Elemental partitioning and microstructural development in duplex stainless steel weld metal

A thermodynamic analysis which is capable of estimating the austenite/ferrite equilibria in duplex stainless steels has been carried out using the sublattice thermodynamic model. The partitioning of alloying elements between the austenite and ferrite phases has been calculated as a function of temperature. The results showed that chromium partitioning was not influenced significantly by the temperature. The molybdenum, on the other hand, was found to partition preferentially into ferrite phase as the temperature decreases. A strong partitioning of nickel into the austenite was observed to decrease gradually with increasing temperature. Among the alloying elements, average nitrogen concentration was found to have the most profound effect on the phase balance and the partitioning of nitrogen into the austenite. The partitioning coefficient of nitrogen (the ratio of the mole fraction of nitrogen in the austenite to that in the ferrite) was found to be as high as 7.0 around 1300 K. Consequently, the volume fraction of austenite was influenced by relatively small additions of nitrogen. The results are compared with the experimentally observed data in a duplex stainless steel weld metal in conjunction with the solid state δ → δ + γ phase transformation. Particular attention was given to the morphological instability of grain boundary austenite allotriomorphs. A compariso between the experimental results and calculations indicated that the instability associated with irregular austenite perturbations results from the high degree of undercooling. The results suggest that the model can be used successfully to understand the development of the microstructure in duplex stainless steel weld metals.

The importance of Na(plus)-K(plus)-Cl- cotransport in nitrogen mustard induced cell death

The incubation of murine leukaemic L1210 cells in vitro for 4 hours (hr) with 10uM nitrogen mustard (HN2), a bifunctional alkylating agent, inhibited the influx of the potassium congener, 88rubidium+ ( 86Rb+) by the selective inhibition of the Na+-K+-CI- cotransporter. The aim of this project was to investigate the importance of this lesion in HN2-induced cytotoxicity. 86Rb+ uptake in human erythrocytes was inhibited by high concentrations of HN2 (2mM) and occurred in two phases.In the first hour both the Na+/K+ ATPase pump and the Na+-K+-CI- cotransporter were equally inhibited but after 2 hrs exposure to 2mM HN2, the Na+ -K+ -CI- cotransporter was significantly more inhibited than the Na+/K+ ATPase pump. In contrast, both potassium transport systems were equally inhibited in L1210 cells incubated for 10 minutes with 1mM HN2. The selective inhibition of the Na+-K+-CI- cotransporter, after a 3 hrs exposure to 10uM HN2, was not absolved by coincubation with 5ug/ml cycloheximide (CHX), an inhibitor of protein synthesis. Incubation of L1210 cells with concentrations of diuretics which completely inhibited Na+-K+-CI- cotransport did not enhance the cytotoxicity of either HN2 or its monofunctional analogue 2-chloroethyldimethylamine (Me-HN1). The incubation of L1210 cells with a twice strength Rosewell Park Memorial Institute 1640 media did not enhance the toxicity of HN2. An L1210 cell line (L1210FR) was prepared which was able to grow in toxic concentrations of furosemide and exhibited a similiar sensitivity to HN2 as parental L1210 cells. Treatment of L1210 cells with 10uM HN2 resulted in a decrease in cell volume which was concurrent with the inhibition of the Na+-K+-CI- cotransporter. This was not observed in L1210 cells treated with either 1 or O.SuM HN2. Thus, possible differences in the cell death, in terms of necrosis and apoptosis, induced by the different concentrations of HN2 was investigated. The cell cycle of L1210 cells appeared to be blocked non-specifically by 10uM HN2 and in S and G2/M by either 1 or 0.5uM HN2. There were no significant changes in the cytosolic calcium concentrations of L1210 cells for up to 48 hrs after exposure to the three concentrations of HN2. No protection against th_ toxic effects of HN2 was observed in L1210 cells incubated with 5ug/ml CHX for up to 6 hrs. Incubation for 12 or 18 hrs with a non-toxic concentration (5mM) of L-Azetidine-2- carboxylic acid (ACA) enhanced the toxicity of low concentrations (<0.5uM) of HN2.