Ductile fracture mechanisms in a structural steel

Microstructural fracture processes in a BS4360 Grade 50D structural steel with lower sulphur content were studied in smooth tensile specimen tests and Charpy-size bend bar tests. Based on the experimental analysis, an experimental void growth relation with the plastic strain and stress triaxiality and multiplying factor on void growth were determined. Experimental results show that the void growth relation can be reasonably used to estimate the constraint in the specimens containing the notch or crack, also they can be used to evaluate the variations of the stress triaxiality in front of the notch and crack tip under general yielding condition. Side-grooves obviously increase the constraint of the CVN specimens. Strain hardening leads to increasing the stress triaxiality, and decelerating the net void growth. This is especially true for the values of stress triaxiality more than about one. Additionally, the effect of the stress triaxiality on the critical void growth corresponding to the onset of ductile tearing was preliminarily investigated. In this work, a large number of smaller specimens were tested to investigate the ductile-brittle transition behaviour of the structural steel. A void growth rate explanation was suggested for evaluating the temperature transition behaviour. The elastic-plastic fracture tough-ness values based on small specimen tests, such as pre-cracked side-grooved bending specimen and short bar tensile specimen, may give large overestimates of the plane strain fracture toughness.

Fracture behaviour of an aluminide coating on a single crystal nickel base superalloy

Measurement of the coating fracture strain of an aluminide coating on a single crystal nickel base superalloy has been performed both in three-point bending and using variable wall thickness testpieces. As-aged specimens, 28 to 33 μm in thickness, were tested at room temperature, 600, 700 and 750 °C; specimens pre-exposed for 140 h at 850 and 1100 °C in air and vacuum were tested at room temperature. Fracture strains varied from 0.52 to 0.70% for as-aged specimens tested at temperatures up to 700 °C and specimens exposed at 850 °C and tested at room temperature. The crack path for these conditions was intergranular or transgranular in the main coating, along carbide-matrix interfaces in the coating transition zone, and at an angle of 30-45° to the original crack path in the substrate. The as-aged coating tested at 750 °C was ductile; a ductile-brittle transition occurs between 700 and 750 °C for the strain rate used (1 × 10-5 s-1). Following 1100 °C pre-exposure, specimens were ductile at room temperature with fractures strains of several percent. In this condition the crack morphology changed to one of subsurface nucleation in β grains and at β-γ′ interfaces. © 1993.

Using overlay test to evaluate fracture properties of field-aged asphalt concrete

Field material testing provides firsthand information on pavement conditions which are most helpful in evaluating performance and identifying preventive maintenance or overlay strategies. High variability of field asphalt concrete due to construction raises the demand for accuracy of the test. Accordingly, the objective of this study is to propose a reliable and repeatable methodology to evaluate the fracture properties of field-aged asphalt concrete using the overlay test (OT). The OT is selected because of its efficiency and feasibility for asphalt field cores with diverse dimensions. The fracture properties refer to the Paris’ law parameters based on the pseudo J-integral (A and n) because of the sound physical significance of the pseudo J-integral with respect to characterizing the cracking process. In order to determine A and n, a two-step OT protocol is designed to characterize the undamaged and damaged behaviors of asphalt field cores. To ensure the accuracy of determined undamaged and fracture properties, a new analysis method is then developed for data processing, which combines the finite element simulations and mechanical analysis of viscoelastic force equilibrium and evolution of pseudo displacement work in the OT specimen. Finally, theoretical equations are derived to calculate A and n directly from the OT test data. The accuracy of the determined fracture properties is verified. The proposed methodology is applied to a total of 27 asphalt field cores obtained from a field project in Texas, including the control Hot Mix Asphalt (HMA) and two types of warm mix asphalt (WMA). The results demonstrate a high linear correlation between n and −log A for all the tested field cores. Investigations of the effect of field aging on the fracture properties confirm that n is a good indicator to quantify the cracking resistance of asphalt concrete. It is also indicated that summer climatic condition clearly accelerates the rate of aging. The impact of the WMA technologies on fracture properties of asphalt concrete is visualized by comparing the n-values. It shows that the Evotherm WMA technology slightly improves the cracking resistance, while the foaming WMA technology provides the comparable fracture properties with the HMA. After 15 months aging in the field, the cracking resistance does not exhibit significant difference between HMA and WMAs, which is confirmed by the observations of field distresses.