The chemistry of ceramic glazes

The development of ideas and theories concerning the structure of glazes, as one of the glassy materials, are reviewed in the general introduction. The raw materials and the manufacturing process for glazes are described (Chapter One). A number of new vanadyl(IV) dipyridylamine and tripyrldylamine complexes have been prepared, various spectroscopic techniques are used in the investigation of the vanadyl ion in a weak ligand field, the situation of those found in a glaze environment (Chapter Three). In glaze recipes containing silica, potash feldspar, china clay, MO(M= Ca, Sr, Sa, Ti and Zn) and NiO, the ligand field theory is used in the elucidation of the effect of M (in MO) on the absorption spectra and coordination behaviour of Ni(II) in glazes. The magnetic and visible spectral results are reviewed in terms of Dietzel's idea of field strength of M and also in terms of Shteinberg's theory of glaze structure. X-ray diffraction is used for the identification of various species that formed after the firing process of glazes (Chapter Four). In Chapter Five, [] Mossbauer spectroscopy, supplemented by E.S.R., X-ray and visible spectral measurements are used in the investigation of iron in a glaze composition similar to that used in Chapter Four. The Mossbauer results are used in following the influence of; M in MO (M= Sr, Ca and Ba), oxides of titanium(IV) and vanadium(V ), and firing conditions on the chemistry of iron. Generally the iron(II) and iron(III) in the fired glazes are in octahedral sites although there are a range of similar, though not identical environments. A quite noticable influence of M (in MO) on the resonance line width is seen. In one case evidence is found for iron(IV) in an iron/vanadium glaze. E.S.R. of vanadium containing glazes indicate that vanadium is present as V02+ in a highly distorted tetragonal environment .

The cutting performance of sialon ceramic tools

The thesis deals with a research programme in which the cutting performance of a new generation of ceramic cutting tool material is evaluated using the turning process. In part one, the performance of commercial Kyon 2000 sialon ceramic inserts is studied when machining a hardened alloy steel under a wide range of cutting conditions. The aim is to formulate a pattern of machining behaviour in which tool wear is related to a theoretical interpretation of the temperatures and stresses generated by the chip-tool interaction. The work involves a correlation of wear measurement and metallographic examination of the wear area with the measurable cutting data. Four main tool failure modes are recognised: (a) flank and crater wear (b) grooving wear (c) deformation wear and (d) brittle failure Results indicate catastrophic edge breakdown under certain conditions. Accordingly in part two, the edge geometry is modified to give a double rake tool; a negative/positive combination. The results are reported for a range of workpiece materials under orthogonal cutting conditions. Significant improvements in the cutting performance are achieved. The improvements are explained by a study of process parameters; cutting forces, chip thickness ratio, chip contact length, temperature distribution, stress distribution and chip formation. In part three, improvements in tool performance are shown to arise when the edge chamfer on a single rake tool is modified. Under optimum edge chamfer conditions a substantial increase in tool life is obtained compared with the commercial cutting geometry.

An X-ray micro-fluorescence study to investigate the distribution of Al, Si, P and Ca ions in the surrounding soft tissue after implantation of a calcium phosphate-mullite ceramic composite in a rabbit animal model

Synthetic calcium phosphates, despite their bioactivity, are brittle. Calcium phosphate-mullite composites have been suggested as potential dental and bone replacement materials which exhibit increased toughness. Aluminium, present in mullite, has however been linked to bone demineralisation and neurotoxicity: it is therefore important to characterise the materials fully in order to understand their in vivo behaviour. The present work reports the compositional mapping of the interfacial region of a calcium phosphate-20 wt% mullite biocomposite/soft tissue interface, obtained from the samples implanted into the long bones of healthy rabbits according to standard protocols (ISO-10993) for up to 12 weeks. X-ray micro-fluorescence was used to map simultaneously the distribution of Al, P, Si and Ca across the ceramic-soft tissue interface. A well defined and sharp interface region was present between the ceramic and the surrounding soft tissue for each time period examined. The concentration of Al in the surrounding tissue was found to fall by two orders of magnitude, to the background level, within similar to 35 mu m of the implanted ceramic.