Some aspects of the microbiological properties of polymers and composite materials

The interaction of microorganisms with glass-reinforced polyester resins(GRP), both under laboratory and simulated operating conditions, has been examined following reports of severl! fungal biodeterioration. Although GRP was not previously associated with substantial microbial growth, small amounts of microbial activity would pose problems for products associated with comestible materials. The microbiology of the raw materials was investigated, two ingredients were supportive to microbial populations whilst five materials were biostatic or inhibitory in their action. Production laminate was not susceptible to microbial deterioration or inhibitory to microbes. Incorporation of zinc stearate, one of the supportive ingredients, at 300% manufacturing level or drastic undercuring produced laminate capable of supporting microbial growth but only after a non-biotic stage of degradation. Study of the long-term population dynamics of cisterns of GRP and competitive materials under conditions simulating in-service conditions, monitoring microbial numbers within the experimental vessels and comparing with the populations of the supply water, suggests that the performance of GRP cisterns is slightly superior to conventional competitive materials. An investigation of the biological performance of GRP cisterns in an isolated area of known microbiological hazard was conducted. Severe biodeterioration had been experienced with Preform GRP articles moulded using different production techniques, but substitution of current GRP articles resulted in no recurrence of the problem. All attempts to establish the fungal isolate responsible for the phenomena in cisterns under controlled conditions failed. Scanning Electron Microscopy of GRP surfaces showed that although differences exist between current and Preform laminates, these could not satisfactorily explain the differences in service behaviour. These results and the results of the British Plastics Federation Expert Working Group interlaboratory study are discussed in relation to the original report of gross fungal biodeterioration and, to the design of future testing programmes for the products of industrial concerns.

Reliability of fibre Bragg gratings in polymer optical fibre

In this paper we report on investigations of some of the factors that have a bearing on the reliability and repeatability of polymer fibre Bragg gratings. The main issues discussed are the fibre preform composition, the fibre drawing conditions and the thermal history of the fibre grating.

Thermal effects on the photoelastic coefficient of polymer optical fibers

We measure the radial profile of the photoelastic coefficient C(r) in single-mode polymer optical fibers (POFs), and we determine the evolution of C(r) after annealing the fibers at temperatures from 40°C to 80°C. We demonstrate that C(r) in the fibers drawn from a preform without specific thermal pre-treatment changes and converges to values between 1.2 and 1.6×10-12 Pa-1 following annealing at 80°C. The annealed fibers display a smoothened radial profile of C(r) and a lowered residual birefringence. In contrast, the mean value of C(r) of the fiber drawn from a preform that has been pre-annealed remains constant after our annealing process and is significantly higher, i.e., 4×10-12 Pa-1. The annealing process decreases the residual birefringence to a lower extent as well. These measurements indicate the impact of annealing on the thermal stability of the photoelastic coefficient of POFs, which is an essential characteristic in view of developing POF-based thermomechanical sensors.