The boundary lubricated friction and wear of low alloy steel

Pin on disc wear machines were used to study the boundary lubricated friction and wear of AISI 52100 steel sliding partners. Boundary conditions were obtained by using speed and load combinations which resulted in friction coefficients in excess of 0.1. Lubrication was achieved using zero, 15 and 1000 ppm concentrations of an organic dimeric acid additive in a hydrocarbon base stock. Experiments were performed for sliding speeds of 0.2, 0.35 and 0.5 m/s for a range of loads up to 220 N. Wear rate, frictional force and pin temperature were continually monitored throughout tests and where possible complementary methods of measurement were used to improve accuracy. A number of analytical techniques were used to examine wear surfaces, debris and lubricants, namely: Scanning Electron Microscopy (SEM), Auger Electron Spectroscopy (AES), Powder X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), optical microscopy, Back scattered Electron Detection (BSED) and several metallographic techniques. Friction forces and wear rates were found to vary linearly with load for any given combination of speed and additive concentration. The additive itself was found to act as a surface oxidation inhibitor and as a lubricity enhancer, particularly in the case of the higher (1000 ppm) concentration. Wear was found to be due to a mild oxidational mechanism at low additive concentrations and a more severe metallic mechanism at higher concentrations with evidence of metallic delamination in the latter case. Scuffing loads were found to increase with increasing additive concentration and decrease with increasing speed as would be predicted by classical models of additive behaviour as an organo-metallic soap film. Heat flow considerations tended to suggest that surface temperature was not the overriding controlling factor in oxidational wear and a model is proposed which suggests oxygen concentration in the lubricant is the controlling factor in oxide growth and wear.

Global optimisation of cold-formed steel sections

In this thesis, standard algorithms are used to carry out the optimisation of cold-formed steel purlins such as zed, channel and sigma sections, which are assumed to be simply supported and subjected to a gravity load. For zed, channel and sigma section, the local buckling, distortional buckling and lateral-torsional buckling are considered respectively herein. Currently, the local buckling is based on the BS 5950-5:1998 and EN 1993-1-3:2006. The distortional buckling is calculated by the direct strength method employing the elastic distortional buckling which is calculated by three available approaches such as Hancock (1995), Schafer and Pekoz (1998), Yu (2005). In the optimisation program, the lateral-torsional buckling based on BS 5950-5:1998, AISI and analytical model of Li (2004) are investigated. For the optimisation program, the programming codes are written for optimisation of channel, zed and sigma beam. The full study has been coded into a computer-based analysis program (MATLAB).

The breakdown of stainless steels in strong acids

A study was made of the corrosion behaviour in the ASTM standard Nitric acid and Oxalic acid tests, of two commercial AISI type 304L steels in the as received condition and after various heat treatments. Optical microscopy and SEM, TEM and STEM in conjunction with energy dispersive x-ray analysis, were used to correlate the corrosion behaviour of these steels with their microstructure. Some evidence of phosphorus segregation at grain boundaries was found. The corrosion behaviour at microstructural level was studied by examining on the TEM thin foils of steel that had been exposed to boiling nitric acid. Banding attack in the nitric acid and oxalic acid tests was studied using SEM and EPNA and found to be due to the micro-segregation of chromium and nickel. Using two experimental series of 304L, one a 17% Cr, 91 Ni, steel with phosphorus additions from 0.006% to 0.028%, the other a 20% Cr, 121 Ni steel with boron additions from 0.0011 to 0.00B51. The effect of these elements on corrosion in the nitric acid test was studied. The effect of different cooling rates and different solution treatment temperature on the behaviour of these steels was examined. TEM and STEM in conjunction with energy-dispersive x-ray analysis were again used to study the microstructure of the steels. Phosphorus was found to affect the corrosion behaviour but no effect was found with boron.