Another angle on contact lens surface analysis

Purpose: Dynamic contact angle (DCA) methods have advantages over other contact angle methodologies, not least that they can provide more than single contact angle values. Here we illustrate the use of DCA analysis to provide “fingerprint” characterisation of contact lens surfaces, and the way that different materials change in the early stages of wear. Method: The DCA method involves attaching to a microbalance weighted strips cut from a lens. The strips are then cyclically inserted into and removed from an aqueous solution. Conventionally, readings of force taken from linear portions of the resultant dipping curves are translated into advancing (CAa) and receding contact (CAr) angles. Additionally, analysis of the force versus immersion profile provides a “fingerprint” characterisation of the state of the lens surface. Results: CAa and CAr values from DCA traces provide a useful means of differentiating gross differences in hydrophilicity and molecular mobility of surfaces under particular immersion and emersion conditions, such as dipping rate and dwell times. Typical values for etafilcon A (CAa:63.1; CAr:37) and balafilcon B (CAa:118.4; CAr:36.4) illustrate this. Surface modifications induced in lens manufacture are observed to produce not only changes in these value, which may be small, but also changes in the DCA “fingerprint” (slope, undulations, length of plateau). Interestingly, similar changes are induced in the first few hours of lens wear with some lens-patient combinations. Conclusions: Although single parameter contact angles are useful for material characterisation, information of potential clinical interest can be obtained from more detailed analysis of DCA traces.

Applicability of contact angle techniques used in the analysis of contact lenses, part 1:comparative methodologies

Objectives and Methods: Contact angle, as a representative measure of surface wettability, is often employed to interpret contact lens surface properties. The literature is often contradictory and can lead to confusion. This literature review is part of a series regarding the analysis of hydrogel contact lenses using contact angle techniques. Here we present an overview of contact angle terminology, methodology, and analysis. Having discussed this background material, subsequent parts of the series will discuss the analysis of contact lens contact angles and evaluate differences in published laboratory results. Results: The concepts of contact angle, wettability and wetting are presented as an introduction. Contact angle hysteresis is outlined and highlights the advantages in using dynamic analytical techniques over static methods. The surface free energy of a material illustrates how contact angle analysis is capable of providing supplementary surface characterization. Although single values are able to distinguish individual material differences, surface free energy and dynamic methods provide an improved understanding of material behavior. The frequently used sessile drop, captive bubble, and Wilhelmy plate techniques are discussed. Their use as both dynamic and static methods, along with the advantages and disadvantages of each technique, is explained. Conclusions: No single contact angle technique fully characterizes the wettability of a material surface, and the application of complimenting methods allows increased characterization. At present, there is not an ISO standard method designed for soft materials. It is important that each contact angle technique has a standard protocol, as small protocol differences between laboratories often contribute to a variety of published data that are not easily comparable. © 2013 Contact Lens Association of Ophthalmologists.

Through-thickness plasma modification of biodegradable and nonbiodegradable porous polymer constructs

Pure poly(lactide-co-glycolide) and polystyrene surfaces are not very suitable to support cell adhesion/ spreading owing to their hydrophobic nature and low surface energy. The interior surfaces of large porous 3D scaffolds were modified and activated using radio-frequency, low-pressure air plasma. An increase in the wettability of the surface was observed after exposure to air plasma, as indicated by the decrease in the contact angles of the wet porous system. The surface composition of the plasma-treated polymers was studied using X-ray photoelectron spectroscopy. pH-dependent zeta-potential measurements confirm the presence of an increased number of functional groups. However, the plasma-treated surfaces have a less acidic character than the original polymer surfaces as seen by a shift in their isoelectric point. Zeta-potential, as well as contact angle measurements, on 3D scaffolds confirm that plasma treatment is a useful tool to modify the surface properties throughout the interior of large scaffolds. © 2008 Wiley Periodicals, Inc.

Anisotropic surface energetics and wettability of macroscopic form I paracetamol crystals

Advancing (θA) and receding (θR) contact angles were measured with several probe liquids on the external facets (201), (001), (011), and (110) of macroscopic form I paracetamol crystals as well as the cleaved (internal) facet (010). For the external crystal facets, dispersive surface energies γd calculated from the contact angles were found to be similar (34 ± 1 mJ/m2), while the polar components varied significantly. Cleaving the crystals exposed a more apolar (010) surface with very different surface properties, including γd = 45 ± 1 mJ/m2. The relative surface polarity (γp/γ) of the facets in decreasing order was (001) > (011) > (201) > (110) > (010), which agreed with the fraction of exposed polar hydroxyl groups as determined from C and O 1s X-ray photoelectron spectroscopy (XPS) spectra, and could be correlated with the number of non-hydrogen-bonded hydroxyl groups per unit area present for each crystal facet, based on the known crystal structures. In conclusion, all facets of form I paracetamol crystals examined exhibited anisotropic wetting behavior and surface energetics that correlated to the presence of surface hydroxyl groups.  © 2006 American Chemical Society.

Use of imaging technology to better understand soft contact lens fit dynamics

The principal theme of this thesis is the identification of additional factors affecting, and consequently to better allow, the prediction of soft contact lens fit. Various models have been put forward in an attempt to predict the parameters that influence soft contact lens fit dynamics; however, the factors that influence variation in soft lens fit are still not fully understood. The investigations in this body of work involved the use of a variety of different imaging techniques to both quantify the anterior ocular topography and assess lens fit. The use of Anterior-Segment Optical Coherence Tomography (AS-OCT) allowed for a more complete characterisation of the cornea and corneoscleral profile (CSP) than either conventional keratometry or videokeratoscopy alone, and for the collection of normative data relating to the CSP for a substantial sample size. The scleral face was identified as being rotationally asymmetric, the mean corneoscleral junction (CSJ) angle being sharpest nasally and becoming progressively flatter at the temporal, inferior and superior limbal junctions. Additionally, 77% of all CSJ angles were within ±50 of 1800, demonstrating an almost tangential extension of the cornea to form the paralimbal sclera. Use of AS-OCT allowed for a more robust determination of corneal diameter than that of white-to-white (WTW) measurement, which is highly variable and dependent on changes in peripheral corneal transparency. Significant differences in ocular topography were found between different ethnicities and sexes, most notably for corneal diameter and corneal sagittal height variables. Lens tightness was found to be significantly correlated with the difference between horizontal CSJ angles (r =+0.40, P =0.0086). Modelling of the CSP data gained allowed for prediction of up to 24% of the variance in contact lens fit; however, it was likely that stronger associations and an increase in the modelled prediction of variance in fit may have occurred had an objective method of lens fit assessment have been made. A subsequent investigation to determine the validity and repeatability of objective contact lens fit assessment using digital video capture showed no significant benefit over subjective evaluation. The technique, however, was employed in the ensuing investigation to show significant changes in lens fit between 8 hours (the longest duration of wear previously examined) and 16 hours, demonstrating that wearing time is an additional factor driving lens fit dynamics. The modelling of data from enhanced videokeratoscopy composite maps alone allowed for up to 77% of the variance in soft contact lens fit, and up to almost 90% to be predicted when used in conjunction with OCT. The investigations provided further insight into the ocular topography and factors affecting soft contact lens fit.