The chemistry of ceramic glazes

The development of ideas and theories concerning the structure of glazes, as one of the glassy materials, are reviewed in the general introduction. The raw materials and the manufacturing process for glazes are described (Chapter One). A number of new vanadyl(IV) dipyridylamine and tripyrldylamine complexes have been prepared, various spectroscopic techniques are used in the investigation of the vanadyl ion in a weak ligand field, the situation of those found in a glaze environment (Chapter Three). In glaze recipes containing silica, potash feldspar, china clay, MO(M= Ca, Sr, Sa, Ti and Zn) and NiO, the ligand field theory is used in the elucidation of the effect of M (in MO) on the absorption spectra and coordination behaviour of Ni(II) in glazes. The magnetic and visible spectral results are reviewed in terms of Dietzel's idea of field strength of M and also in terms of Shteinberg's theory of glaze structure. X-ray diffraction is used for the identification of various species that formed after the firing process of glazes (Chapter Four). In Chapter Five, [] Mossbauer spectroscopy, supplemented by E.S.R., X-ray and visible spectral measurements are used in the investigation of iron in a glaze composition similar to that used in Chapter Four. The Mossbauer results are used in following the influence of; M in MO (M= Sr, Ca and Ba), oxides of titanium(IV) and vanadium(V ), and firing conditions on the chemistry of iron. Generally the iron(II) and iron(III) in the fired glazes are in octahedral sites although there are a range of similar, though not identical environments. A quite noticable influence of M (in MO) on the resonance line width is seen. In one case evidence is found for iron(IV) in an iron/vanadium glaze. E.S.R. of vanadium containing glazes indicate that vanadium is present as V02+ in a highly distorted tetragonal environment .

Living cationic polymerization of isobutene

The polymerization of isobutene initiated by 1-chloro-1-phenylethane has been investigated, and molecular weight studies conducted using size exclusion chromatography. Polymerizations carried out in a 40/60 (v/v) mixture of dichloromethaneIcyclohexane, using titanium (IV) chloride as a catalyst in the presence of pyridine at -30 °C were found to be controlled and living. The number average molecular weights of the polymers increased linearly with monomer conversion, and the molecular weight distributions were between 1.15 and 1.20. Efficiencies of initiation were between 80 and 100%, and evidence was found to suggest that backbiting to the initiator had occurred, resulting in the formation of cyclic oligomers during the early stages of polymerization. The kinetics of polymerization can be explained in terms of active species in. equilibrium with dormant species. The effects of temperature. and dielectric constant on this equilibrium were studied and a model based upon the Fuoss equation was developed. Pyridine was found to behave as proton trap in the system, and when it was used in excess the rate of polymerization was retarded. By assuming that the catalyst and pyridine formed a one to one complex, it was possible to show that the reaction was second order with respect to the catalyst. The synthesis of low molecular weight polyisobutenes was studied. When the concentration of initiator was increased relative to that of the isobutene, such that the theoretical degree of polymerization was 20 or less, the rate of initiation was slow compared to propagation. The efficiency of initiation in these polymerizations was typically between 30 and 40 %. Optimal conditions of temperature. and.catalyst concentration were established, leading to a 60 % efficiency of initiation. A one-pot synthesis of phenol end-capped polyisobutene was attempted by adding phenol at the end of a living polymerization. Evidence to substantiate the existence of capped polymer chains in the resultant product was inconclusive. Block copolymerizations of oxetane and isobutene were conducted using 1-chloro-1phenylethane/TiCl4, but no copolymer or oxetane homopolymer could be isolated.

The effect of zinc and titanium on the structure of calcium-sodium phosphate based glass

An array of different structural probes has been used to define the effect of adding Zn and Ti to a sodium-calcium phosphate glass. X-ray absorption spectroscopy at the Zn K-edge suggests that the Zn atoms occupy mixed (4- and 6-fold) sites within the glass matrix. X-ray diffraction reveals a feature at 2.03 angstrom that develops with the addition of Zn and Ti and is consistent with Zn-O and Ti-O near-neighbour distances. Neutron diffraction is used to resolve two distinct P-O distances and highlights the decrease in P center dot center dot center dot P coordination number from 2.0 to 1.7 as the Ti metal concentration rises, which is attributed to the O/P fraction moving away from the metaphosphate value of 3.0 to 3.1 with the addition of Ti. Other correlations, such as those associated with CaO(x) and NaO(x) polyhedra, remain largely unaffected. These results suggest that the network forming P center dot center dot center dot P correlation is most disrupted, with the disorder parameter rising from 0.07 to 0.10 angstrom with the additional modifiers. Zn appears to be introduced into the network as a direct replacement for Ca and causes no structural variation over the composition range studied.

Titanium phosphate glass microspheres for bone tissue engineering

We have demonstrated the successful production of titanium phosphate glass microspheres in the size range of ~10-200 µm using an inexpensive, efficient, easily scalable process and assessed their use in bone tissue engineering applications. Glasses of the following compositions were prepared by melt-quench techniques: 0.5P2O5-0.4CaO-(0.1 - x)Na2O-xTiO2, where x = 0.03, 0.05 and 0.07 mol fraction (denoted as Ti3, Ti5 and Ti7 respectively). Several characterization studies such as differential thermal analysis, degradation (performed using a novel time lapse imaging technique) and pH and ion release measurements revealed significant densification of the glass structure with increased incorporation of TiO2 in the glass from 3 to 5 mol.%, although further TiO2 incorporation up to 7 mol.% did not affect the glass structure to the same extent. Cell culture studies performed using MG63 cells over a 7-day period clearly showed the ability of the microspheres to provide a stable surface for cell attachment, growth and proliferation. Taken together, the results confirm that 5 mol.% TiO2 glass microspheres, on account of their relative ease of preparation and favourable biocompatibility, are worthy candidates for use as substrate materials in bone tissue engineering applications.