Effect of the temperature on the composition of lignin pyrolysis products

The temperature dependence of the pyrolysis products of two types of lignin (Alcell lignin and Asian lignin) was investigated using pyrolysis-gas chromatography-mass spectrometry (PyGC-MS). About 50 compounds were identified and quantified for each type of lignin over a temperature range of 400-800C. The maximum yield of phenolic compounds was obtained at 600C for both lignins, which was 17.2% for Alcell lignin and 15.5% for Asian lignin. Most of the phenolic compounds had an individual yield of less than 1%; however, for Alcell lignin, 5-hydroxyvanillin was the highest yield at 4.29 wt%on dry ash-free lignin, and for Asian lignin, 2-methoxy-4-vinylphenol was the highest yield at 4.15 wt % on dry ash-free lignin.

The effect of the environment on the mechanical properties of medical grade silicones

Silicone spacers have been in use as replacement joints in the human hand for over 30 years. Since they were first used there has been a number of designs all of which have had problems with fracture. This may be due to a defect in the material caused during implantation, or by bony intrusions within the arthritic hand after implantation. The aim of this research was to investigate the effect of the environment on the mechanical properties of medical grade silicones used for human implantation. The materials were subjected to static tensile testing after various forms of ageing. The environmental conditions included temperatures of 37 and 80°C and the environments of Ringer's solution, distilled water, and air. The environmental conditions employed resulted in reduced mechanical strength with ageing time of the silicones. This research supports the view that failure of silicone implants in the hand could be partly attributed to the effects of environmental ageing of the material.