The Mechanisms of wear of the video head

      This thesis examines the mechanism of wear occuring to the video head and their effect on signal reproduction. in particular it examines the wear occuring to manganese-zinc ferrite heads in sliding contact with iron oxide media.       A literature survey is presented, which covers magnetic recording technologies, focussing on video recording. Existing work on wear of magnetic heads is also examined, and gaps in the theoretical account of wear mechanisms presented in the literature are identified.       Pilot research was carrried out on the signal degradation and wear associated witha number of commercial video tapes, containing a range of head cleaning agents. From this research, the main body of the research was identified. A number of methods of wear measurement were examined for use in this project. Knoop diamond indentation was chosen because experimentation showed it to be capable of measuring wear occuring in situ. This technique was then used to examine the wear associated with different levels of A12O3 and Cr2O3 head cleaning agents.      The results of the research indicated that, whilst wear of the video head increases linearly with increasing HCA content, signal degradation does not vary significantly. The most significant differences in wear and signal reproduction were observed between the two HCAs. The signal degradation of heads worn with tape samples containing A12O3 HCA was found to be lower than heads worn with tapes containing Cr2O3 HCA.      The results also indicate that the wear to the head is an abrasive process characterised by ploughing of the ferrite surface and chipping of the edges of the head gap. Both phenomena appear to be caused by poor iron oxide and head cleaning particles, which create isolated asperities on the tape surface.   

Mild wear in dry and lubricated sliding systems

A vertical pin on horizontal disc machine has been used to conduct a series of experiments in air under dry and lubricating sliding conditions. For dry sliding low load and speed combinations were chosen to correspond to the mild wear region below the Welsh T1 transition. Lubricated tests were conducted under flooded conditions using Esso Technical White Oil alone and with a 0.1% stearic acid additive, for load and speed ranges that produced substantial amounts of asperity contact and thus a boundary lubricated regime of wear. The test material in all cases was AISI 52100 steel, for unlubricated sliding subjected to loads from 5 to 50 N and a range of speeds from 10-3 to 1.0 ms-1, and for lubricated sliding loads of 50 to 123 N and for speeds of 10-2 to 1.0 ms-1. Unlubricated wear debris was found to be a mixture of -Fe_2O_3 and -Fe. Unlubricated wear was found to occur via a thin film logarithmic oxide growth followed by agglomeration into thicker oxide plateaux 2 to 10 m in thickness. Lubricated wear occurred via thick film diffusion controlled oxide growth producing homogeneous oxide plateaux 0.1 to 0.2 m in thickness. X-ray photoelectron spectroscopy identified the presence of a surface film on pins worn in White Oil with stearic acid, which is thought to be iron stearate. A model has been developed for unlubricated wear based upon the postulated growth of thin film oxides by a logarithmic rate law. The importance of sliding geometry and environment to the dominant wear mechanism has been illustrated.

The role of oxidation in the protection of sliding metal surfaces

This study is concerned with the mechanisms of growth and wear of protective oxide films formed under various tribological conditions. In the study three different tribological systems are examined in each of which oxidational wear is the dominant equilibrium mode. These are an unlubricated steel on steel system sliding at low and elevated temperatures, a boundary lubricated aluminium bronze on steel system and an unlubricated reciprocating sliding 9% Cr steel system operated at elevated temperature, in an atmosphere of carbon dioxide. The results of mechanical measurements of wear and friction are presented for a range of conditions of load, speed and temper.ature for the systems, together with the results of extensive examinations of the surfaces and sub­ surfaces by various physical methods of analysis. The major part of the thesis, however, is devoted to the development and application of surface models and theoretical quantative expressions in order to explain the observed oxidational wear phenomena. In this work, the mechanisms of formation of load bearing ox ide plateaux are described and are found to be dependent on system geometry and environment. The relative importance of ''in contact" and "out of contact" oxidation is identified together with growth rate constants appropriate to the two situations. Hypotheses are presented to explain the mechanisms of removal of plateaux to form wear debris. The latter hypotheses include the effects of cyclic stressing and dislocation accumulation, together with effects associated with the kinetics of growth and physical properties of the various oxides. The proposed surf ace mode1s have led to the develop­ ment of quantitative expressions for contact temperature, unlubricated wear rates, boundary lubricated wear rates and the wear of rna ter ial during the transition from severe to mild wear. In general theoretical predictions from these expressions are in very good agreement with experimental values.

The effect of elevated temperature on the wear of stainless steel in contact with tungsten carbide

The bearings in the air motors of modern jet aircraft engines must operate dry in hostile conditions at temperatures up to 500° C, where the thrust races in the actuators operate at temperatures up to 300° C. One of the few metallurgical combinations which can function efficiently under these conditions is martensitic stainless steel on tungsten carbide. The work described was initiated to isolate the wear mechanisms of two such steels in contact with tungsten carbide at temperatures up to 500° C. Experiments were carried out on angular contact bearings similar to these used in service, where both rolling and sliding is present and also for pure sliding conditions using a pin-on-disc apparatus. Wear measurements of the bearings were obtained with wear rates, friction and surface temperatures from the pin-on-disc machine for a series of loads and speeds. Extensive X-ray diffraction analysis was carried out on the wear debris, with also S.E.M. analysis and hardness tests on the worn surfaces along with profilometry measurements of the disc. The oxidational parameters of the steel were obtained from measurements of oxide growth rates by ellipsometry. Three distinct mechanisms of wear were established and the latter two were found to be present in both configurations. These involve an oxidational-abrasive mechanism at loads below 40 N with pin surface temperatures up to about 300 °C, with the mechanism changing to severe wear for higher loads. As the temperature increases a third wear mechanism appears due to transfer of relatively soft oxide films to the steel surface reducing the wear rate. Theoretical K factors were derived and compared with experimental values which were found to be in good agreement for the severe wear mechanism. The pin-on-disc experiments may be useful as a screening test for material selection, without the considerable cost of producing the angular contact bearings.