Bioactive glass sol-gel foam scaffolds:evolution of nanoporosity during processing and in situ monitoring of apatite layer formation using small- and wide-angle X-ray scattering

Recent work has highlighted the potential of sol-gel-derived calcium silicate glasses for the regeneration or replacement of damaged bone tissue. The work presented herein provides new insight into the processing of bioactive calcia-silica sol-gel foams, and the reaction mechanisms associated with them when immersed in vitro in a simulated body fluid (SBF). Small-angle X-ray scattering and wide-angle X-ray scattering (diffraction) have been used to study the stabilization of these foams via heat treatment, with analogous in situ time-resolved data being gathered for a foam immersed in SBF. During thermal processing, pore sizes have been identified in the range of 16.5-62.0 nm and are only present once foams have been heated to 400 degrees C and above. Calcium nitrate crystallites were present until foams were heated to 600 degrees C; the crystallite size varied from 75 to 145 nm and increased in size with heat treatment up to 300 degrees C, then decreased in size down to 95 rim at 400 degrees C. The in situ time-resolved data show that the average pore diameter decreases as a function of immersion time in SBF, as calcium phosphates grow on the glass surfaces. Over the same time, Bragg peaks indicative of tricalcium phosphate were evident after only 1-h immersion time, and later, hydroxycarbonate apatite was also seen. The hydroxycarbonate apatite appears to have preferred orientation in the (h,k,0) direction.

An XPS study of pulsed plasma polymerised allyl alcohol film growth on polyurethane

The growth of highly functionalised poly allyl alcohol films by pulsed plasma polymerisation of CH2 double bond; length as m-dashCHCH2OH on biomedical grade polyurethane has been followed by X-ray photoelectron spectroscopy (XPS) and contact angle measurements. Film thickness is observed to increase approximately linearly with plasma modification time, suggesting a layer-by-layer growth mode of poly allyl alcohol. Water contact angle measurements reveal the change in the surface free energy of wetting decreases linearly with plasma modification up to the monolayer point after which a constant limiting value of −24 mJ m−2 was attained. Films prepared at 20 W plasma power with a duty cycle of 10 μs:500 μs exhibit a high degree of hydroxyl (single bondOH) retention with minimal fragmentation of the monomer observed. Increasing the plasma power up to 125 W is found to improve single bondOH retention at the expense of ether formation generating films close to the monomer stoichiometry. Duty cycle plays an important role in controlling both film composition and thickness, with longer off times increasing single bondOH retention, while longer on times enhance allyl alcohol film growth.

Preparation and property testing of compatibilized poly(l-lactide)/thermoplastic polyurethane blends

Poly(l-lactide) (PLL) has been blended with a polycaprolactone-based thermoplastic polyurethane (TPU) elastomer as a toughening agent and a poly(l-lactide-co-caprolactone) (PLLCL) copolymer as a compatibilizer. Both 2-component (PLL/TPU) and 3-component (PLL/TPU/PLLCL) blends were prepared by melt mixing, characterized, hot-pressed into thin sheets and their tensile properties tested. The results showed that, although the TPU could toughen the PLL, the blends were largely immiscible leading to phase separation. However, addition of the PLLCL copolymer improved blend compatibility. The best all-round properties were found for the 3-component blend of composition PLL/TPU/PLLCL = 90/10/10 parts by weight.