Physicochemical properties of Pt-SO4/Al2O3 alkane oxidation catalysts

A series of sulfated alumina catalysts were synthesised by wet impregnation with sulfate-containing solutions. The degree of surface sulfation and corresponding surface acidity could be readily tuned by varying the molarity of impregnating solution. Strong acid treatments (>0.1 M) induced aluminium-sulfate crystallisation with a concomitant decrease in porosity and surface acidity. Platinum-doped sulfated aluminas showed enhanced activity towards methane, ethane and propane combustion. Activity scaled with the degree of accessible surface sulfate and platinum loading, however C-H bond scission appeared rate-limiting over both pure and presulfated aluminas. The magnitude of sulfate-promoted propane oxidation was greatest under heavily oxidising conditions (C3H6∶O2 > 1:20) but independent of Pt loading, confirming that support-mediated alkane activation is the dominant factor in the promotional mechanism.

Physicochemical properties of WOx/ZrO2 catalysts for palmitic acid esterification

A series of WOx/ZrO2 with various tungsten loadings was prepared via incipient-wetness impregnation of zirconium hydroxide. The resulting thermally processed materials were characterised by XRD, XPS, porosimetry, NH3-TPD and pyridine FTIR spectroscopy to elucidate their composition, morphology and acidity, and subsequently tested in the esterification of palmitic acid with methanol. Catalytic performance was strongly dependent upon calcination temperature and W surface density. Esterification activity increased with increasing surface W density, reaching a maximum at 8.9Wnm-2 corresponding to near monolayer coverage. Subsequent growth of crystalline WO3 lowered activity, consistent with a decrease in the density of active surface sites. Calcination temperatures as high as 800°C increased surface acidity and hence catalytic activity. The formation of polymeric tungstate species on zirconia is necessary to generate the Brönsted acid sites responsible for palmitic acid esterification under mild conditions. © 2014 Elsevier B.V.

Structure-reactivity correlations in sulphated-zirconia catalysts for the isomerisation of α-pinene

A range of mesoporous sulphated zirconias with tuneable structural and catalytic properties have been prepared by direct impregnation. The surface sulphate coverage can be readily varied, achieving a maximum value of ∼0.2 monolayers. High-temperature calcination induces the crystallisation of tetragonal zirconia while suppressing the monoclinic phase and enhances surface acidity. Superacid sites only appear above a critical threshold SO4 coverage of 0.08 mL (corresponding to 0.44 wt% total S). Sulphated zirconias show good activity towards α-pinene isomerisation of under mild conditions. Conversion correlates with the number Brønsted acid sites, while the selectivity towards mono- versus polycyclic products depends on the corresponding acid site strength; superacidity promotes limonene formation over camphene.

A hydrothermally stable transition alumina by condensation-enhanced self-assembly and pyrolysis crystallization:application in the steam reforming of methane

The preparation of a steam-based hydrothermally stable transition alumina is reported. The gel was derived from a synthetic sol-gel route where Al-tri-sec-butoxide is hydrolysed in the presence of a non-ionic surfactant (EO20PO70EO20), HCl as the catalyst and water (H2O/Al = 6); the condensation was enhanced by treating the hydrolysed gel with tetrabutylammonium hydroxide (TBAOH), after which it was dried at 60 °C by solvent evaporation. The so-obtained mesophase was crystallized under argon at 1200 °C (1 h) producing a transition alumina containing δ/α, and possibly θ, alumina phases. Due to its surface acidity, the pyrolysis conditions transform the block copolymer into a cross-linked char structure that embeds the alumina crystallites. Calcination at 650 °C generates a fully porous material by burning the char; a residual carbon of 0.2 wt.% was found, attributed to the formation of surface (oxy)carbides. As a result, this route produces a transition alumina formed by nanoparticles of about 30 nm in size on average, having surface areas in the range of 59-76 m2 g-1 with well-defined mesopores centered at 14 nm. The material withstands steam at 900 °C with a relative surface area rate loss lower than those reported for δ-aluminas, the state-of-the-art MSU-X γ-alumina and other pure γ-aluminas. The hydrothermal stability was confirmed under relevant CH4 steam reforming conditions after adding Ni; a much lower surface area decay and higher CH4 conversion compared to a state-of-the-art MSU-X based Ni catalyst were observed. Two effects are important in explaining the properties of such an alumina: the char protects the particles against sintering, however, the dominant effect is provided by the TBAOH treatment that makes the mesophase more resistant to coarsening and sintering. This journal is © the Partner Organisations 2014.