Polymer PCF Bragg grating sensors based on poly(methyl methacrylate) and TOPAS cyclic olefin copolymer

Fibre Bragg grating (FBG) sensors have been fabricated in polymer photonic crystal fibre (PCF). Results are presented using two different types of polymer optical fibre (POF); first multimode PCF with a core diameter of 50µm based on poly(methyl methacrylate) (PMMA) and second, endlessly single mode PCF with a core diameter of 6µm based on TOPAS cyclic olefin copolymer. Bragg grating inscription was achieved using a 30mW continuous wave 325nm helium cadmium laser. Both TOPAS and PMMA fibre have a large attenuation of around 1dB/cm in the 1550nm spectral region, limiting fibre lengths to no longer than 10cm. However, both have improved attenuation of under 10dB/m in the 800nm spectral region, thus allowing for fibre lengths to be much longer. The focus of current research is to utilise the increased fibre length, widening the range of sensor applications. The Bragg wavelength shift of a grating fabricated in PMMA fibre at 827nm has been monitored whilst the POF is thermally annealed at 80°C for 7 hours. The large length of POF enables real time monitoring of the grating, which demonstrates a permanent negative Bragg wavelength shift of 24nm during the 7 hours. This creates the possibility to manufacture multiplexed Bragg sensors in POF using a single phase mask in the UV inscription manufacturing. TOPAS holds certain advantages over PMMA including a much lower affinity for water, this should allow for the elimination of cross-sensitivity to humidity when monitoring temperature changes or axial strain, which is a significant concern when using PMMA fibre.

Photosensitivity mechanism of undoped poly(methyl methacrylate) under UV radiation at 325 nm and its spatial resolution limit

In this Letter, we provide evidence suggesting that the main photosensitive mechanism of an undoped poly(methyl methacrylate)-based microstructured optical fiber under UV radiation at 325 nm is a competitive process of both photodegradation and polymerization. We found experimentally that increasing strain during photo-inscription leads to an increased photosensitivity, which is evidence of photodegradation. Likewise, refractive index change in the fiber was measured to be positive, which provides evidence for further polymerization of the material. Finally, we relate the data obtained to the spatial recording resolution of the samples. © 2014 Optical Society of America.

Humidity responsivity of poly(methyl methacrylate)-based optical fiber Bragg grating sensors

The humidity response of poly(methyl methacrylate) (PMMA)-based optical fiber Bragg gratings (POFBGs) has been studied. The characteristic wavelength of the grating is modulated by water absorption-induced swelling and refractive index change in the fiber. This work indicates that anisotropic expansion may exist in PMMA optical fiber, reducing the humidity responsivity of the grating and introducing uncertainty in the responsivity from fiber to fiber. By pre-straining a grating, one can get rid of this uncertainty and simultaneously improve the POFBG response time. © 2014 Optical Society of America.

Synthesis, self-assembly and (absence of) protein interactions of poly(glycerol methacrylate)-silicone macro-amphiphiles

The present study focuses on the synthesis of amphiphilic block copolymers containing poly(glycerol monomethacrylate) (PGMMA), showing the advantages of a protection/deprotection strategy based on silyl groups. PGMMA blocks were synthesized via ATRP started by a double functional poly(dimethyl siloxane) (PDMS) macroinitiator of molecular weight ≈7000 g mol-1. The resulting triblock copolymers were characterized by low polydispersity (generally ≤1.1) and their aggregation concentration in water was essentially dominated by the PDMS block length (critical aggregation concentration substantially invariant for GMMA degree of polymerization ≥30). For GMMA blocks with DP > 50, the self-assembly in water produced 35-50 nm spherical micelles, while shorter hydrophilic chains produced larger aggregates apparently displaying worm-like morphologies. Block copolymers with long GMMA chains (DP ≈ 200) produced particularly stable micellar aggregates, which were then selected for a preliminary assessment of the possibility of adsorption of plasma proteins (albumin and fibrinogen); using diffusion NMR as an analytical technique, no significant adsorption was recorded both on micelles and on soluble PGMMA employed as a control, indicating the possibility of a "stealth" behaviour. This journal is © 2013 The Royal Society of Chemistry.

Poly(methyl methacrylate) model study of optical surface quality after excimer laser photorefractive keratectomy

Purpose: To evaluate lenses produced by excimer laser ablation of poly(methyl methacrylate) (PMMA) plates. Setting: University research laboratory. Methods: Two Nidek EC-5000 scanning-slit excimer laser systems were used to ablate plane-parallel plates of PMMA. The ablated lenses were examined by focimetry, interferometry, and mechanical surface profiling. Results: The spherical optical powers of the lenses matched the expected values, but the cylindrical powers were generally lower than intended. Interferometry revealed marked irregularity in the surface of negative corrections, which often had a positive “island” at their center. Positive corrections were generally smoother. These findings were supported by the results of mechanical profiling. Contrast sensitivity measurements carried out when observing through ablated lenses whose power had been neutralized with a suitable spectacle lens of opposite sign confirmed that the surface irregularities of the ablated lenses markedly reduced contrast sensitivity over a range of spatial frequencies. Conclusion: Improvements in beam delivery systems seem desirable.

Direct observation of morphological development during the spin-coating of polystyrene-poly(methyl methacrylate) polymer blends

We present results of the direct observation, in real-space, of the phase separation of high molecular weight polystyrene and poly(methyl methacrylate) from ortho-xylene using our newly developed technique of high speed stroboscopic interference microscopy. Taking a fixed concentration (3 wt % in o-xylene) at a fixed composition (1:4 by weight) and by varying the rotational rate during the spin-coating process, we are able to observe the formation of a range of phase separated bicontinuous morphologies of differing length-scales. Importantly, we are able to show that the mechanism by which the final phase separated structure is formed is through domain coarsening when rich in solvent, before vitrification occurs and fixes the phase separated structure. The ability to directly observe morphological development offers a route toward controlling the length-scale of the final morphology through process control and in situ feedback, from a single stock solution. © 2013 Wiley Periodicals, Inc.

Enhancing the sensitivity of poly(methyl methacrylate) based optical fiber Bragg grating temperature sensors

In poly(methyl methacrylate) (PMMA)-based optical fiber gratings (POFBGs), the temperature response is determined by thermal expansion and the thermo-optic effect of the fiber. Because thermal expansion introduces a positive change and the thermo-optic effect introduces a negative change in the Bragg wavelength of the POFBG, they cancel out each other to some extent, leading to reduced and varying temperature sensitivity. By pre-straining a POFBG, the contribution of thermal expansion can be removed, and, consequently, the temperature sensitivity of POFBG can be greatly enhanced. Theoretical analysis also indicates a reduced thermo-optic coefficient of POFBG due to restrained linear expansion that matches experimental results.

The suitability of biodegradable poly(dl-lactide-co-glycolide)75:25 microspheres for the sustained release of antibiotics

Post-operative infections resulting from total hip arthroplasty are caused by bacteria such as Staphylococcus aureus and Pseudomonas aeruginosa entering the wound perioperatively or by haemetogenous spread from distant loci of infection. They can endanger patient health and require expensive surgical revision procedures. Gentamicin impregnated poly (methyl methacrylate) bone cement is traditionally used for treatment but is often removed due to harbouring bacterial growth, while bacterial resistance to gentamicin is increasing. The aim of this work was to encapsulate the antibiotics vancomycin, ciprofloxacin and rifampicin within sustained release microspheres composed of the biodegradable polymer poly (dl-lactide-co-glycolide) [PLCG] 75:25. Topical administration to the wound in hydroxypropylmethylcellulose gel should achieve high local antibiotic concentrations while the two week in vivo half life of PLCG 75:25 removes the need for expensive surgical retrieval operations. Unloaded and 20% w/w antibiotic loaded PLCG 75:25 microspheres were fabricated using a Water in Oil emulsification with solvent evaporation technique. Microspheres were spherical in shape with a honeycomb-like internal matrix and showed reproducible physical properties. The kinetics of in vitro antibiotic release into newborn calf serum (NCS) and Hank's balanced salt solution (HBSS) at 37°C were measured using a radial diffusion assay. Generally, the day to day concentration of each antibiotic released into NCS over a 30 day period was in excess of that required to kill St. aureus and Ps. auruginosa. Only limited microsphere biodegradation had occurred after 30 days of in vitro incubation in NCS and HBSS at 37°C. The moderate in vitro cytotoxicity of 20% w/w antibiotic loaded microspheres to cultured 3T3-L1 cells was antibiotic induced. In conclusion, generated data indicate the potential for 20% w/w antibiotic loaded microspheres to improve the present treatment regimens for infections occurring after total hip arthroplasty such that future work should focus on gaining industrial collaboration for commercial exploitation.

An XPS study of pulsed plasma polymerised allyl alcohol film growth on polyurethane

The growth of highly functionalised poly allyl alcohol films by pulsed plasma polymerisation of CH2 double bond; length as m-dashCHCH2OH on biomedical grade polyurethane has been followed by X-ray photoelectron spectroscopy (XPS) and contact angle measurements. Film thickness is observed to increase approximately linearly with plasma modification time, suggesting a layer-by-layer growth mode of poly allyl alcohol. Water contact angle measurements reveal the change in the surface free energy of wetting decreases linearly with plasma modification up to the monolayer point after which a constant limiting value of −24 mJ m−2 was attained. Films prepared at 20 W plasma power with a duty cycle of 10 μs:500 μs exhibit a high degree of hydroxyl (single bondOH) retention with minimal fragmentation of the monomer observed. Increasing the plasma power up to 125 W is found to improve single bondOH retention at the expense of ether formation generating films close to the monomer stoichiometry. Duty cycle plays an important role in controlling both film composition and thickness, with longer off times increasing single bondOH retention, while longer on times enhance allyl alcohol film growth.

Strain and temperature sensitivity of a single mode polymer optical fiber

We have measured the optical phase sensitivity of fiber based on poly(methyl methacrylate) under near-single-mode conditions at 632.8 nm wavelength. The elongation sensitivity is 131±3×105 rad m-1 and the temperature sensitivity is -212±26 rad m-1 K-1. These values are somewhat larger than those for silica fiber and are consistent with the values expected on the basis of the bulk polymer properties.

Measurements of stress-optic coefficient in polymer optical fibers

We have systematically measured the differential stress-optic coefficient, ?C, in a number of poly(methyl methacrylate) (PMMA) fibers drawn with different stress, ranging from 2 up to 27 MPa. ?C was determined in transverse illumination by measuring the dependence of birefringence on additional axial stress applied to the fiber. Our results show that ?C in PMMA fibers has a negative sign and ranges from -4.5 to -4.5×10-12 Pa-1, depending on the drawing stress. Increase of the drawing stress results in greater initial fiber birefringence and lower ?C.

Water diffusion into UV inscripted long period grating in microstructured polymer fibre

A long period grating was photoinscribed step-by-step in microstructured poly(methyl methacrylate) fiber for the first time using a continuous wave HeCd laser at 325 nm, irradiating the fiber with a power of 1 mW. The grating had a length of 2 cm and a period of 1 mm. A series of cladding mode coupling resonances were observed throughout the spectral region studied of 600 to 1100 nm. The resonance wavelengths were shown to be sensitive to the diffusion of water into the fiber.

Quantifying hydrogel response using laser light scattering

The pH and counter-ion response of a microphase separated poly(methyl methacrylate)-block-poly(2-(diethylamino)ethyl methacrylate)-block-poly(methyl methacrylate) hydrogel has been investigated using laser light scattering on an imprinted micron scale topography. A quartz diffraction grating was used to create a micron-sized periodic structure on the surface of a thin film of the polymer and the resulting diffraction pattern used to calculate the swelling ratio of the polymer film in situ. A potentiometric titration and a sequence of counter ion species, taken from the Hofmeister series, have been used to compare the results obtained using this novel technique against small angle X-ray scattering (nanoscopic) and gravimetric studies of bulk gel pieces (macroscopic). For the first time, the technique has been proven to be an inexpensive and effective analytical tool for measuring hydrogel response on the microscopic scale.

Effect of the Hofmeister anions upon the swelling of a self-assembled pH-responsive hydrogel

We report the effect of a range of monovalent sodium salts on the molecular equilibrium swelling of a simple synthetic microphase separated poly(methyl methacrylate)-block-poly(2-(diethylamino)ethyl methacrylate)-block-poly(methyl methacrylate) (PMMA88-b-PDEA223-b-PMMA88) pH-responsive hydrogel. Sodium acetate, sodium chloride, sodium bromide, sodium iodide, sodium nitrate and sodium thiocyanate were selected for study at controlled ionic strength and pH; all salts are taken from the Hofmeister series (HS). The influence of the anions on the expansion of the hydrogel was found to follow the reverse order of the classical HS. The expansion ratio of the gel measured in solutions containing the simple sodium halide salts (NaCl, NaBr, and NaI) was found to be strongly related to parameters which describe the interaction of the ion with water; surface charge density, viscosity coefficient, and entropy of hydration. A global study which also included nonspherical ions (NaAce, NaNO3 and NaSCN) showed the strongest correlation with the viscosity coefficient. Our results are interpreted in terms of the Collins model,(1) where larger ions have more mobile water in the first hydration cage immediately surrounding the gel, therefore making them more adhesive to the surface of the stationary phase of the gel and ultimately reducing the level of expansion.