Ductile fracture mechanisms in a structural steel

Microstructural fracture processes in a BS4360 Grade 50D structural steel with lower sulphur content were studied in smooth tensile specimen tests and Charpy-size bend bar tests. Based on the experimental analysis, an experimental void growth relation with the plastic strain and stress triaxiality and multiplying factor on void growth were determined. Experimental results show that the void growth relation can be reasonably used to estimate the constraint in the specimens containing the notch or crack, also they can be used to evaluate the variations of the stress triaxiality in front of the notch and crack tip under general yielding condition. Side-grooves obviously increase the constraint of the CVN specimens. Strain hardening leads to increasing the stress triaxiality, and decelerating the net void growth. This is especially true for the values of stress triaxiality more than about one. Additionally, the effect of the stress triaxiality on the critical void growth corresponding to the onset of ductile tearing was preliminarily investigated. In this work, a large number of smaller specimens were tested to investigate the ductile-brittle transition behaviour of the structural steel. A void growth rate explanation was suggested for evaluating the temperature transition behaviour. The elastic-plastic fracture tough-ness values based on small specimen tests, such as pre-cracked side-grooved bending specimen and short bar tensile specimen, may give large overestimates of the plane strain fracture toughness.

Hydrogen embrittlement contributions to fatigue crack growth in a structural steel

The detrimental effects of a hydrogen atmosphere on the fatigue resistance of BS 4360 steel have been assessed by a comparison of crack growth rates in air and hydrogen at a low cycling frequency (0.1Hz), and at a number of temperature (25, 50 and 80 °C). The crack propagation rates in air are almost independent of temperature over this range, but those measured in hydrogen differ by more than an order of magnitude between 25 and 80 °C. The greatest enhancement is seen at 25 °C and at high values of ΔK, the maximum occurring between 40–45 MPa √m at each temperature. There is little hydrogen contribution to crack growth at values of ΔK below 20 MPa √m for R = 0.1. The enhancement of crack growth rates is reflected by the presence of ‘quasi-cleavage’ facets on the fatigue fracture surfaces of specimens tested in hydrogen. These are most apparent where the greatest increases in growth rate are recorded. The facets show linear markings, which run both parallel and perpendicular to the direction of crack growth. The former are analogous to the ‘river’ lines noted on brittle cleavage facets, and reflect the propagation direction. The latter are more unusual, and indicate that facet formation by hydrogen embrittlement during fatigue is a step-wise process.

Implications of restructuring and privatisation for competitiveness and perfomance:two Brazilian steel companies

The thesis examines the effects of the privatisation process on productivity, competitiveness and performance in two major Brazilian steel companies, which were privatised in between 1991 and 1993. The case study method was adopted in this research due to its strengths as a useful technique allowing in-depth examination of the privatisation process, the context in which it happened and its effects on the companies. The thesis has developed a company analysis framework consisting of three components: management, competitiveness/productivity and performance and examined the evidence on the companies within this framework.The research indicates that there is no straightforward relationship between privatisation, competitiveness and performance. There were many significant differences in the management and technological capabilities, products and performance of the two companies, and these have largely influenced the effects of privatisation on each company. Company Alpha's strengths in technological and management capabilities and high value added products explain strong productivity and financial performance during and after privatisation. Company Beta's performance was weak before the privatisation and remained weak immediately after. Before the privatisation, weaknesses in management, commodity type low value added products and shortage of funds for investment were the major problems. These were compounded by greater government interference. Despite major restructuring, the poor performance has continued after privatisation largely because the company has not been able to improve its productivity sufficiently to be cost competitive in commodity type markets. Both companies state that their strategies have changed significantly. They claim to be more responsive to market conditions and customers and are attempting to develop closer links with major customers. It is not possible to assess the consequences of these changes in the short time that has elapsed since privatisation but Alpha appears to be more effective in developing a coherent strategy because of its strengths. Both companies accelerated their programme of organisational restructuring and reducing the number of their employees during the privatisation process to improve productivity and performance. Alpha has attained standards comparable to major international steel companies. Beta has had to make much bigger organisational changes and cuts in its labour force but its productivity levels still remain low in comparison with Alpha and international competitors.

Nonmetallic inclusion modification and its effect on the final properties of a linepipe steel

Five linepipe type steels were produced in order to study the effect of calcium and magnesium injection on their final properties. Two of these steels were at the extremes of the sulphide range i.e. 0.003 and 0.017% sulphur with no injection attempted; thereby, providing standards to compare with the injected steels. The oxygen level varied from 21 to 63 p.p.m. The cast ingots were controlled-rolled and isothermally rolled in order to study the deformation characteristics of the residual non-metallic inclusions. The structure and cleanliness of these steels was evaluated metallographically using the light microscope, SEM, and image analysis and the results related to their Charpy toughness and HIC resistance. Increasing sulphur levels decreased final properties of the steel. In the untreated state, with as little as 0.003% sulphur, test orientation was highly influential. Modification of sulphur bearing steels was achieved with low modifying element to sulphur ratios provided that the oxygen content was very low. Injection of calcium into steel caused interaction with oxide and sulphide inclusions which was biased toward oxide reduction relative to sulphur removal. Magnesium again reduced oxides and appeared to be linked with aluminia containing inclusions in the final product. It produced improved toughness values relative to a similar sulphur containing calcium treated steel. The results of this work could be extended to establish the mechanism of inclusion modification with magnesium additions to sulphur bearing steels.

A knowledge-based system for process planning in a seamless steel tube plant

The thesis describes the work carried out to develop a prototype knowledge-based system 'KBS-SETUPP' to generate process plans for the manufacture of seamless tubes. The work is specifically related to a plant in which hollows are made from solid billets using a rotary piercing process and then reduced to required size and finished properties using the fixed plug cold drawing process. The thesis first discusses various methods of tube production in order to give a general background of tube manufacture. Then a review of the automation of the process planning function is presented in terms of its basic sub-tasks and the techniques and suitability of a knowledge-based system is established. In the light of such a review and a case study, the process planning problem is formulated in the domain of seamless tube manufacture, its basic sub-tasks are identified and capabilities and constraints of the available equipment in the specific plant are established. The task of collecting and collating the process planning knowledge in seamless tube manufacture is discussed and is mostly fulfilled from domain experts, analysing of existing manufacturing records specific to plant, textbooks and applicable Standards. For the cold drawing mill, tube-drawing schedules have been rationalised to correspond with practice. The validation of such schedules has been achieved by computing the process parameters and then comparing these with the drawbench capacity to avoid over-loading. The existing models cannot be simulated in the computer program as such, therefore a mathematical model has been proposed which estimates the process parameters which are in close agreement with experimental values established by other researchers. To implement the concepts, a Knowledge-Based System 'KBS- SETUPP' has been developed on Personal Computer using Turbo- Prolog. The system is capable of generating process plans, production schedules and some additional capabilities to supplement process planning. The system generated process plans have been compared with the actual plans of the company and it has been shown that the results are satisfactory and encouraging and that the system has the capabilities which are useful.

Structural behaviour and design of load-bearing falsework

Tne object of this research was to investigate the behaviour of birdcage scaffolding as used in falsework structures, assess the suitability of existing design methods and make recommendations for a set of design rules. Since excessive deflection is as undesirable in a structure as total collapse, the project was divided into two sections. These were to determine the ultimate vertical and horizontal load-carrying capacity and also the deflection characteristics of any falsework. So theoretical analyses were developed to ascertain the ability of both the individual standards to resist vertical load, and of the bracing to resist horizontal load.Furthermore a model was evolved which would predict the horizontal deflection of a scaffold under load using strain energy methods. These models were checked by three series of experiments. The first was on individual standards under vertical load only. The second series was carried out on full scale falsework structures loading vertically and horizontally to failure. Finally experiments were conducted on scaffold couplers to provide additional verification of the method of predicting deflections. This thesis gives the history of the project and an introduction into the field of scaffolding. It details both the experiments conducted and the theories developed and the correlation between theory and experiment. Finally it makes recommendations for a design method to be employed by scaffolding designers.

The structural properties of glassfibre reinforced plastics

The research work described in this thesis is concerned with the development of glassfibre reinforced plastics for structural uses in Civil Engineering construction. The first stage was primarily concerned with the design of GRP lamintes with structura1 properties and method of manufacture suitable for use with relatively large structural components. A cold setting, pressure moulding technique was developed which proved to be efficient in reducing the void content in the composite and minimising the exothermic effect due to curing. The effect of fibre content and fibre arrangement on strength and stiffness of the cornposite was studied and the maximum amount of' fibre content that could be reached by the adopted type of moulding technique was determined. The second stage of the project was concerned with the introduction of steel-wire "sheets" into the GRP cornposites, to take advantage of the high modulus of steel wire to improve the GRP stiffness and to reduce deformation. The experimental observations agreed reasonably well with theoretical predictions in both first and second stages of the work. The third stage was concerned with studying the stability of GRP flat rectangular plates subjected to uniaxial compression or pure shear, to simulate compression flanges or shear webs respectively. The investigation was concentrated on the effect of fibre arrangement in the plate on buckling load. The effect of the introduction of steel-wire sheets on the plate stability in compression was also investigated. The boundary conditions were chosen to be close to those usually assumed in built-up box-sections for both compression flanges and webs. The orthotropic plate and the mid-plane symmetric were used successfully in predicting the buckling load theoretically. In determining the buckling load experimentally, two methods were used. The Southwell plot method and electrical strain gauge method. The latter proved to be more reliable in predicting the buckling load than the former, especially for plates under uniaxial compression. Sample design charts for GRP plates that yield and buckle simultaneously under compression are also presented in the thesis. The final stage of the work dealt with the design and test of GRP beams. The investigation began by finding the optimum cross-section for a GRP beam. The cross-section which was developed was a thin walled corrugated section which showed higher stiffness than other cross-sections for the same cross-sectional area (i.e. box, I, and rectangular sections). A cold setting, hand layings technique was used in manufacturing these beams wbich were of nine types depending on the type of glass reinforcement employed and the arrangement of layers in the beam. The simple bending theory was used in the beam design and proved to be satisfactory in predicting the stresses and deflections. A factor of safety of 4 was chosen for design purposes and considered to be suitable for long term use under static load. Because of its relatively low modulus, GRP beams allowable deflection was limited to 1/120th of the span which was found to be adequate for design purposes. A general discussion of the behaviour of GRP composites and their place relative to the more conventional structural material was also presented in the thesis.

Structural limits and teachers' perspectives

This thesis is about the relationship between schooling and the economic and political structures which constrain its institutional framework. It focusses on teachers, as mediators of structural constraints, and on middle schools, as institutions which occupy a functionally transitional place between the primary and secondary traditions. In approaching the problem of linking the different perspectives of macro and micro sociologies, I argue the view that the individual mediates the contradictions between the socially cooperative processes of production and the competitive individualism which legitimates the private appropriation of wealth and income. The link is observable in the schooling process as a pattern of contradictions and tensions mediated by the rhetoric of equality of opportunity. In order to elucidate the link, the processes within the boundaried institutions must be viewed in the context of those changing tensions within the state administrative systems, which reverberate into schools as economic and political constraints. Framed within the ideology of the Flowden Report (1967), middle schooling was set within a discourse which stressed cooperative relationships rather than competitive standards. Since the mid-1970s, administrative policies have heightened the competitive battle for declining resources and attacked the Plowden ideology. Focussing the fieldwork on six middle schools in one local authority, T use an eclectic methodology to relate economic and political policies, generated in the state administrative system, to the situation in the schools between 1979 and 1981. The methodology incorporates a time dimension in order to highlight the tensions as they play upon teachers' changing definitions of the changing situation. I conclude that the intersubjective socio-cultural relations of schooling cannot be properly explained without making explicit the changing tensions in the rule/resource relationships which teachers mediate through their particular institutions.

The formulation of artificial reference standards for use within the ELISPOT assay

Whether to assess the functionality of equipment or as a determinate for the accuracy of assays, reference standards are essential for the purposes of standardisation and validation. The ELISPOT assay, developed over thirty years ago, has emerged as a leading immunological assay in the development of novel vaccines for the assessment of efficacy. However, with its widespread use, there is a growing demand for a greater level of standardisation across different laboratories. One of the major difficulties in achieving this goal has been the lack of definitive reference standards. This is partly due to the ex vivo nature of the assay, which relies on cells being placed directly into the wells. Thus, the aim of this thesis was to produce an artificial reference standard using liposomes, for use within the assay. Liposomes are spherical bilayer vesicles with an enclosed aqueous compartment and therefore are models for biological membranes. Initial work examined pre-design considerations in order to produce an optimal formulation that would closely mimic the action of the cells ordinarily placed on the assay. Recognition of the structural differences between liposomes and cells led to the formulation of liposomes with increased density. This was achieved by using a synthesised cholesterol analogue. By incorporating this cholesterol analogue in liposomes, increased sedimentation rates were observed within the first few hours. The optimal liposome formulation from these studies was composed of 2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC), cholesterol (Chol) and brominated cholesterol (Brchol) at a 16:4:12 µMol ratio, based on a significantly higher (p<0.01) sedimentation (as determined by a percentage transmission of 59 ± 5.9 % compared to the control formulation at 29 ± 12 % after four hours). By considering a range of liposome formulations ‘proof of principle’ for using liposomes as ELISPOT reference standards was shown; recombinant IFN? cytokine was successfully entrapped within vesicles of different lipid compositions, which were able to promote spot formation within the ELISPOT assay. Using optimised liposome formulations composed of phosphatidylcholine with or without cholesterol (16 µMol total lipid) further development was undertaken to produce an optimised, scalable protocol for the production of liposomes as reference standards. A linear increase in spot number by the manipulation of cytokine concentration and/or lipid concentrations was not possible, potentially due to the saturation that occurred within the base of wells. Investigations into storage of the formulations demonstrated the feasibility of freezing and lyophilisation with disaccharide cryoprotectants, but also highlighted the need for further protocol optimisation to achieve a robust reference standard upon storage. Finally, the transfer of small-scale production to a medium lab-scale batch (40 mL) demonstrated this was feasible within the laboratory using the optimised protocol.

The deoxidation of steel with simple and complex deoxidisers

The deoxidation of steel with complex deoxidisers was studied at 1550°C and compared with silicon, aluminium and silicon/aluminium alloys as standards. The deoxidation alloy systems, Ca/Si/Al, Mg/Si/Al and Mn/Si/Al, were chosen for the low liquidus temperatures of many of their oxide mixtures and the potential deoxidising power of their constituent elements. Product separation rates and compositional relationships following deoxidation were examined. Silicon/aluminium alloy deoxidation resulted in the product compositions and residual oxygen contents expected from equilibrium and stoichiometric considerations, but with the Ca/Si/Al and Mg/Si/Al alloys the volatility of calcium and magnesium prevented them participating in the final solute equilibrium, despite their reported solubility in liquid iron. Electron-probe microanalysis of the products showed various concentrations of lime and magnesia, possibly resulting from reaction between the metal vapours and dissolved oxygen.The consequent reduction of silica activity in the products due to the presence of CaO and hgO produced an indirect effect of calcium and magnesium on the residual oxygen content. Product separation rates, indicated by vacuum fusion analyses, were not significantly influenced by calcium and magnesium but the rapid separation of products having a high Al2O3Si02 ratio was confirmed. Manganese participated in deoxidation, when present either as an alloying element in the steel or as a deoxidation alloy constituent. The compositions of initial oxide products were related to deoxidation alloy compositions. Separated products which were not alumina saturated, dissolved crucible material to achieve saturation. The melt equilibrated with this slag and crucible by diffusion to determine the residual oxygen content. MnO and SiO2 activities were calculated, and the approximate values of MnO deduced for the compositions obtained. Separation rates were greater for products of high interfacial tension. The rates calculated from a model based on Stoke's Law, showed qualitative agreement with experimental data when corrected for coalescence effects.

The influence of a coal gasifier atmosphere on fatigue crack growth rates in BS 4360 steel

Fatigue crack growth tests have been carried out in a number of gaseous environments in order to assess their effects on the crack propagation resistance of BS 4360 grade 50EE, a weldable structural steel. Crack growth rates at 25 °C are up to 20 times higher in hydrogen than in air, but there is no effect when hydrogen is present as a 30% constituent of a simplified product gas (SPG). Indeed, crack growth rates in such a mixture are slightly lower than those measured in air, being comparable with those observed in an inert environment. The other gases present in the SPG are CO, CO2 and CH4, and it is probable that the carbon monoxide is responsible for nullifying the embrittling effects of hydrogen, by preferentially adsorbing on to the surface of the steel and thus blocking hydrogen entry. Experimental observations suggest that oxygen has the same effect when small quantities are allowed to diffuse into a non-flowing hydrogen environment around a propagating crack. The results are encouraging in terms of the suitability of conventional structural steels such as BS 4360 for gas plant applications. The gas mixtures present in such an environment would not have the severe detrimental effects on fatigue crack growth resistance which result from the presence of 'pure' hydrogen. © 1993.