The effect of barium substitution on the ferroelectric properties of Sr2 Nb2 O7 Ceramics

This work revealed that the solid solution compounds of Sr 2-xBaxNb2O7 are promising lead-free materials for high-temperature piezoelectric sensor application. These compounds were confirmed as ferroelectric materials with high Curie points (> 900°C) by their piezoelectric activity after poling, ferroelectric domain switching in their P-E hysteresis loops and thermal depoling behavior. The effect of Ba substitution on the structure and properties of Sr 2-xBaxNb2O7 (x < 1.0) was investigated. The solid solution limit of Sr2-xBaxNb 2O7 was determined by XRD as x < 0.6. The a-, b-, c- axes, and cell volume increase with Ba addition. The textured ceramics of Sr2-xBaxNb2O7 were prepared for the first time. The highest d33 was measured as 3.6 ± 0.1 pC/N for Sr1.8Ba0.2Nb2O7. © 2012 The American Ceramic Society.

Piezoelectric and dielectric properties of Ce substituted La2Ti2O7 ceramics

The ferroelectric and dielectric properties of cerium (Ce) substituted La2Ti2O7 (LTO) have been investigated. Single phase, dense La2-xCexTi2O7 (x=0.15, 0.25, 0.35) ceramics were prepared by spark plasma sintering. The solubility limit of Ce in La2-xCexTi2O7 was found to be between 0.35 and 0.5. The a-, b- and c-axes of the unit cell decrease with increasing Ce substitution. The Curie point (Tc) of La2-xCexTi2O7 (x=0, 0.15, 0.25, 0.35) decreases and dielectric constant and loss increase with increasing Ce substitution. Cerium can increase the d33 of La2Ti2O7. The highest d33 was 3.9±0.1pC/N for La1.85Ce0.15Ti2O7 textured ceramic. © 2012 Elsevier Ltd.

Synthesis and thermoelectric properties of Yb-doped Ca0.9-x Yb x La0.1MnO3 ceramics

The microstructure and thermoelectric properties of Yb-doped Ca0.9-x Yb x La0.1 MnO3 (0 ≤ x ≤ 0.05) ceramics prepared by using the Pechini method derived powders have been investigated. X-ray diffraction analysis has shown that all samples exhibit single phase with orthorhombic perovskite structure. All ceramic samples possess high relative densities, ranging from 97.04% to 98.65%. The Seebeck coefficient is negative, indicating n-type conduction in all samples. The substitution of Yb for Ca leads to a marked decrease in the electrical resistivity, along with a moderate decrease in the absolute value of the Seebeck coefficient. The highest power factor is obtained for the sample with x = 0.05. The electrical conduction in these compounds is due to electrons hopping between Mn3+ and Mn4+, which is enhanced by increasing Yb content.