in highest proliferation at day 2 (220,000 cells), HGF and LIF (108,000 cells), and HGF and IL-6 (80,000 cells) both at 5 days. Viability at 37°C was maintained during the five days at 98-99%. The formulation was successful in myotube formation while maintaining a high purity of myoblasts in culture. The new formulation induced controlled release of growth factors and skeletal myoblasts delivery under favorable conditions while increasing the proliferation of myoblasts.