Novel biodegradable fibres for applications in tissue engineering and drug delivery

The preparation and characterisation of novel biodegradable polymer fibres for application in tissue engineering and drug delivery are reported. Poly(e-caprolactone) (PCL) fibres were produced by wet spinning from solutions in acetone under low shear (gravity flow) conditions. The tensile strength and stiffness of as-spun fibres were highly dependent on the concentration of the spinning solution. Use of a 6% w/v solution resulted in fibres having strength and stiffness of 1.8 MPa and 0.01 GPa respectively, whereas these values increased to 9.9 MPa and 0.1 GPa when fibres were produced from 20% w/v solutions. Cold drawing to an extension of 500% resulted in further increases in fibre strength (up to 50 MPa) and stiffness (0.3 GPa). Hot drawing to 500% further increased the fibre strength (up to 81 MPa) and stiffness (0.5 GPa). The surface morphology of as-spun fibres was modified, to yield a directional grooved pattern by drying in contact with a mandrel having a machined topography characterised by a peak-peak separation of 91 mm and a peak height of 30 mm. Differential scanning calorimetery (DSC) analysis of as-spun fibres revealed the characteristic melting point of PCL at around 58°C and a % crystallinity of approximately 60%. The biocompatibility of as-spun fibres was assessed using cell culture. The number of attached 3T3 Swiss mouse fibroblasts, C2C12 mouse myoblasts and human umbilical vein endothelial cells (HUVECs) on as-spun, 500% cold drawn, and gelatin coated PCL fibres were observed. The results showed that the fibres promoted cell proliferation for 9 days in cell culture and was slightly lower than on tissue culture plastic. The morphology of all cell lines was assessed on the various PCL fibres using scanning electron microscopy. The cell function of HUVECs growing on the as-spun PCL fibres was evaluated. The ability HUVECs to induce an immune response when stimulated with lipopolysaccaride (LPS) and thereby to increase the amount of cell surface receptors was assessed by flow cytometry and reverse transcription-polymerase chain reaction (RT-PCR). The results showed that PCL fibres did not inhibit this function compared to TCP. As-spun PCL fibres were loaded with 1 % ovine albumin (OVA) powder, 1% OVA nanoparticles and 5% OVA nanoparticles by weight and the protein release was assessed in vitro. PCL fibres loaded with 1 % OVA powder released 70%, 1% OVA nanoparticle released 60% and the 5% OVA nanoparticle released 25% of their protein content over 28 days. These release figures did not alter when the fibres were subjected to lipase enzymatic degradation. The OVA released was examined for structural integrity by SDS-PAGE. This showed that the protein molecular weight was not altered after incorporation into the fibres. The bioactivity of progesterone was assessed following incorporation into PCL fibres. Results showed that the progesterone released had a pronounced effect on MCF-7 breast epithelial cells, inhibiting their proliferation. The PCL fibres display high fibre compliance, a potential for controlling the fibre surface architecture to promote contact guidance effects, favorable proliferation rate of fibroblasts, myoblasts and HUVECs and the ability to release pharmaceuticals. These properties recommended their use for 3-D scaffold production in soft tissue engineering and the fibres could also be exploited for controlled presentation and release of biopharmaceuticals such as growth factors.

Nuclear magnetic resonance studies of molecular interactions and structures

This thesis is concerned with the investigation, by nuclear magnetic resonance spectroscopy, of the molecular interactions occurring in mixtures of benzene and cyclohexane to which either chloroform or deutero-chloroform has been added. The effect of the added polar molecule on the liquid structure has been studied using spin-lattice relaxation time, 1H chemical shift, and nuclear Overhauser effect measurements. The main purpose of the work has been to validate a model for molecular interaction involving local ordering of benzene around chloroform. A chemical method for removing dissolved oxygen from samples has been developed to encompass a number of types of sample, including quantitative mixtures, and its supremacy over conventional deoxygenation technique is shown. A set of spectrometer conditions, the use of which produces the minimal variation in peak height in the steady state, is presented. To separate the general diluting effects of deutero-chloroform from its effects due to the production of local order a series of mixtures involving carbon tetrachloride, instead of deutero-chloroform, have been used as non-interacting references. The effect of molecular interaction is shown to be explainable using a solvation model, whilst an approach involving 1:1 complex formation is shown not to account for the observations. It is calculated that each solvation shell, based on deutero-chloroform, contains about twelve molecules of benzene or cyclohexane. The equations produced to account for the T1 variations have been adapted to account for the 1H chemical shift variations in the same system. The shift measurements are shown to substantiate the solvent cage model with a cage capacity of twelve molecules around each chloroform molecule. Nuclear Overhauser effect data have been analysed quantitatively in a manner consistent with the solvation model. The results show that discrete shells only exist when the mole fraction of deutero-chloroform is below about 0.08.

Arthur Lindo Patterson, his function and element preferences in early crystal structures

In 1934, Arthur Lindo Patterson showed that a map of interatomic vectors is obtainable from measured X-ray diffraction data without phase information. Such maps were interpretable for simple crystal structures, but proliferation and overlapping of peaks caused confusion as the number of atoms increased. Since the peak height of a vector between two particular atoms is related to the product of their atomic numbers, a complicated structure could effectively be reduced to a simple one by including just a few heavy atoms (of high atomic number) since their interatomic vectors would stand out from the general clutter. Once located, these atoms provide approximate phases for Fourier syntheses that reveal the locations of additional atoms. Surveys of small-molecule structures in the Cambridge Structural Database during the periods 1936-1969, when Patterson methods were commonly used, and 1980-2013, dominated by direct methods, demonstrate large differences in the abundance of certain elements. The moderately heavy elements K, Rb, As and Br are the heaviest elements in the structure more than 3 times as often in the early period than in the recent period. Examples are given of three triumphs of the heavy atom method and two initial failures that had to be overcome. © 2014 © 2014 Taylor & Francis.

Chemical constituents associated with sewage settling velocity profiles

A methodology has been developed to measure the chemical constituents associated with the settling velocity fractions that comprise a wastewater settling velocity profile (SVP). 31 wastewater samples were collected from fifteen different catchments in England and Wales. For each catchment, settling velocity and associated chemical constituent profiles were determined. The results are mainly for Suspended Solids (SS), Chemical Oxygen Demand (COD), Phosphorus (P) and Total Kjeadahl Nitrogen (TKN), however these are supplemented by the results from 5 events for a suite of heavy metals. COD, P, Hg, Mn and Pb were found to be predominantly associated with the solid phase and TKN, Al, Cu and Fe with the liquor phase of the wastewater samples. The results in the thesis are expressed as mass of pollutant (g) per mass total SS (kg). COD and P were found to be mainly associated with the sinkers and had a particular affinity for solids with settling velocities in the range 0.9-9.03mm/sec. TKN was mainly associated with the soluble phase, however of the solids that did settle, a peak was found to be associated within the settling velocity range 0.9-9.03mm/sec. The relationships identified for COD and P were generally found to be unaffected by flow conditions and catchment characteristics. However, TKN was found to be affected by catchment type. Data on the distribution of heavy metals was limited, and no specific relationships with solids were identified. 16 mean pollutant profiles are presented in the thesis. Presentation of the data in this form will enable the results to be of use in the design of sedimentation devices to predict removal efficiencies for solids and associated pollutants. The findings of the research may also be applied to modelling tools to provide further characteristics on the solids that are modelled than is currently used. This would enhance the overall performance of tools used in integrated catchment modelling.

Drivers of peak sales for pharmaceutical brands

Peak sales are an important metric in the pharmaceutical industry. Specifically, managers are focused on the height-of-peak-sales and the time required achieving peak sales. We analyze how order of entry and quality affect the level of peak sales and the time-to-peak-sales of pharmaceutical brands. We develop a growth model that includes these two variables as well as control variables for own and competitive marketing activities. We find that early entrants achieve peak sales later, and they have higher peak-sales levels. High-quality brands achieve peak sales earlier, and their peak-sales levels are higher. In addition, quality has a moderating effect on the order of entry effect on time-to-peak-sales. Our results indicate that late entrants have longer expected time-to-peak-sales when they introduce a brand with high quality.