Co3O4 nanostructures with a high rate performance as anode materials for lithium-ion batteries, prepared via book-like cobalt-organic frameworks

The self-assembly of cobalt coordination frameworks (Co-CPs) with a two-dimensional morphology is demonstrated by a solvothermal method. The morphology of the Co-CPs has been controlled by various solvothermal conditions. The two-dimensional nanostructures agglomerated by Co3O4 nanoparticles remained after the pyrolysis of the Co-CPs. The as-synthesized Co3O4 anode material is characterized by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge measurements. The morphology of Co3O4 plays a crucial role in the high performance anode materials for lithium batteries. The Co3O4 nanoparticles with opened-book morphology deliver a high capacity of 597 mA h g-1 after 50 cycles at a current rate of 800 mA g-1. The opened-book morphology of Co3O4 provides efficient lithium ion diffusion tunnels and increases the electrolyte/Co3O4 contact/interfacial area. At a relatively high current rate of 1200 mA g-1, Co3O4 with opened-book morphology delivers an excellent rate capability of 574 mA h g-1.

Synthesis and characterization of some carbon based nanostructures

Carbon thin films were synthesized using the original Thermionic Vacuum Arc (TVA) method. Mechanical properties were investigated using Micro Materials NanoTest 500 instrument using a NT Berkovich indenter. XPS provides a quantitative analysis of the surface composition and X-ray generated Auger electron spectroscopy (XAES) performed by Thermoelectron ESCALAB 250 revealed information about the sp3:sp2 ratio of the carbon bondings. Structure and morphology was studied by Transmission Electron Microscope CM120ST, providing information on the grain size distribution of the crystalline diamond structures. © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Electrocatalytic regeneration of atmospherically aged MoS2 nanostructures via solution-phase sulfidation

The performance of MoS2 as a hydrogen evolution catalyst is diminished by exposure to air. We demonstrate a solution phase technique to resulfidate MoSxO2-x using Na2S2O3. The success of the method was judged by performance as a H+ reduction catalyst. Following sulfidation samples displayed a favourable decrease in both onset potential and Tafel slope, with the best decreasing from -0.23 V to -0.18 V (vs. SHE), and 282 mV dec-1 to 87 mV dec-1 respectively. Ageing studies indicate that this method may be used to recycle the MoS2 repeatedly without losing catalytic performance, although repeated sulfidation did result in homogenisation of the nanostructure.

Synthesis and characterization of some carbon based nanostructures

The aim of present paper is to present the latest results on investigations of the carbon thin film deposited by Thermionic Vacuum Arc (TVA) method and laser pyrolysis. X-ray photoelectron spectroscopy (XPS) and X-ray generated Auger electron spectroscopy (XAES) were used to determine composition and sp2 to sp3 ratios in the outer layers of the film surfaces. The analyses were conducted in a Thermoelectron ESCALAB 250 electron spectrometer equipped with a hemispherical sector energy analyser. Monochromated Al K X-radiation was employed for the XPS examination, at source excitation energy of 15 KeV and emission current of 20 mA. Analyzer pass energy of 20 eV with step size of 0.1 eV and dwell time of 100 ms was used throughout. © 2010 SPIE.

Large scale fabrication of nitrogen vacancy-embedded diamond nanostructures for single-photon source applications

Some color centers in diamond can serve as quantum bits which can be manipulated with microwave pulses and read out with laser, even at room temperature. However, the photon collection efficiency of bulk diamond is greatly reduced by refraction at the diamond/air interface. To address this issue, we fabricated arrays of diamond nanostructures, differing in both diameter and top end shape, with HSQ and Cr as the etching mask materials, aiming toward large scale fabrication of single-photon sources with enhanced collection efficiency made of nitrogen vacancy (NV) embedded diamond. With a mixture of O2 and CHF3 gas plasma, diamond pillars with diameters down to 45 nm were obtained. The top end shape evolution has been represented with a simple model. The tests of size dependent single-photon properties confirmed an improved single-photon collection efficiency enhancement, larger than tenfold, and a mild decrease of decoherence time with decreasing pillar diameter was observed as expected. These results provide useful information for future applications of nanostructured diamond as a single-photon source.