Catalyst studies on the ring opening of tetrahydrofuran-dimethanol to 1,2,6-hexanetriol

The metal catalyzed hydrogenolysis of the biomass-derived THF-dimethanol to 1,2,6-hexanetriol using heterogeneous catalysts was investigated. Bimetallic Rh-Re catalysts (4 wt% Rh and a Re/Rh (mol. ratio of 0.5) on a silica support gave the best performance and 1,2,6-hexanetriol was obtained in 84% selectivity at 31% conversion (120 C, 80 bar, 4 h); the selectivity reaches a maximum of 92% at 80 C. The product distribution at prolonged reaction times or higher temperatures or both shows the formation of diols and mono-alcohols, indicating that the 1,2,6-hexanetriol is prone to subsequent hydrodeoxygenation reactions. Different silica supports were investigated and optimal results were obtained with an amorphous silica featuring an intermediate surface area and an average mesopore size of about 6 nm. TPR and XPS surface analysis support the presence of mixed Rh and Re particles. The redox Reδ+/ReTotal surface ratio correlates with the conversion in a volcano type dependency. Both gas phase as well as Rh200Re1OH cluster DFT calculations support an acid-metal bifunctional mechanism and explain the products distribution. © 2013 Elsevier B.V. All rights reserved.

Studies in the anionic polymerization of methyl methacrylate

A study has been made of the anionic polymerization of methyl methacrylate using butyllithium and polystyryl lithium as initiators and using aluminium triisobutyl as a cocatalyst. The aspects of the polymerization that were examined were the effect of changing the order of addition of reagents, the temperature at which polymerization takes place and the polarity of the solvent. Trends were assessed in terms of molecular weight, molecular weight distribution and tacticity. In addition, a second monomer addition test was carried out to verify that the polymerization was truly a living one, and a kinetic study was attempted. Studies to investigate the effect of changing the order of addition of reagents showed that polymer with similar polydispersities and tacticities are produced whether the pre-mixing (mixing initiator and cocatalyst before addition of monomer) or the post-mixing (mixing monomer and cocatalyst before addition of initiator) method were used. However, polymerizations using the post-mixing mixing method demonstrated lower initiator efficiencies, possibly indicating a different initiating species. Investigations into the effect of changing the polymerization temperature show the molecular weight distribution to narrow as the temperature decreases, although a small amount of low molecular weight tailing was also observed at low temperature. A clear relationship between tacticity and temperature was observed with syndiotacticity increasing with decreasing temperature. Changes in solvent polarity were achieved by using mixtures of the standard solvent, toluene, with varying amounts of cyclohexane, tetrahydrofuran or dichloromethane. Experiments at low solvent polarity (using toluene/cyclohexane mixtures) showed problems with initiator solubility but produced polymer with lower polydispersity and higher syndiotacticity than in toluene alone. Experiments using toluene/THF mixtures yielded no polymer, thought to be owing to a side reaction between THF and aluminium triisobutyl. Increased solvent polarity, achieved using toluene/dichloromethane mixtures produced polymer with higher polydispersity and at lower yields than the conventional system, but also with higher syndiotacticity. Second monomer addition reactions demonstrated that the polymerization was 'living' since an increase in molecular weight was observed with no increase in polydispersity. Kinetic studies demonstrated the high speed of the polymerization but yielded no useful data.

The polymerization of lactic acid anhydrosulphite by anionic initiators

This thesis is primarily concerned with the synthesis and polymerization of 5-methyl-1;3, 2-dioxathiolan-4-one-2-oxide (lactic acid anhydrosulphite (LAAS)) using anionic initiators under various conditions. Poly(lactic acid) is a biodegradable polymer which finds many uses in biomedical applications such as drug-delivery and wound-support systems. For such applications it is desirable to produce polymers having predictable molecular weight distributions and crystallinity, The use of anionic initiators offers a potential route to the creation of living polymers. The synthesis of LAAS was achieved by means of an established route though the procedure was modified to some extent and a new method of purification of the monomer using copper oxides was introduced, Chromatographic purification methods were also examined but found to be ineffective. An unusual impurity was discovered in some syntheses and this was identified by means of 1H and 13C NMR, elemental analysis and GC-MS. Since poly-α-esters having hydroxyl-bearing substituents might be expected to have high equilibrium water contents and hence low surface tension characteristics which might aid bio-compatibility, synthesis of gluconic acid anhydrosulphite was also attempted and the product characterised by 1H and 13C NMR. The kinetics of the decomposition of lactic acid anhydrosulphite by lithium tert-butoxide in nitrobenzene has been examined by means of gas evolution measurements. The kinetics of the reaction with potassium tert-butoxide (and also sec-butyl lithium) in tetrahydrofuran has been studied using calorimetric techniques. LAAS was block co-polymerized with styrene and also with 1,3-butadiene in tetrahydrofuran (in the latter case a statistical co-polymer was also produced).

The use of enzyme catalysts in organic media for the synthesis of biodegradable polyesters

The enzyme catalysed polytransesterification of diesters with diols was investigated under various conditions. The most consistent results were obtained using crude porcine pancreatic lipase (PPL) suspended in anhydrous diethyl ether. Addition of molecular sieve to the above system gave higher molecular weight products. The PPL catalysed reaction of bis(2,2,2-trichlorethyl) adipate and glutarate with butane-1,4-diol in anhydrous ether with and without molecular sieve was investigated over a range of times from 8 to 240 hours. The 72 hour adipate reaction with molecular sieve gave the highest molecular weight polymer (Mn 6,500 and Mw 9,400). The glutarate gave the maximum molecular weight polyester after 24 hours (Mn 5,700 and Mw 9,500). Occasionally the glutarate reaction produced very high molecular weight polyester-enzyme complexes. Toluene generally gave lower molecular weight products than diethyl ether. Dichloromethane and tetrahydrofuran gave mainly dimers and trimers. Alternative enzyme and diol systems were also investigated. These yielded no polymeric products. The molecular weights of the polyesters were determined by 1H NMR end-group analysis and by GPC. The molecular weights determined by NMR were on average about twice as great as those determined by GPC. The synthesis of the following diesters is described: i)Bis(2,2,2-trichloroethyl) succinate, glutarate, adipate, trans-3-hexenedioate, and trans-3,4-epoxyadipate. ii) Diphenyl glutarate and adipate.iii)Bis(2,2,2-fluoroethyl) glutarate and trans-3-hexendioate.iv) Divinyl glutarate. v) N,N'Glutaryl dicyclohexanone oxime.The polytransesterification of all the above esters with diols was investigated. The easily synthesised bis(2,2,2-trichloroethyl) glutarate and adipate gave the best results and the work was concentrated on these two esters.

Synthesis and characterization of triazolotriazines

The Dimroth rearrangement in ring-fused 1,2,4-triazoles has been reviewed in detail in Part I and the synthesis of all known triazolo-triazines is described in Part II. Experimental investigations concerned the establishinent of the skeletal arrangement of a variety of triazolotriazines formed by several synthetic routes. Interaction of 3-amino-5-hydrazino-12,4-triazole and benzilafforded 2-amino-6, 7-diphenyl-1, 2,4-triazolo[ 5, 1-c-]-1,2,4-triazine,whereas cyclization of 5,6-diphenyl-3-hydrazino-1,2,4-triazine withcyanogen bromide resulted in the isomeric 3-amino-6,7-diphenyl,-1,2,4-triazolo [4, 3-b]-1,2,4-triazine: both amines were deaminated with amyl nitrite in boiling tetrahydrofuran without rearrangement of the heterocyclic skeleton. 6,7-Diphenyl-1,2,4-triazolo[5,1-cJ-1,2.4-triazine, synthesized from 3-hydrazino-1,2,4-triazole and benzil, formed a covalent hydrate which could be detected spectroscopically in solution, and a covalemt methanolate and ethanolate which could be isolated. A new route to 3-amino-5-hydrazino-pyrazole is described and cyclization to 7-amino-3,4-diphenyl-pyrazolo[ 5,1-.c]-1,2,4-triazine was achieved with benzil. The diazonium nitrate of 3-amino-1,2,4-triazole coupled with ethyl cyanoacetate to yield a mixture of two geometrical isomers of ethyl 2-(2H-1,2,4-triazol-3-ylhydrazono) cyanoacetate.Recrystallization of the crude coupling mixture from aqueous ethanol gave a single hydra-zone which cyclized predominantly to ethyl 7-amino-1,2,4-triazolo[5,1-c]-1,2,4-triazine-6-carboxylate in acid conditions and 6-cyano-1,2,4-triazolo[ 5,1-c]-1,2,4~triazin-7(4H)-one under basic conditions. The nature of the cyclizing medium also controlled the cyclization of .the (pyrazol-ylhydrazono) cyanoacetate hut the corresponding (tetrazol- ylhydrazono) cyanoacetate gave only ethyl 7-aminotetrazolo[ 5,1-cJ-1,2,4- -triazine-6-carboxylate. 2-( 2H-1,2,4-Triazol-3-:ylhydrazono) malonitrile cyclized unambiguously to 7-amino-6-cyano-1,2,4-triazolo-[ 5,1-c]-1,2,4- triazine. Drastic hydrolysis of ethyl 2-(2H-1,2,4-triazol-3-yllhydrazono)-cyanoacetate, ethyl 7-amino-1, 2,4-triazolo[ 5,1-c]-1,2,4-triazine-6-carboxylate, 6-cyano-1,2,4-triazolo[ 5,1-c]-1,2,4-triazin-7{ 4H)-one and 7-amino-6- cyano-1,2,4-triazolo[5,1-c]-1,2,4-triazine gave a hydrate of 1,2,4-triazo1o[5,1-c ]-1,2,4-triazin-7(4H)-one. Mass spectral fragmentations of 7-aminoazolo-[5,1-c]-1,2,4-triazinesconfirm that the azole ring is more stable than the 1,2,4-triazine ring on electron impact.

Electrospinning pH-responsive block copolymer nanofibers

Electrospinng of a fibrous triblock copolymer consisting of poly(methyl methacrylate-block-poly[2-(diethylamino) ethyl methacrylate]-block-poly(methyl methacrylate) (PMMA-b-PDEA-b-PMMA) has been discussed. A mixed co-solvent system of tetrahydrofuran (THF) and dimethylformamide (DMF) was used to electrospin fibrous PMMA-b-PDEA-b-PMMA and its influence on surface morphology and diameter of the electrospun fiber was also investigated in an attempt to control the fiber diameter. The concentration range between 20 and 40 wt % was found suitable for electrospinning of PMMA-b-PDEA-b-PMMA in a THF/DMF system. It was also observed that the average fiber diameter decreased as the content of DMF was increased. A significant decrease in fiber diameter was observed when moving from a THF solution to a THF/DMF system at a ratio of 70:30.

Controlled growth of poly(2-(diethylamino)ethyl methacrylate) brushes via atom transfer radical polymerisation on planar silicon surfaces

Progress in making pH-responsive polyelectrolyte brushes with a range of different grafting densities is reported. Polymer brushes of poly(2-(diethylamino)ethyl methacrylate) were synthesised via atom transfer radical polymerisation on silicon wafers using a 'grafted from' approach. The [11-(2-bromo-2-methyl) propionyloxy]undecyl trichlorosilane initiator was covalently attached to the silicon via silylation, from which the brushes were grown using a catalytic system of copper(I) chloride and pentamethyldiethylenetriamine in tetrahydrofuran at 80°C. X-ray reflectivity was used to assess the initiator surfaces and an upper limit on the grafting density of the polymer was determined. The quality of the brushes produced was analysed using ellipsometry and atomic force microscopy, which is also discussed.