3 resultados para Viscosity
em Aston University Research Archive
Resumo:
An international round robin study of the viscosity measurements and aging of fast pyrolysis bio-oil has been undertaken recently, and this work is an outgrowth from that effort. Two bio-oil samples were distributed to two laboratories for accelerated aging tests and to three laboratories of long-term aging studies. The accelerated aging test was defined as the change in viscosity of a sealed sample of bio-oil held for 24 h at 80 °C. The test was repeated 10 times over consecutive days to determine the intra-laboratory repeatability of the method. Other bio-oil samples were placed in storage at three temperatures, 21, 5, and -17 °C, for a period of up to 1 year to evaluate the change in viscosity. The variation in the results of the accelerated aging test was shown to be low within a given laboratory. The long-term aging studies showed that storage of a filtered bio-oil under refrigeration can minimize the amount of change in viscosity. The accelerated aging test gave a measure of change similar to that of 6-12 months of storage at room temperature for a filtered bio-oil. Filtration of solids was identified as a key contributor to improving the stability of the bio-oil as expressed by the viscosity based on results of the accelerated aging tests as well as long-term aging studies. Only the filtered bio-oil consistently gave useful results in the accelerated aging and long-term aging studies. The inconsistency suggests that better protocols need to be developed for sampling bio-oils. These results can be helpful in setting standards for use of bio-oil, which is just coming into the marketplace. © 2012 American Chemical Society.
Resumo:
An international round robin study of the stability of fast pyrolysis bio-oil was undertaken. Fifteen laboratories in five different countries contributed. Two bio-oil samples were distributed to the laboratories for stability testing and further analysis. The stability test was defined in a method provided with the bio-oil samples. Viscosity measurement was a key input. The change in viscosity of a sealed sample of bio-oil held for 24 h at 80 °C was the defining element of stability. Subsequent analyses included ultimate analysis, density, moisture, ash, filterable solids, and TAN/pH determination, and gel permeation chromatography. The results showed that kinematic viscosity measurement was more generally conducted and more reproducibly performed versus dynamic viscosity measurement. The variation in the results of the stability test was great and a number of reasons for the variation were identified. The subsequent analyses proved to be at the level of reproducibility, as found in earlier round robins on bio-oil analysis. Clearly, the analyses were more straightforward and reproducible with a bio-oil sample low in filterable solids (0.2%), compared to one with a higher (2%) solids loading. These results can be helpful in setting standards for use of bio-oil, which is just coming into the marketplace. © 2012 American Chemical Society.
Resumo:
The viscosity of four aged bio-oil samples was measured experimentally at various shear rates and temperatures using a rotational viscometer. The experimental bio-oils were derived from fast pyrolysis of beech wood at 450, 500, and 550 °C and Miscanthus at 500 °C (in this work, they were named as BW1, BW2, BW3, and MXG) in a bubbling fluidized bed reactor. The viscosity of all bio-oils was kept constant at various shear rates at the same temperature, which indicated that they were Newtonian fluids. The viscosity of bio-oils was strongly dependent upon the temperature, and with the increase of the temperature from 30 to 80 °C, the viscosity of BW1, BW2, BW3, and MXG decreased by 90.7, 93.3, 92.6, and 90.2%, respectively. The Arrhenius viscosity model, which has been commonly used to represent the temperature dependence of the viscosity of many fluids, did not fit the viscosity-temperature experimental data of all bio-oils very well, especially in the low- and high-temperature regions. For comparison, the Williams-Landel-Ferry (WLF) model was also used. The results showed that the WLF model gave a very good description of the viscosity-temperature relationship of each bio-oil with very small residuals and the BW3 bio-oil had the strongest viscosity-temperature dependence.