The effects of metallurgical variables on the mechanical properties of high-chromium cast irons

The.use of high-chromium cast irons for abrasive wear resistance is restricted due to their poor fracture toughness properties. An.attempt was made to improve the fracture characteristics by altering the distribution, size and.shape of the eutectic carbide phase without sacrificing their excellent wear resistance. This was achieved by additions of molybdenum or tungsten followed by high temperature heat treatments. The absence of these alloying elements or replacement of them with vanadium or manganese did not show any significant effect and the continuous eutectic carbide morphology remained the same after application of high temperature heat treatments. The fracture characteristics of the alloys with these metallurgical variables were evaluated for both sharp-cracks and blunt notches. The results were used in conjunction with metallographic and fractographic observations to establish possible failure mechanisms. The fracture mechanism of the austenitic alloys was found to be controlled not only by the volume percent but was also greatly influenced by the size and distribution of the eutectic carbides. On the other hand, the fracture mechanism of martensitic alloys was independent of the eutectic carbide morphology. The uniformity of the secondary carbide precipitation during hardening heat treatments was shown to be a reason for consistant fracture toughness results being obtained with this series of alloys although their eutectic carbide morphologies were different. The collected data were applied to a model which incorporated the microstructural parameters and correlated them with the experimentally obtained valid stress intensity factors. The stress intensity coefficients of different short-bar fracture toughness test specimens were evaluated from analytical and experimental compliance studies. The.validity and applicability of this non-standard testing technique for determination of the fracture toughness of high-chromium cast irons were investigated. The results obtained correlated well with the valid results obtained from standard fracture toughness tests.

Fatigue cracking from stress concentration in mild steel

Pulsating; tension fatigue tests have been carried out on edge notched specimens of a mild steel. An electrical potential drop technique was used to determine the number of cycles taken to initiate cracks and the rate at which the cracks grew across the specimen. The results could be described by the range of stress intensity factor, which for crack initiation was modified to take account of the notch root radius. Analysis of elastic stress distributions at cracks and notches and models of plasticity at crack tips are used to discuss the results. Limited evidence in the literature indicates that the fracture mechanics approach may provide a general description of crack initiation and growth in notched specimens, and a simple graphical method of calculating fatigue lives is described. The results are used to illustrate the effects of specimen size and geometry on the fatigue life of notched specimens. The relevance of the work to the assessment of the significance of defects in welds is discussed.

Effect of mean stress on hydrogen assisted fatique crack propagation in duplex stainless steel

Hydrogen assisted subcritical cleavage of the ferrite matrix occurs during fatigue of a duplex stainless steel in gaseous hydrogen. The ferrite fails by a cyclic cleavage mechanism and fatigue crack growth rates are independent of frequency between 0.1 and 5 Hz. Macroscopic crack growth rates are controlled by the fraction of ferrite grains cleaving along the crack front, which can be related to the maximum stress intensity, Kmax. A superposition model is developed to predict simultaneously the effects of stress intensity range (ΔK) and K ratio (Kmin/Kmax). The effect of Kmax is rationalised by a local cleavage criterion which requires a critical tensile stress, normal to the {001} cleavage plane, acting over a critical distance within an embrittled zone at the crack tip. © 1991.

Fatigue of commercial aluminium alloys

Fatigue crack propagation has been observed for a number of commercial aluminium alloys. Comparable data was obtained for a variety of crack and specimen geometries over a range of crack lengths for a given alloy. Where crack propagation only was of interest the initiation event has been excluded by pre-cracking the specimen using a fin of material adjacent to the crack face. By this method a controlled defect size is introduced in to the specimen. By modification of the D.C. potential drop method it has been shown possible to measure the growth of cracking from 0.12mm by this method. Crack growth from defects greater than 0.6mm have been shown to give conventional crack propagation deduced by principle of similitude. Fatigue fracture surface analysis has been conducted for cracking from both free surfaces and from blunt notches. A `quasi cleavage' feature has been identified and is shown to be prominent when the fatigue stress intensity range is below 10 MNm-3/2.

Creep crack growth in cast steam turbine casing steels

The creep rupture properties of cast ½Cr½Mo¼V and 1Cr1Mo¼V alloy steel used in the manufacture of power station steam generating plant. have been investigated. The effects of constraint and geometry on the creep rupture properties are also considered. The validity of various criteria controlling macroscopic creep crack growth in cast CrMoV alloys has been examined. It is found that neither the stress intensity factor nor reference stress correlate satisfactorily the creep crack growth rates at the test temperature of 550°C. Certain minimum displacements must be achieved for crack initiation and propagation. It is found that this displacement as measured by crack opening displacement or crack aspect ratio, is the same in both compact tension and centre-cracked panel geometries, is invariant with crack length and decreases with increasing constraint. The effect of constraint on creep crack growth rate in the two geometries is less conclusive. A new model describing creep crack growth in cast CrMoV alloy steels has been developed. The model is based on the results from a numerical finite element creep analysis of the relaxation and redistribution of stress ahead of an incubating creep crack . It is found that macroscopic creep crack growth in a material undergoing either plane stress or plane strain deformation can be described by a fracture stress which is based on the Von Mises equivalent stress. It has been shown that this model is capable of rationalising all of the experimental crack velocity data from the cast CrMoV alloys. The resultant degree of data correlation is far superior to that obtained when using the stress intensity factor or reference stress. A cumulative damage creep fracture model based upon the results from the numerical analysis has been developed. It is found that the model is capable of predicting the behaviour of propagating creep cracks in cast CrMoV alloys from smooth bar creep rupture data.

Fracture toughness of SIC, Si3N4, and sialon ceramics using controlled surface flaws

Knoop and Vickers indentation cracks have frequently been used as model 'precracks' in ceramic bend specimens for fracture toughness (K1c) determination. Indentation residual stress reduces the measured K1c but can be removed or accounted for by grinding, annealing, or modelling. Values of K1c are obtained for four materials using Vickers indentations and an improved stress intensity factor. Methods for residual stress removal or incorporation are compared, and the most reliable stress removal alternative is identified for each material. © 1996 The Institute of Materials.

Role of reinforcement/matrix interfacial strength in fatigue crack propagation in particulate SiC reinforced aluminum alloy 8090

A study has been made of the influence of the reinforcement/matrix interfacial strength on fatigue crack propagation in a powder metallurgy aluminum alloy 8090-SiC particulate composite. The interfacial region has been altered by two separate routes, the first involving aging of the 8090 matrix, with the subsequent formation of precipitate free zones at the boundaries, and the second consisting of oxidizing the surface of the SiC particles before their incorporation into the composite. In the naturally aged condition, oxidation of the SiC leads to a reduction in fatigue crack growth resistance at higher values of stress intensity range ΔK. This is due to a proportion of the crack growth occurring through voids formed in association with many of the weak SiC interfaces which have retained a layer of thick surface oxide after processing. On overaging no difference in crack growth rate is discernible between the oxidized and unoxidized SiC composites. It is proposed that this is due to similar levels of interfacial weakening having occurred in both composites, indicating that this is an important factor in the reduction of the high ΔK crack growth resistance of the unoxidized SiC composite on aging.

Intrinsic thresholds in polycrystalline Udimet 720

The long crack threshold behaviour of polycrystalline Udimet 720 has been investigated. Faceted crack growth is seen near threshold when the monotonic crack tip plastic zone is contained within the coarsest grain size. At very high load ratios R (=P min/P max) it is possiblefor the monotonic crack tip plastic zone to exceed the coarsest grain size throughout the entire crack growth regime and non1aceted structure insensitive crack growth is then seen down to threshold. Intrinsic threshold values were obtained for non1aceted and faceted crack growth using a constant K max, increasing K min, computer controlled load shedding technique (K is stress intensity factor). Very high R values are obtained at threshold using this technique (0.75-0.95), eliminating closure effects, so the intrinsic resistance of the material to crack propagation is reflected in these values. The intrinsic non1aceted threshold value ΔK th is lower (2.3 MN m -3/2) than the intrinsicfaceted ΔK th value (4.8 MN m -3/2). This is thought to reflect not only the effect of crack branching and deflection (in the faceted case) on the crack driving force, but also the inherent difference in resistance of the material to the two different crack propagation micromechanisms. © 1993 The Institute of Materials.

Fatigue crack propagation in nickel-base superalloys:effects of microstructure, load ratio, and temperature

The current state of knowledge and understanding of the long fatigue crack propagation behavior of nickel-base superalloys are reviewed, with particular emphasis on turbine disk materials. The data are presented in the form of crack growth rate versus stress intensity factor range curves, and the effects of such variables as microstructure, load ratio, and temperature in the near-threshold and Paris regimes of the curves, are discussed.

Temperature effects on fatigue thresholds and structure sensitive crack growth in a nickel-base superalloy

Fatigue thresholds and slow crack growth rates have been measured in a powder formed nickel-base superalloy from room temperature to 600°C. Two grain sizes were investigated: 5-12 μm and 50 μm. It is shown that the threshold increases with grain size, and the difference is most pronounced at room temperature. Although crack growth rates increase with temperature in both microstructures, the threshold is only temperature dependent in the material with the larger grain size. It is also only in the latter that the room temperature threshold falls when the load ratio is increased from 0.1 to 0.5. At 600°C the higher load ratio causes a 20% reduction in the threshold irrespective of grain size. The results are discussed in terms of surface roughness and oxide-induced crack closure, the former being critically related to the type of crystallographic crack growth, which is in turn shown to be both temperature and stress intensity dependent. © 1983.

Short and long fatigue crack growth in a SiC reinforced aluminium alloy

Fatigue crack growth behaviour in a 15 wt% SiC particulate reinforced 6061 aluminium alloy has been examined using pre-cracked specimens. Crack initiation and early growth of fatigue cracks in smooth specimens has also been investigated using the technique of periodic replication. The composite contained a bimodal distribution of SiC particle sizes, and detailed attention was paid to interactions between the SiC particles and the growing fatigue-crack tip. At low stress intensity levels, the proportion of coarse SiC particles on the fatigue surfaces was much smaller than that on the metallographic sections, indicating that the fatigue crack tends to run through the matrix avoiding SiC particles. As the stress intensity level increases, the SiC particles ahead of the growing fatigue crack tip are fractured and the fatigue crack then links the fractured particles. The contribution of this monotonic fracture mode resulted in a higher growth rate for the composite than for the unreinforced alloy. An increase in the proportion of cracked, coarse SiC particles on the fatigue surface was observed for specimens tested at a higher stress ratio.

Effects of crack length and shape on the fracture toughness of a high strength steel 300m

The results of fracture toughness tests on a high strength steel 300m are presented. These results show (i) that in the presence of through-thickness cracks the toughness remains constant down to (a/W)-ratios as low as 0.01 and failure loads up to 0.85σy, and (ii) that the material is more resistant to crack growth when the cracks are semi-elliptical in shape, giving a toughness value which is almost 25 per cent higher than the through-thickness one. Three independent stress analyses are used to obtain stress intensity values for the semi-elliptical cracks and additional confirmation of the increase in toughness comes from stretch zone measurements.

Effects of grain size and microstructure on threshold values and near threshold crack growth in powder-formed Ni-base superalloy

Threshold stress intensity values, ranging from ∼6 to 16 MN m −3/2 can be obtained in powder-formed Nimonic AP1 by changing the microstructure. The threshold and low crack growth rate behaviour at room temperature of a number of widely differing API microstructures, with both ‘necklace’ and fully recrystallized grain structures of various sizes and uniform and bimodal γ′-distributions, have been investigated. The results indicate that grain size is an important microstructural parameter which can control threshold behaviour, with the value of threshold stress intensity increasing with increasing grain size, but that the γ′-distribution is also important. In this Ni-base alloy, as in many others, near threshold fatigue crack growth occurs in a crystallographic manner along {111} planes. This is due to the development of a dislocation structure involving persistent slip bands on {111} planes in the plastic zone, caused by the presence of ordered shearable precipitates in the microstructure. However, as the stress intensity range is increased, a striated growth mode takes over. The results presented show that this transition from faceted to striated growth is associated with a sudden increase in crack propagation rate and occurs when the size of the reverse plastic zone at the crack tip becomes equal to the grain size, independent of any other microstructural variables.

Improved methodology to evaluate fracture properties of warm-mix asphalt using overlay test

This study developed a reliable and repeatable methodology to evaluate the fracture properties of asphalt mixtures with an overlay test (OT). In the proposed methodology, first, a two-step OT protocol was used to characterize the undamaged and damaged behaviors of asphalt mixtures. Second, a new methodology combining the mechanical analysis of viscoelastic force equilibrium in the OT specimen and finite element simulations was used to determine the undamaged properties and crack growth function of asphalt mixtures. Third, a modified Paris's law replacing the stress intensity factor by the pseudo J-integral was employed to characterize the fracture behavior of asphalt mixtures. Theoretical equations were derived to calculate the parameters A and n (defined as the fracture properties) in the modified Paris's law. The study used a detailed example to calculate A and n from the OT data. The proposed methodology was successfully applied to evaluate the impact of warm-mix asphalt (WMA) technologies on fracture properties. The results of the tested specimens showed that Evotherm WMA technology slightly improved the cracking resistance of asphalt mixtures, while foaming WMA technology provided comparable fracture properties. In addition, the study found that A decreased with the increase in n in general. A linear relationship between 2log(A) and n was established.