Surface and subsurface Vickers indentation cracks in SiC, Si3N4, and sialon ceramics

The nature of subsurface cracks formed under and around Vickers hardness indentations is often assumed rather than identified. Subsurface cracks in four engineering ceramics are revealed using a penetrant technique, and flaw dimensions are recorded. The resulting data are used to investigate several aspects of indentation cracking, such as crack shape, functional relationships between indentation load and flaw dimensions, and the performance of indentation fracture toughness equations. An R curve is constructed for each of the materials. © 1995 The Institute of Materials.

Field experiments on the dispersal, establishment and colonization of lichens on a slate rock surface

A sample of run-off water from a vertical, slate rock surface in Wales, U.K. contained abundant fragments of the lichen Parmelia glabratula ssp. fuliginosa from about 0.6 to 8.0 mm in diameter, a few fragments of Parmelia conspersa from 0.6 to 4.0 mm in diameter and a large number of unidentified propagules from 0.2 to 0.5 mm in diameter. The colonization of permanent plots on the rock surface was studied over six years. At the end of the experiment relatively few thalli of Parmelia conspersa, Parmelia glabratula ssp. fuliginosa and Buellia aethalea had established in plots on undisturbed and newly-exposed slate. Fragments (2 mm in diameter) of Parmelia conspersa placed on horizontal pieces of slate survived up to 120 days in cracks, 20 days on a thin smear of bird droppings but only 2-3 days on smooth slate, against small joints in the rock or in small holes. Isidia of Parmelia conspersa placed on horizontal pieces of slate established equally in plots on smooth undisturbed slate and in plots on the surface exposed after the removal of large Parmelia conspersa thalli, but less well on newly-exposed slate. These results suggest that lichen propagules are abundant in run-off water but establishment is a hazardous process. This may be attributable to a shortage of suitable sites on the substratum for attachment of propagules.

Fracture toughness of SIC, Si3N4, and sialon ceramics using controlled surface flaws

Knoop and Vickers indentation cracks have frequently been used as model 'precracks' in ceramic bend specimens for fracture toughness (K1c) determination. Indentation residual stress reduces the measured K1c but can be removed or accounted for by grinding, annealing, or modelling. Values of K1c are obtained for four materials using Vickers indentations and an improved stress intensity factor. Methods for residual stress removal or incorporation are compared, and the most reliable stress removal alternative is identified for each material. © 1996 The Institute of Materials.