Noncovalent coatings for the separation of synthetic polypeptides by nonaqueous capillary electrophoresis

Recently, we demonstrated the possibility to extend the range of capillary electrophoresis (CE) applications to the separation of non-water-soluble synthetic polymers. This work focuses on the control of the electro-osmotic flow (EOF) and on the limitation of the solute adsorption in nonaqueous electrolytes. For these purposes, different strategies were investigated. For the initial, a viscous additive (ethylene glycol or glycerol) was used in the electrolyte in order to decrease the EOF magnitude and, possibly, to compete with solute adsorption. A second strategy was to modify, before separation, the fused-silica capillary wall by the adsorption of poly(ethylene oxide) (PEO) via hydrogen bonding. The influence of the molecular mass of the adsorbed PEO on the EOF magnitude and direction was studied in electrolytes based on methanol/acetonitrile mixtures containing ammonium ions. For PEO molecular masses above 1000 g/mol, reversed (anodic) EOF were reported in accordance with previous results obtained with PEO covalently bonded capillaries. The influence of the nature and the concentration of the background electrolyte cation on the EOF magnitude and direction were also investigated. A third strategy consisted in modifying the capillary wall by the adsorption of a cationic polyelectrolyte layer. Advantageously, this polyelectrolyte layer suppressed the adsorption of the polymer solutes onto the capillary wall. The results obtained in this work confirm the high potential and the versatility of CE for the characterization of ionizable organic polymers in nonaqueous media.

Nonaqueous capillary zone electrophoresis of synthetic organic polypeptides

Poly(Nε-trifluoroacetyl-l-lysine) was used as a model solute to investigate the potential of nonaqueous capillary electrophoresis (NACE) for the characterization of synthetic organic polymers. The information obtained by NACE was compared to that derived from size exclusion chromatography (SEC) experiments, and the two techniques were found to be complimentary for polymer characterization. On one hand, NACE permitted (i) the separation of oligomers according to their molar mass and (ii) the separation of the polymers according to the nature of the end groups. On the other hand, SEC experiments were used for the characterization of the molar mass distribution for higher molar masses. Due to the tendency of the solutes (polypeptides) to adsorb onto the fused-silica capillary wall, careful attention was paid to the rinsing procedure of the capillary between runs in order to keep the capillary surface clean. For that purpose, the use of electrophoretic desorption under denaturating conditions was very effective. Optimization of the separation was performed by studying (i) the influence of the proportion of methanol in a methanol/acetonitrile mixture and (ii) the influence of acetic acid concentration in the background electrolyte. Highly resolved separation of the oligomers (up to a degree of polymerization n of ∼50) was obtained by adding trifluoroacetic acid to the electrolyte. Important information concerning the polymer conformations could be obtained from the mobility data. Two different plots relating the effective mobility data to the degree of polymerization were proposed for monitoring the changes in polymer conformations as a function of the number of monomers.

On the hydrothermal stability of MCM-41. Evidence of capillary tension-induced effects

MCM-41's limited hydrothermal stability has been often related to the hydrolysis of Si-O-Si bonds due to the low degree of condensation, its thin walls or a combination of them. In this work, evidence for an additional factor is provided; a physical effect that occurs during the drying of the hydrothermally treated calcined material due to the intense capillary stress exerted in water. Depending on both physical (i.e. mechanical) and chemical (i.e. hydrolysis) resistances, the structure undergoes differently. Three MCM-41 samples with different degree of condensation were investigated. The most remarkable results are found with un-aged TEOS based material, which gets fully disordered and shrunk for all applied hydrothermal temperatures in water. Comparison between water and a low-surface-tension-solvent drying revealed that capillarity is responsible for the loss of ordering (and shrinkage) at moderate hydrothermal temperatures. The material's structure is hexagonal and shrinkage-free under the low-surface-tension-solvent route. At a high hydrothermal temperature, hydrolysis is extensive and responsible for the loss of ordering. The other remarkable finding regards the aged MCM-41 mesostructure that maintains the hexagonal features at all applied temperatures in water, and it is more stable against capillarity at high temperature. The Na-metasilicate based material is mechanically very stable and gets disordered at high temperature due to hydrolysis.