Photochemical degradation of polystyrene

In this work the oxidative degradation of pure polystyrene, polybutadiene and butadiene-modified polystyrene (normally called high impact polystyrene or HIPS) have been studied using a variety of physical and chemical techniques. The changes in dynamic-mechanical properties occurring during the ultra-violet light accelerated weathering of these polymers were followed by a visco-elastometric technique (Rheovibron) in the solid phase over a wide temperature range. Selective cross-linking of the polybutadiene in high-impact polystyrene caused the depression of the low temperature damping peak (tan d) with a corresponding sharp peak in tan d at ambient temperature accompanied by an integral rise in complex modulus. During the same period of photoxidation, the hydroperoxide concentration and gel content increased rapidly, reaching a maximum before decomposing photolytically with the destruction of unsaturation and with the formation of stable oxidation products. Infra-red spectroscopy showed the formation of carbonyl and hydroxyl groups. a,ß-unsaturated carbonyl was also identified and was formed by decomposition of both allylic hydroperoxide and initial peroxidic gel by ß-scission of the graft between polybutadiene and polystyrene. With further photoxidation a more stable ether gel was formed involving the destruction of the conjugating double bond of a,ß-unsaturated carbonyl. Addition of saturated and unsaturated ketones which are potential sensitisers of photoxidation to high-impact polystyrene and polybutadiene failed to photo-initiate the oxygen absorption of the polymers. A prior thermal oxidative treatment on the other hand eliminated the auto- accelerating stage leading to linear kinetics as the concentration of thermally-produced hydroperoxide approached a maximum. Antioxidants which act by destroying hydroperoxide lengthened the induction period to rapid oxygen absorption, whilst a phenolic antioxidant behaved as a weak photo-activator initially and a retarder later. Prior photolysis of high-impact polystyrene photo-activated the unsaturated component and caused similar changes in dynamic-mechanical properties to those found during photoxidation although at a much lower rate. Polybutadiene behaves as a photo-pro-oxidant for the destruction of polystyrene in high-impact polystyrene.

The behaviour of antioxidants in polyolefins under conditions of U.V. exposure

The effects of antioxidants and stabilizers on the oxidative degradation of polyolefins (low density polyethylene [LDPE] and polypropylene [PPJ have been studied after subjecting to prior high temperature processing treatments. The changes in the both chemical and physical properties of unstabilized polymers occurring during processing were found to be strongly dependent on the amount of oxygen present in the mixer. Subsequent thermal and photo-oxidation showed very similar characteristics and the chromophore primarily responsible for:both thermo and photooxidative degradation of unstabilized polymers was found to be hydroperoxide formed during processing. Removal of hydroperoxide by heat treatment in an inert atmosphere although increasing ketonic carbonyl concentration, markedly decreased the rate of photo-oxidation, introducing an induction period similar to that of an unprocessed sample. It was concluded that hydroperoxides are the most important initiators in normally processed polymers during the early stages of photo-oxidation. Antioxidants such as metal dithiocarbamates which act by destroying peroxides into non-radica1 products were found to be efficient melt stabilizers for polyolefins and effective UV stabilizers during the initial photo-oxidation stage, whilst a phenolic antioxidant, n-octadecyl-3-(3',5'-di-terbutyl 4'hydroxypheny1) propionate (Irganox 1076) retarded photo-oxidation rate in the later stages. A typical 'UV absorber' 2-hydroxy-4-octyloxy-benzophenone (HOBP) has a minor thermal antioxidant action but retarded photo-oxidation at all stages. A substituated piperidine derivative, Bis [2.2.6.6-tetramethylpiperidlnyl-4] sebacate (Tinuvin 770) behaved as an pro-oxidant during thermal oxidation of polyolefins but was an effective stabilizer against UV light. The UV absorber, HOBP synergised effectively with both peroxide decomposing antioxidants (metal dithiocarbamates) and a chain-breaking antioxidant (Irganox 1076) during photo-oxidation of the poymers studed whereas the combined effect was additive during thermal oxidation. By contrast, the peroxide decornposers and chain-breaking antioxidant (Irganox 1076) which were effective synergists during thermal oxidation of LDPE· were antagonistic during photo-oxidation. The mechanisms of these processes are discussed.

The antioxidant role of vitamin E in polyolefins

Polymers are subject to oxidation throughout their lifecycle. Antioxidants are generally incorporated in polymers to inhibit or minimise oxidative degradation. Hindered phenolic antioxidants are important stabilisers for polyolefins. However, hindered phenols undergo chemical transformations while performing their antioxidant function during processing and fabrication. In addition, antioxidants are subject to loss from polymers during processing, or subsequently in-service. Migration of antioxidants is a major concern in applications involving polymers in direct contact with food and human environment. This concern is compounded by the realisation that very little is known about the nature and the migration behaviour of antioxidant transformation products. In this work, the antioxidant role of the biological antioxidant -tocopherol (Vitamin E) , which is structurally similar to many synthetic hindered phenols, is investigated in low density polyethylene (LDPE) and polypropylene (PP). The melt stabilising effectiveness of -tocopherol (Toc) was found to be very high, higher than that of commercial hindered phenol antioxidants, such as Irganox 1076 (Irg 1076) and Irganox 1010 (Irg 1010), after multiple extrusions, especially at very low concentrations. The high antioxidant activity of Toc was shown to be due, at least in part, to the formation of transformation products during processing. The main products formed are stereoisomers of dimers and trimers, as well as aldehydes and a quinone - the relative concentration of each was shown to depend on the processing severity, the initial antioxidant concentration and oxygen availability. These transformation products are shown to impart better, similar or lower melt stability to the polymer than the parent antioxidant. The nature of the products formed from Toc during processing was compared with those formed during processing of Irg 1076 and Irg 1010 with LDPE and a mechanism for the melt stabilisation of Toc was proposed and compared with the stabilisation mechanisms of the synthetic antioxidants Irg 1076 and Irg 1010.

Thermo-oxidative stabilization of poly(lactic acid) with antioxidant intercalated layered double hydroxides

Two antioxidant modified layered double hydroxides (AO-LDHs) were successfully prepared by theintercalation of 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (IrganoxCOOH) and 6-hydroxy-2,5,7,8-tetramethylchroman-2-carboxylic acid (Trolox) in the layered structure of LDH. It was foundthat by anchoring the phenolic moieties to the LDH layers the antioxidant power is retained in the caseof Trolox, and even amplified in the case of IrganoxCOOH. A small amount of the two AO-LDHs wasincorporated into poly(lactic acid), PLA, by solution mixing and melt extrusion. The thermo-oxidativestability of the composites was compared with that of the neat PLA and PLA containing free AOs. SECanalysis indicates that, after a controlled period of ageing, both the AO-LDHs protect the PLA fromchain scission. The oxidation induction time (OIT, DSC) at 230 °C shows also the beneficial effects ofthe presence of the functional filler in the polymer matrix. Further, results from a preliminary migrationtest suggest that the AO species have a low tendency to migrate away from the AO-LDHs embedded inthe polymer matrix thus keeping the AO protected inside the nanofiller layers thereby remaining activefor a longer time.