Results of the IEA round Robin on viscosity and aging of fast pyrolysis bio-oils:long-term tests and repeatability

An international round robin study of the viscosity measurements and aging of fast pyrolysis bio-oil has been undertaken recently, and this work is an outgrowth from that effort. Two bio-oil samples were distributed to two laboratories for accelerated aging tests and to three laboratories of long-term aging studies. The accelerated aging test was defined as the change in viscosity of a sealed sample of bio-oil held for 24 h at 80 °C. The test was repeated 10 times over consecutive days to determine the intra-laboratory repeatability of the method. Other bio-oil samples were placed in storage at three temperatures, 21, 5, and -17 °C, for a period of up to 1 year to evaluate the change in viscosity. The variation in the results of the accelerated aging test was shown to be low within a given laboratory. The long-term aging studies showed that storage of a filtered bio-oil under refrigeration can minimize the amount of change in viscosity. The accelerated aging test gave a measure of change similar to that of 6-12 months of storage at room temperature for a filtered bio-oil. Filtration of solids was identified as a key contributor to improving the stability of the bio-oil as expressed by the viscosity based on results of the accelerated aging tests as well as long-term aging studies. Only the filtered bio-oil consistently gave useful results in the accelerated aging and long-term aging studies. The inconsistency suggests that better protocols need to be developed for sampling bio-oils. These results can be helpful in setting standards for use of bio-oil, which is just coming into the marketplace. © 2012 American Chemical Society.

NOx storage-reduction characteristics of Ba-based lean NOx trap catalysts subjected to simulated road aging

In order to study the effect of washcoat composition on lean NOx trap (LNT) aging characteristics, fully formulated monolithic LNT catalysts containing varying amounts of La-stabilized CeO2 (5 wt% La2O3) or CeO2-ZrO2 (Ce:Zr = 70:30) were subjected to accelerated aging on a bench reactor. Subsequent catalyst evaluation revealed that aging resulted in deterioration of the NOx storage, NOx release and NOx reduction functions, whereas the observation of lean phase NO2 slip for all of the aged catalysts indicated that LNT performance was not limited by the kinetics of NO oxidation. After aging, all of the catalysts showed increased selectivity to NH3 in the temperature range 250–450 °C. TEM, H2 chemisorption, XPS and elemental analysis data revealed two main changes which can explain the degradation in LNT performance. First, residual sulfur in the catalysts, present as BaSO4, decreased catalyst NOx storage capacity. Second, sintering of the precious metals in the washcoat was observed, which can be expected to decrease the rate of NOx reduction. Additionally, sintering is hypothesized to result in segregation of the precious metal and Ba phases, resulting in less efficient NOx spillover from Pt to Ba during NOx adsorption, as well as decreased rates of reductant spillover from Pt to Ba and reverse NOx spillover during catalyst regeneration. Spectacular improvement in LNT durability was observed for catalysts containing CeO2 or CeO2-ZrO2 relative to their non-ceria containing analog. This was attributed to (i) the ability of ceria to participate in NOx storage/reduction as a supplement to the main Ba NOx storage component; (ii) the fact that Pt and CeO2(-ZrO2) are not subject to phase segregation; and (iii) the ability of ceria to trap sulfur, resulting in decreased sulfur accumulation on the Ba component.

Upgrading of fast pyrolysis oils by hot filtration

A hot filtration unit downstream of a 1kg/h fluidised bed fast pyrolysis reactor was designed and built. The filter unit operates at 450oC and consists of 1 exchangeable filter candle with reverse pulse cleaning system. Hot filtration experiments up to 7 hours were performed with beech wood as feedstock. It was possible to produce fast pyrolysis oils with a solid content below 0.01 wt%. The additional residence time of the pyrolysis vapours and secondary vapour cracking on the filter cake caused an increase of non-condensable gases at the expense of organic liquid yield. The oils produced with hot filtration showed superior quality properties regarding viscosity than standard pyrolysis oils. The oils were analysed by rotational viscosimetry and gel permeation chromatography before and after accelerated aging. During filtration the separated particulates accumulate on the candle surface and build up the filter cake. The filter cake leads to an increase in pressure drop between the raw gas and the clean gas side of the filter candle. At a certain pressure drop the filter cake has to be removed by reverse pulse cleaning to regenerate the pressure drop. The experiments showed that successful pressure drop recovery was possible during the initial filtration cycles, thereafter further cycles showed minor pressure drop recovery and therefore a steady increase in differential pressure. Filtration with pre-coating the candle to form an additional layer between the filter candle and cake resulted in total removal of the dust cake.

Effect of thermal and mechanical processing on tensile properties of powder formed 2124 aluminium and 2124 Al-SiC p metal matrix composite

The aging responses of 2124 Al-SiC p metal matrix composite (MMC) and unreinforced matrix alloy are studied and related to variations in tensile properties. The MMC is aged from Wo starting conditions: (i) stretched and naturally aged and (ii) re-solution treated. Accelerated aging occurs in both MMC conditions compared with unreinforced alloy. Tensile strengths and elastic moduli are improved in the MMC compared with the alloy, but ductility is reduced. Stretched MMC exhibits higher strength but lower ductility and modulus than re-solutioned MMC. The re-solutioned MMC fails by microvoid coalescence in low aging conditions, and by void nucleation and shear in high aging conditions. Failure of the stretched MMC initiates at the surface at specimen shoulders, illustrating the increased notch sensitivity of this condition, and propagates via a zigzag shear fracture mode. Zigzag facet size increases on gross aging. Particle fracture occurs during tensile failure, but also before testing as a result of the manufacturing process. © 1995 The Institute of Materials.