Biomorphous SiC ceramics prepared from cork oak as precursor

Porous ceramic materials of SiC were synthesized from carbon matrices obtained via pyrolysis of natural cork as precursor. We propose a method for the fabrication of complex-shaped porous ceramic hardware consisting of separate parts prepared from natural cork. It is demonstrated that the thickness of the carbon-matrix walls can be increased through their impregnation with Bakelite phenolic glue solution followed by pyrolysis. This decreases the material's porosity and can be used as a way to modify its mechanical and thermal characteristics. Both the carbon matrices (resulted from the pyrolysis step) and the resultant SiC ceramics are shown to be pseudomorphous to the structure of initial cork. Depending on the synthesis temperature, 3C-SiC, 6H-SiC, or a mixture of these polytypes, could be obtained. By varying the mass ratio of initial carbon and silicon components, stoichiometric SiC or SiC:C:Si, SiC:C, and SiC:Si ceramics could be produced. The structure, as well as chemical and phase composition of the prepared materials were studied by means of Raman spectroscopy and scanning electron microscopy.

Femtosecond laser writing of buried waveguides in erbium III-Doped oxyfluoride glasses and nano-glass-ceramics

Femtosecond-pulsed laser writing of waveguides, a few mm long, is demonstrated; waveguides were written orthogonally to the writing beam inside the bulk of ErIII-doped oxyfluoride glasses at a depth of 160 mum. The writing beam was 795 nm wavelength, 54 fs pulse duration and 11 MHz repetition rate. Tracks were written at pulse energies of 13.1 nJ to 26.1 nJ and sample translational velocity of 10 mmmiddot.s-1 to 28 mmmiddots-1. The influence of translational velocity and pulse energy on the cross-sectional shape and integrity of the written tracks is reported. Tracks tend to be narrower as the pulse energy is lowered or translational velocity decreased. Above 22.9 nJ, pulse energy, tracks tend to crack. The estimated refractive index profile of one track has a maximum increase of refractive index of 0.003 at the centre. These glasses normally form nano-glass-ceramics on heat treatment just above the glass transformation temperature (Tg). Here, a post-fs-writing heat-treatment just above Tg causes nano-ceramming of the glass sample and removes a light-guiding peripheral region of the fs-written tracks suggesting that this region may have been fs-modified by stress alone. Waveguiding at 651 nm and 973 nm wavelengths, and upconversion, are demonstrated in optimally written tracks.

Zirconia and alumina based catalysts for steam reforming of naphthalene

The present paper deals with experimentation of ZrO2 and Al2O3-supported catalysts for conversion of naphthalene, chosen as tar model compound of pyrolysis or gasification syngas. In particular, the reforming capacity of active metals and promoters such as Co, Ni, Fe, Cr, Ce and Pt was tested in a fixed bed reactor at temperature from 400 to 900 °C. As regards ZrO2-supported catalysts, the best results were achieved by the Ni/Fe/Pt catalyst with 96% naphthalene conversion, 78% and 280% as CO and H2 production yield at 800 °C. Regarding Al2O3-supported catalysts, they were more active on average than the zirconia ones, achieving a very good performance even at 500 °C (90–100% naphthalene conversion, 30–40% CO yield and 300–350% H2 yield at 550 °C). Influence of different amounts of alumina, montmorillonite and carbon on carrier composition as well as pellets’ size were also studied. Both zirconia and alumina catalysts showed deactivation at higher temperatures due to coke deposition, resulting in a strong H2 production drop. Regeneration of catalysts by O2 and steam as well as activation by H2 were also studied. The activated catalyst was able to convert more than 99% naphthalene at 450 °C with a CO and H2 production yield of 26% and 420%, respectively.

The effect of barium substitution on the ferroelectric properties of Sr2 Nb2 O7 Ceramics

This work revealed that the solid solution compounds of Sr 2-xBaxNb2O7 are promising lead-free materials for high-temperature piezoelectric sensor application. These compounds were confirmed as ferroelectric materials with high Curie points (> 900°C) by their piezoelectric activity after poling, ferroelectric domain switching in their P-E hysteresis loops and thermal depoling behavior. The effect of Ba substitution on the structure and properties of Sr 2-xBaxNb2O7 (x < 1.0) was investigated. The solid solution limit of Sr2-xBaxNb 2O7 was determined by XRD as x < 0.6. The a-, b-, c- axes, and cell volume increase with Ba addition. The textured ceramics of Sr2-xBaxNb2O7 were prepared for the first time. The highest d33 was measured as 3.6 ± 0.1 pC/N for Sr1.8Ba0.2Nb2O7. © 2012 The American Ceramic Society.

Femtosecond laser writing of buried waveguides in erbium III-Doped oxyfluoride glasses and nano-glass-ceramics

Femtosecond-pulsed laser writing of waveguides, a few mm long, is demonstrated; waveguides were written orthogonally to the writing beam inside the bulk of ErIII-doped oxyfluoride glasses at a depth of 160 mum. The writing beam was 795 nm wavelength, 54 fs pulse duration and 11 MHz repetition rate. Tracks were written at pulse energies of 13.1 nJ to 26.1 nJ and sample translational velocity of 10 mmmiddot.s-1 to 28 mmmiddots-1. The influence of translational velocity and pulse energy on the cross-sectional shape and integrity of the written tracks is reported. Tracks tend to be narrower as the pulse energy is lowered or translational velocity decreased. Above 22.9 nJ, pulse energy, tracks tend to crack. The estimated refractive index profile of one track has a maximum increase of refractive index of 0.003 at the centre. These glasses normally form nano-glass-ceramics on heat treatment just above the glass transformation temperature (Tg). Here, a post-fs-writing heat-treatment just above Tg causes nano-ceramming of the glass sample and removes a light-guiding peripheral region of the fs-written tracks suggesting that this region may have been fs-modified by stress alone. Waveguiding at 651 nm and 973 nm wavelengths, and upconversion, are demonstrated in optimally written tracks.

Fracture toughness of SIC, Si3N4, and sialon ceramics using controlled surface flaws

Knoop and Vickers indentation cracks have frequently been used as model 'precracks' in ceramic bend specimens for fracture toughness (K1c) determination. Indentation residual stress reduces the measured K1c but can be removed or accounted for by grinding, annealing, or modelling. Values of K1c are obtained for four materials using Vickers indentations and an improved stress intensity factor. Methods for residual stress removal or incorporation are compared, and the most reliable stress removal alternative is identified for each material. © 1996 The Institute of Materials.

Surface and subsurface Vickers indentation cracks in SiC, Si3N4, and sialon ceramics

The nature of subsurface cracks formed under and around Vickers hardness indentations is often assumed rather than identified. Subsurface cracks in four engineering ceramics are revealed using a penetrant technique, and flaw dimensions are recorded. The resulting data are used to investigate several aspects of indentation cracking, such as crack shape, functional relationships between indentation load and flaw dimensions, and the performance of indentation fracture toughness equations. An R curve is constructed for each of the materials. © 1995 The Institute of Materials.

Etching and microstructure of engineering ceramics

Engineering ceramics are often difficult to prepare metallographically because of their hardness, wear resistance and chemical inertness. Two silicon carbides, a silicon nitride and a sialon, are prepared and etched using several different techniques. The most efficient methods are identified. © 1995.

Corrosion of silicon carbide ceramics using conventional and electrochemical methods

Silicon carbide ceramics are candidate materials for use in aggressive environments, including those where aqueous acids are present. Standard corrosion testing methods such as immersion testing are not always sufficiently sensitive for these ceramics owing to the very low, almost unobservable, corrosion rates encountered. Using electrochemical methods the corrosion processes can be assisted, leading to higher rates and thus the elucidation of reaction mechanisms. The behaviour of a sintered and a reaction bonded silicon carbide has been investigated in aqueous HCl, HF, HNO3, and H2SO4, using standard immersion and new electrochemical methods. Both materials were passive in HCl, HNO3, and H2SO4 because of the formation of a surface silica film, and were active in HF. In HF, corrosion of sintered silicon carbide was slight and the residual silicon was removed from reaction bonded specimens.

Conformal sulfated zirconia monolayer catalysts for the one-pot synthesis of ethyl levulinate from glucose

Here we describe a simple route to creating conformal sulphated zirconia monolayers throughout an SBA-15 architecture that confers efficient acid-catalysed one-pot conversion of glucose to ethyl levulinate.

Structure-reactivity correlations in sulphated-zirconia catalysts for the isomerisation of α-pinene

A range of mesoporous sulphated zirconias with tuneable structural and catalytic properties have been prepared by direct impregnation. The surface sulphate coverage can be readily varied, achieving a maximum value of ∼0.2 monolayers. High-temperature calcination induces the crystallisation of tetragonal zirconia while suppressing the monoclinic phase and enhances surface acidity. Superacid sites only appear above a critical threshold SO4 coverage of 0.08 mL (corresponding to 0.44 wt% total S). Sulphated zirconias show good activity towards α-pinene isomerisation of under mild conditions. Conversion correlates with the number Brønsted acid sites, while the selectivity towards mono- versus polycyclic products depends on the corresponding acid site strength; superacidity promotes limonene formation over camphene.

New negative temperature coefficient thermistor ceramics in Mn-doped CaCu3-xMnxTi4O12 (0≤x≤1) system

New negative temperature coefficient (NTC) ceramics based on CaCu 3-xMnxTi4O12 (0≤x≤1) compositions have been investigated. The grain size of the CaCu 3-xMnxTi4O12 samples decreases at first and then increases with increasing Mn content. The X-ray photoelectron spectroscopy analysis corroborates the presence of Mn3+ and Mn 4+ in Mn-doped samples, which results in a decrease in the activation energy. All the NTC thermistors prepared show a linear relationship between the natural logarithm of the resistivity and the reciprocal temperature, indicative of NTC characteristics. The Mn-doped CaCu3-xMnxTi 4O12 NTC thermistors provide various electrical properties, depending on Mn content. The values of ρ25, B constant and activation energy of the NTC thermistors are in the range of 2.22×106-3.22×108 Ω cm, 5488-8031 K, and 0.473-0.692 eV, respectively. © 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.