Hydrodebromination of bromobenzene over Pt(111)

The surface chemistry of benzene and bromobenzene over Pt(111) has been studied by temperature-programmed XPS/MS and NEXAFS. Time-resolved XPS shows that benzene adopts a single chemically distinguishable environment during low-temperature adsorption within the monolayer, with a saturation coverage at θC6H6 = 0.2 ML. Around 20% of a benzene monolayer desorbs molecularly, while the remainder dehydrogenates to surface carbon. Bromobenzene likewise adsorbs molecularly at 90 K, giving rise to two C 1s environments at 284.4 and 285.3 eV corresponding to the C−H and C−Br functions, respectively. The saturation C6H5Br monolayer coverage is 0.11 ML. NEXAFS reveals that bromobenzene adopts a tilted geometry, with the ring plane at 60 ± 5° to the surface. Bromobenzene multilayers desorb at ∼180 K, with higher temperatures promoting competitive molecular desorption versus C−Br scission within the monolayer. Approximately 30% of a saturated bromobenzene monolayer either desorbs reversibly or as reactively formed hydrocarbons. Debromination yields a stable (phenyl) surface intermediate and atomic bromine at 300 K. Further heating results in desorption of reactively formed H2, C6H6, and HBr; however, there was no evidence for either biphenyl or Br2 formation. Pt(111) is an efficient surface for low-temperature bromobenzene hydrodebromination to benzene and HBr. © 2007 American Chemical Society.

Sulfate-enhanced catalytic destruction of 1,1,1-trichlorethane over Pt(111)

The catalytic destruction of 1,1,1-trichloroethane (TCA) over model sulfated Pt(111) surfaces has been investigated by fast X-ray photoelectron spectroscopy and mass spectrometry. TCA adsorbs molecularly over SO4 precovered Pt(111) at 100 K, with a saturation coverage of 0.4 monolayer (ML) comparable to that on the bare surface. Surface crowding perturbs both TCA and SO4 species within the mixed adlayer, evidenced by strong, coverage-dependent C 1s and Cl and S 2p core-level shifts. TCA undergoes complete dechlorination above 170 K, accompanied by C−C bond cleavage to form surface CH3, CO, and Cl moieties. These in turn react between 170 and 350 K to evolve gaseous CO2, C2H6, and H2O. Subsequent CH3 dehydrogenation and combustion occurs between 350 and 450 K, again liberating CO2 and water. Combustion is accompanied by SO4 reduction, with the coincident evolution of gas phase SO2 and CO2 suggesting the formation of a CO−SOx surface complex. Reactively formed HCl desorbs in a single state at 400 K. Only trace (<0.06 ML) residual atomic carbon and chlorine remain on the surface by 500 K.

Fast x-ray spectroscopy study of ethene on clean and SO4 precovered Pt{111}

The adsorption and decomposition of ethylene over a Pt{111} single crystalsurface has been investigated by fast x-ray spectroscopy. At 100 K ethene displays precursor-mediated adsorption kinetics, adopting a single environment with a saturation C2H4 coverage of 0.25 ML and binding energy of 283.2 eV. Thermal decomposition proceeds above 240 K via dehydrogenation to ethylidyne with an activation barrier of 57±3 kJ mol−1 and preexponential factor ν=1×1010±0.5 s−1. Site-blocking by preadsorbed SO4 reduces the saturation ethene coverage but induces a new, less reactive π-bonded ethene species centered around 283.9 eV, which in turn decomposes to ethylidyne at 350 K.

A fast XPS study of sulphate promoted propene decomposition over Pt{111}

SO2 oxidation has been followed by Fast XPS over Pt{111}. Preadsorbed oxygen reduces the low temperature saturation coverage of SO2 with respect to the clean surface. Heating a mixed O2/SO2 adlayer results in efficient oxidation of both upright and flat-lying SO2 molecules to surface-bound SO4. Sulphate decomposes above room temperature liberating gas-phase SO2 and SO3. Propene adsorbs molecularly at 100 K over clean Pt{111} and dehydrogenates above 250 K to form a stable propylidyne adlayer, which in turn decomposes above 400 K to form graphitic carbon. Preadsorbed surface sulphate enhances the sticking probability of propene via formation of an alkyl-sulphate complex. Thermal decomposition of this complex accounts for low temperature propene combustion and is accompanied by atomic sulpur deposition. Propylidyne forms as on clean Pt but is less reactive undergoing partial oxidation above 450 K with residual surface oxygen.

A fast XPS study of propene decomposition over clean and sulphated Pt{111}

The thermal decomposition of propene over clean and sulphate precovered Pt{111} has been followed by Fast XPS. The saturation propene coverage over the clean surface is 0.21 mL at 90 K. Propene is stable up to 200 K, above which molecular desorption and dehydrogenation result in the formation of a stable propylidyne intermediate adlayer at 300 K. Propylidyne decomposes above 400 K eventually forming graphitic carbon above 800 K. Preadsorbed surface sulphate promotes room temperature propene combustion associated with the decomposition of a thermally unstable alkyl--sulphate complex. Propylidyne also forms as on clean Pt{111}, but is less reactive, its decomposition above 450 K triggering partial oxidation with residual surface oxygen to liberate gas phase CO.

An investigation of support effects on the Pt-catalysed selective transformation of α,β-unsaturated substrates

Pt catalyst series were prepared on mesoporous SBA-15, SBA-16, KIT-6, true liquidcrystal-templated meso-macroporous SBA-15 and a commercial, low surface area silicasupport. Support structure can be easily fabricated using surfactant templating as a mode ofstringent control on porosity, surface area and internal structure. The impact of varying Pt-support physicochemical properties was systematically studied for the selective transformation of allylic substrates under chemoselective oxidation and hydrogenation regimes, a class of reactions highly applicable to industry. Pt-based heterogeneous catalysts are well-known for their utilisation in the hydrogenation of α,β-unsaturated aldehydes,although the mode of action and lack of systematic studies in the literature fuels continuing debate into the role of Pt nanoparticles and support choice for this area. This project attempts to shed some light on several frequently asked questions in this field. Successful support synthesis and stability after Pt impregnation is confirmed through HRTEM, XRD and N2 porosimetry. Decreasing metal loading promoted dispersion values,regardless of support choice, with surface PtO2 content also showing visible enhancement.Increasing support surface area and mesoporosity exhibited the following trend on Pt dispersion augmentation; low surface area commercial silica < true liquid crystal-templated SBA-15 < SBA-15 < SBA-16 ~ KIT-6. For the selective oxidation of cinnamyl alcohol,increasing PtO2 surface population confers substantial rate enhancements, with turnover frequencies evidencing PtO2 to be the active species .In the Pt-catalysed hydrogenation of cinnamaldehyde, strong support insensitivity was observed towards catalytic activity; as turnover frequencies normalised to Pt metal reveal constant values. However, structure sensitivity to the desired unsaturated alcohol arose,evidencing the requirement of flat, extended Pt (111) facets for C=O hydrogenation. Pt/SBA-15 proved the most selective, reflecting suppressed cinnamyl alcohol hydrogenation, with DRIFTS and in-situ ATR-IR evidencing the key role of support polarity in re-orientation of cinnamaldehyde to favour di-σCO adsorption and C=O versus C=C hydrogenation. High pressures increased activity, whilst a dramatic shift in selectivity from dominant C=C (1 bar)to C=O hydrogenation (10 bar) was also observed, attributed to surface crowding and suppression of di-σCC and η4 di-σCO+πC=C cinnamaldehyde binding modes.

Direct observation of extremely low temperature catalytic dehydrochlorination of 1,1,1-trichloroethane over platinum

Fast X-ray photoelectron spectroscopy reveals that the efficient catalytic destruction of 1,1,1-trichloroethane occurs over Pt{111} surfaces at temperatures as low as 150 K. Decomposition occurs via rapid, sequential C-Cl bond scission to form an alkylidyne surface intermediate that in turn dehydrogenates above room temperature. Atomic chlorine liberated during dehydrochlorination undergoes efficient reaction with surface hydrogen, resulting in the evolution of gaseous HCl and small amounts of ethane, presumably via ethylidyne hydrogenation. Irreversible dehydrogenation of residual hydrocarbon fragments results in significant surface coking above 500 K.