Investigation of the effects of low energy high dose ion bombardment in metals and compound semiconductors

The effect of low energy nitrogen molecular ion beam bombardment on metals and compound semiconductors has been studied, with the aim to investigate at the effects of ion and target properties. For this purpose, nitrogen ion implantation in aluminium, iron, copper, gold, GaAs and AIGaAs is studied using XPS and Angle Resolve XPS. A series of experimental studies on N+2 bombardment induced compositional changes, especially the amount of nitrogen retained in the target, were accomplished. Both monoenergetic implantation and non-monoenergetic ion implantation were investigated, using the VG Scientific ESCALAB 200D system and a d. c. plasma cell, respectively. When the samples, with the exception of gold, are exposed to air, native oxide layers are formed on the surfaces. In the case of monoenergetic implantation, the surfaces were cleaned using Ar+ beam bombardment prior to implantation. The materials were then bombarded with N2+ beam and eight sets of successful experiments were performed on each sample, using a rastered N2+ ion beam of energy of 2, 3, 4 and 5 keV with current densities of 1 μA/cm2 and 5 μA/cm22 for each energy. The bombarded samples were examined by ARXPS. After each complete implantation, XPS depth profiles were created using Ar+ beam at energy 2 ke V and current density 2 μA/cm2 . As the current density was chosen as one of the parameters, accurate determination of current density was very important. In the case of glow discharge, two sets of successful experiments were performed in each case, by exposing the samples to nitrogen plasma for the two conditions: at low pressure and high voltage and high pressure and low voltage. These samples were then examined by ARXPS. On the theoretical side, the major problem was prediction of the number of ions of an element that can be implanted in a given matrix. Although the programme is essentially on experimental study, but an attempt is being made to understand the current theoretical models, such as SATVAL, SUSPRE and TRIM. The experimental results were compared with theoretical predictions, in order to gain a better understanding of the mechanisms responsible. From the experimental results, considering possible experimental uncertainties, there is no evidence of significant variation in nitrogen saturation concentration with ion energy or ion current density in the range of 2-5 ke V, however, the retention characteristics of implantant seem to strongly depend on the chemical reactivity between ion species and target material. The experimental data suggests the presence of at least one thermal process. The discrepancy between the theoretical and experimental results could be the inability of the codes to account for molecular ion impact and thermal processes.

The importance of Na(plus)-K(plus)-Cl- cotransport in nitrogen mustard induced cell death

The incubation of murine leukaemic L1210 cells in vitro for 4 hours (hr) with 10uM nitrogen mustard (HN2), a bifunctional alkylating agent, inhibited the influx of the potassium congener, 88rubidium+ ( 86Rb+) by the selective inhibition of the Na+-K+-CI- cotransporter. The aim of this project was to investigate the importance of this lesion in HN2-induced cytotoxicity. 86Rb+ uptake in human erythrocytes was inhibited by high concentrations of HN2 (2mM) and occurred in two phases.In the first hour both the Na+/K+ ATPase pump and the Na+-K+-CI- cotransporter were equally inhibited but after 2 hrs exposure to 2mM HN2, the Na+ -K+ -CI- cotransporter was significantly more inhibited than the Na+/K+ ATPase pump. In contrast, both potassium transport systems were equally inhibited in L1210 cells incubated for 10 minutes with 1mM HN2. The selective inhibition of the Na+-K+-CI- cotransporter, after a 3 hrs exposure to 10uM HN2, was not absolved by coincubation with 5ug/ml cycloheximide (CHX), an inhibitor of protein synthesis. Incubation of L1210 cells with concentrations of diuretics which completely inhibited Na+-K+-CI- cotransport did not enhance the cytotoxicity of either HN2 or its monofunctional analogue 2-chloroethyldimethylamine (Me-HN1). The incubation of L1210 cells with a twice strength Rosewell Park Memorial Institute 1640 media did not enhance the toxicity of HN2. An L1210 cell line (L1210FR) was prepared which was able to grow in toxic concentrations of furosemide and exhibited a similiar sensitivity to HN2 as parental L1210 cells. Treatment of L1210 cells with 10uM HN2 resulted in a decrease in cell volume which was concurrent with the inhibition of the Na+-K+-CI- cotransporter. This was not observed in L1210 cells treated with either 1 or O.SuM HN2. Thus, possible differences in the cell death, in terms of necrosis and apoptosis, induced by the different concentrations of HN2 was investigated. The cell cycle of L1210 cells appeared to be blocked non-specifically by 10uM HN2 and in S and G2/M by either 1 or 0.5uM HN2. There were no significant changes in the cytosolic calcium concentrations of L1210 cells for up to 48 hrs after exposure to the three concentrations of HN2. No protection against th_ toxic effects of HN2 was observed in L1210 cells incubated with 5ug/ml CHX for up to 6 hrs. Incubation for 12 or 18 hrs with a non-toxic concentration (5mM) of L-Azetidine-2- carboxylic acid (ACA) enhanced the toxicity of low concentrations (<0.5uM) of HN2.