Functionalised polymers

Synthetic routes to polymers possessing functional groups were studied. Direct functionalisation of poly(vinyltoluene) by lithiation and carboxylation resulted in the expected carboxylic acid but reaction was complicated by the production of a mixture of products. Reaction occurred both at the polymer backbone and at the pendant methyl group. Reaction with ethyl formate was also difficult to control and a secondary alcohol was formed even when an excess of the carbonyl compounds was employed. Grignard formation of poly(bromostyrene) was successful but once formed, the derivative rearranged resulting in chain scission and degradation of the polymer. Therefore subsequent reactions of the Grignard reagent with carbonyl groups were unsuccessful in producing functionalised polymers. Reactions of vinyltoluene monomer were more successful. Although complications arose when lithiation and carboxylation of the monomer were carried out using lithium diisopropylamide because the carboxylic acid product reacted with the excess lithium diisopropylamide present, metallation by potassium t-butoxide followed by reaction with 2-(3-chloropropyl)-2-methyl-1,3-dioxalane resulted in the formation of 2-methyl-2(4-(vinylphenyl)-butyl-1,3,-dioxalane. The butyllithium initiated anionic polymerisation of this protected monomer resulted in a polymer which had a very narrow molecular weight distribution (Mw/Mn= 1.05) and subsequent hydrolysis of the polymer resulted in poly(6(vinylphenyl)-hexan-2-one) which was derivatised with 2,4 dinitrophenyl-hydrazine. Functionalisation by modification of the siloxane derivative 3-(methylpropenoxycarbonyl)ltrimethoxysilane was unsuccessful. The acid catalysed exchange reactions of this monomer with alcohols such as eugenol, octan-1-ol, pentan-1-ol, and hexan-1-ol were inefficient, resulting in a mixture of products and unreacted starting materials.

Porous tin film synthesized by electrodeposition and the electrochemical performance for lithium-ion batteries

Porous tin films as anode for lithium-ion batteries are electrodeposited on graphite paper. Homogeneous tin films with significant void space accommodate the volume change during tin lithiation/delithiation. Through adjusting the electrodeposition currents and time, the morphologies and void space of tin films on graphite paper are controllable. At fixed electrodeposition current densities, the prolonged electrodeposition time plays the role in growing big tin particles and resulting the disappearance of void space among tin particles. The increased electrodeposition current plays the role to increase the quantity of tin seeds in thickness of tin film, and the void space among tin particles remains but the thick film limits its electrochemical performance. The tin films electrodeposited at an optimized current densities and for an optimized electrodeposition time, present the best electrochemical performance, because the tin nanoparticles are well dispersed on graphite substrate including void space. The tin film electrodeposited at 0.2 A cm-2 for 2 min shows the capacity of 1.0 mAh cm-2 after 50 charge/discharge cycles. The void space of tin film is very important for the best capacity and cyclic ability. The metallic tin film produced at 0.4 A cm-2 for 3 min remains the uniform and microporous structure after charge/discharge for 50 cycles.