Reliability analysis of encapsulation methods for lead -based paint through an accelerated life testing

The adverse health effects of long-term exposure to lead are well established, with major uptake into the human body occurring mainly through oral ingestion by young children. Lead-based paint was frequently used in homes built before 1978, particularly in inner-city areas. Minority populations experience the effects of lead poisoning disproportionately. ^ Lead-based paint abatement is costly. In the United States, residents of about 400,000 homes, occupied by 900,000 young children, lack the means to correct lead-based paint hazards. The magnitude of this problem demands research on affordable methods of hazard control. One method is encapsulation, defined as any covering or coating that acts as a permanent barrier between the lead-based paint surface and the environment. ^ Two encapsulants were tested for reliability and effective life span through an accelerated lifetime experiment that applied stresses exceeding those encountered under normal use conditions. The resulting time-to-failure data were used to extrapolate the failure time under conditions of normal use. Statistical analysis and models of the test data allow forecasting of long-term reliability relative to the 20-year encapsulation requirement. Typical housing material specimens simulating walls and doors coated with lead-based paint were overstressed before encapsulation. A second, un-aged set was also tested. Specimens were monitored after the stress test with a surface chemical testing pad to identify the presence of lead breaking through the encapsulant. ^ Graphical analysis proposed by Shapiro and Meeker and the general log-linear model developed by Cox were used to obtain results. Findings for the 80% reliability time to failure varied, with close to 21 years of life under normal use conditions for encapsulant A. The application of product A on the aged gypsum and aged wood substrates yielded slightly lower times. Encapsulant B had an 80% reliable life of 19.78 years. ^ This study reveals that encapsulation technologies can offer safe and effective control of lead-based paint hazards and may be less expensive than other options. The U.S. Department of Health and Human Services and the CDC are committed to eliminating childhood lead poisoning by 2010. This ambitious target is feasible, provided there is an efficient application of innovative technology, a goal to which this study aims to contribute. ^

Association between mean residual life (MRL) and failure rate functions for continuous and discrete lifetime distributions

The purpose of this study was to correct some mistakes in the literature and derive a necessary and sufficient condition for the MRL to follow the roller-coaster pattern of the corresponding failure rate function. It was also desired to find the conditions under which the discrete failure rate function has an upside-down bathtub shape if corresponding MRL function has a bathtub shape. The study showed that if discrete MRL has a bathtub shape, then under some conditions the corresponding failure rate function has an upside-down bathtub shape. Also the study corrected some mistakes in proofs of Tang, Lu and Chew (1999) and established a necessary and sufficient condition for the MRL to follow the roller-coaster pattern of the corresponding failure rate function. Similarly, some mistakes in Gupta and Gupta (2000) are corrected, with the ensuing results being expanded and proved thoroughly to establish the relationship between the crossing points of the failure rate and associated MRL functions. The new results derived in this study will be useful to model various lifetime data that occur in environmental studies, medical research, electronics engineering, and in many other areas of science and technology.

New Bivariate Lifetime Distributions Based on Bath-Tub Shaped Failure Rate

A class of lifetime distributions which has received considerable attention in modelling and analysis of lifetime data is the class of lifetime distributions with bath-tub shaped failure rate functions because of their extensive applications. The purpose of this thesis was to introduce a new class of bivariate lifetime distributions with bath-tub shaped failure rates (BTFRFs). In this research, first we reviewed univariate lifetime distributions with bath-tub shaped failure rates, and several multivariate extensions of a univariate failure rate function. Then we introduced a new class of bivariate distributions with bath-tub shaped failure rates (hazard gradients). Specifically, the new class of bivariate lifetime distributions were developed using the method of Morgenstern’s method of defining bivariate class of distributions with given marginals. The computer simulations and numerical computations were used to investigate the properties of these distributions.