Chemical reactions of double bonds in activated carbon:microwave and bromination methods

The reaction of localised C=C bonds on the surface of activated carbons has been shown to be an effective method of chemical modification especially using microwave-assisted reactions.

Enzyme catalysed modification of polymers

The aim of this project was to investigate the enzyme catalysed modification of synthetic polymers. It was found that an immobilised lipase from Candida antartica (Novozyme 435) catalysed the selective epoxidation of poly(butadiene) in the presence of hydrogen peroxide and catalytic quantities of acetic acid. The cis and trans double bonds of the backbone were epoxidised in yields of up to 60 % whilst the pendent vinyl groups were untouched. The effect of varying a number of reaction parameters was investigated. These studies suggested that higher yields of epoxide could not be obtained because of the conformational properties of the partially epoxidised polymer. Application of this process to the Baeyer-Villiger reaction of poly(vinyl phenyl ketone) and poly(vinyl methyl ketone) were unsuccessful. The lack of reactivity was found to be a property of the polymer rather than the enzymatic system employed. Attempts to modify hydroxyl containing polymers and polymers bearing active esters close to the polymer backbone were unsuccessful. Steric factors appear to be the most important influence on the outcome of the reactions.

Biodegradable polyanhydrides as drug delivery systems

Polyanhydrides are useful biodegradable vehicles for controlled drug delivery. In aqueous media the breaking of the anhydride bonds resulting in gradually polymer fragments collapse and release drugs in a controlled manner. In this study, two new biodegradable polyanhydrides copolymers were synthesised using a melt-polycondensation method. The first is poly (bis (p-carboxyphenoxy)-2-butene-co-sebacic acid) (CP2B: SA), which has double bonds along the polymer backbone. The second is crosslinked poly (glutamic acid-sebacic acid-co-sebacic acid) (GluSA: SA), where the conjugated unit of glutamic acid with sebacic acid (glutamic acid-SA) acted as a crosslinking fragment in producing the crosslinking polymer. The two polymers were applied to preparation of microspheres with bovine serum albumin (BSA) as a model protein, using both double emulsion solvent evaporation and spray drying methods. The characterisation of the microspheres, morphology, particle size, and drug loading, was studied. The in vitro hydrolytic degradation of polymers and blank microspheres was monitored using IR, GPC, and DSC. In vitro drug release behaviour was also studied. Though the studies showed cleavages of anhydride bonds occurred rapidly (<5 days), bulks of the polymer microspheres could be observed after a few weeks to a month; and only around 10-35% of the protein was detectable in a four-week period in vitro. We found the pH of the medium exerts a large impact on the release of the protein from the microspheres. The higher the pH, the faster the release. Therefore the release of the protein from the polyanhydride microspheres was pH-sensitive due mainly to the dissolution of monomers from the microspheres.

Effect of contact surfaces on the thermal and photoxidation of dehydrated castor oil

The effect of stainless steel, glass, zirconium and titanium enamel surfaces on the thermal and photooxidative toughening mechanism of dehydrated castor oil films deposited on these surfaces was investigated using different analytical and spectroscopic methods. The conjugated and non-conjugated double bonds were identified and quantified using both Raman spectroscopy and 1D and 2D NMR spectroscopy. The disappearance of the double bonds in thermally oxidised oil-on-surface films was shown to be concomitant with the formation of hydroperoxides (determined by iodometric titration). The type of the surface had a major effect on the rate of thermal oxidation of the oil, but all of the surfaces examined had resulted in a significantly higher rate of oxidation compared to that of the neat oil. The highest effect was exhibited by the stainless steel surface followed by zirconium enamel, titanium enamel and glass. The rate of thermal oxidation of the oil-on-steel surface (at 100 °C, based on peroxide values) was more than five times faster than that of oil-on-glass and more than 21 times faster than the neat oil when compared under similar thermal oxidative conditions. The rate of photooxidation at 60 °C of oil-on-steel films was found to be about one and half times faster than their rate of thermal oxidation at the same temperature. Results from absorbance reflectance infrared microscopy with line scans taken across the depth of thermally oxidised oil-on-steel films suggest that the thermal oxidative toughening mechanism of the oil occurs by two different reaction pathways with the film outermost layers, i.e. furthest away from the steel surface, oxidising through a traditional free radical oxidation process involving the formation of various oxygenated products formed from the decomposition of allylic hydroperoxides, whereas, in the deeper layers closer to the steel surface, crosslinking reactions predominate.

Thermo-oxidative stabilization of poly(lactic acid) with antioxidant intercalated layered double hydroxides

Two antioxidant modified layered double hydroxides (AO-LDHs) were successfully prepared by theintercalation of 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (IrganoxCOOH) and 6-hydroxy-2,5,7,8-tetramethylchroman-2-carboxylic acid (Trolox) in the layered structure of LDH. It was foundthat by anchoring the phenolic moieties to the LDH layers the antioxidant power is retained in the caseof Trolox, and even amplified in the case of IrganoxCOOH. A small amount of the two AO-LDHs wasincorporated into poly(lactic acid), PLA, by solution mixing and melt extrusion. The thermo-oxidativestability of the composites was compared with that of the neat PLA and PLA containing free AOs. SECanalysis indicates that, after a controlled period of ageing, both the AO-LDHs protect the PLA fromchain scission. The oxidation induction time (OIT, DSC) at 230 °C shows also the beneficial effects ofthe presence of the functional filler in the polymer matrix. Further, results from a preliminary migrationtest suggest that the AO species have a low tendency to migrate away from the AO-LDHs embedded inthe polymer matrix thus keeping the AO protected inside the nanofiller layers thereby remaining activefor a longer time.