A general one-pot strategy for the synthesis of high-performance transparent-conducting-oxide nanocrystal inks for all-solution-processed devices

For all-solution-processed (ASP) devices, transparent conducting oxide (TCO) nanocrystal (NC) inks are anticipated as the next-generation electrodes to replace both those synthesized by sputtering techniques and those consisting of rare metals, but a universal and one-pot method to prepare these inks is still lacking. A universal one-pot strategy is now described; through simply heating a mixture of metal-organic precursors a wide range of TCO NC inks, which can be assembled into high-performance electrodes for use in ASP optoelectronics, were synthesized. This method can be used for various oxide NC inks with yields as high as 10 g. The formed NCs are of high crystallinity, uniform morphology, monodispersity, and high ink stability and feature effective doping. Therefore, the inks can be readily assembled into films with a surface roughness of 1.6 nm. Typically, a sheet resistance of 110 Ω sq-1 can be achieved with a transmittance of 88%, which is the best performance for TCO NC ink-based electrodes described to date. These electrodes can thus drive a polymer light-emitting diode (PLED) with a luminance of 2200 cdm-2 at 100 mA cm-2.

Synthesis and evaluation of novel ligands for quantum dot stabilisation and polymerisation studies

This thesis describes the design and synthesis of a variety of functionalised phosphine oxides and sulfides, based on the structure of trioctylphosphine oxide, synthesised for the purpose of surface modification of quantum dots. The ability of the ligands to modify the surface chemistry via displacement of the original hexadecylamine capping layer of quantum dots was evaluated. Finally the surface modified quantum dots were investigated for enhancement in their inherent properties and improved compatibility with the various applications for which they were initially designed. Upon the commencement of research involving quantum dots it became apparent that more information on their behaviour and interaction with the environment was required. The limits of the inherent stability of hexadecylamine capped quantum dots were investigated by exposure to a number of different environments. The effect upon the stability of the quantum dots was monitored by changes in the photoluminescence ability of their cores. Subtle differences between different batches of quantum dots were observed and the necessity to account for these in future applications noted. Lastly the displacement of the original hexadecylamine coating with the "designer" functionalised ligands was evaluated to produce a set of conditions that would result in the best possible surface modification. A general procedure was elucidated however it was discovered that each displacement still required slight adjustment by consideration of the other factors such as the difference in ligand structure and the individuality of the various batches of quantum dots. This thesis also describes a procedure for the addition of a protective layer to the surface of quantum dots by cross-linking the functionalised ligands bound to the surface via an acyclic diene metathesis polymerisation. A detailed description of the problems encountered in the analysis of these materials combined with the use of novel techniques such as diffusion ordered spectroscopy is provided as a means to overcome the limitations encountered. Finally a demonstration of the superior stability, upon exposure to a range of aggressive environments of these protected materials compared with those before cross-linking provided physical proof of the cross-linking process and the advantages of the cross-linking modification. Finally this thesis includes the presentation of initial work into the production of luminescent nanocrystal encoded resin beads for the specific use in solid phase combinatorial chemistry. Demonstration of the successful covalent incorporation of quantum dots into the polymeric matrices of non-functionalised and functionalised resin beads is described. Finally by preliminary work to address and overcome the possible limitations that may be encountered in the production and general employment of these materials in combinatorial techniques is given.

Dynamic restructuring of Pd nanoparticles and single crystals during catalytic selective alcohol oxidation

The aerobic selective oxidation (selox) of alcohols represents an environmentally benign and atom efficient chemical valorisation route to commercially important allylic aldehydes, such as crotonaldehyde and cinnamaldehyde, which find application in pesticides, fragrances and food additives. Palladium nanoparticles are highly active and selective heterogeneous catalysts for such oxidative dehydrogenations, permitting the use of air (or dioxygen) as a green oxidant in place of stoichiometric chromate permanganate saltsor H2O2. Here we discuss how time-resolved, in-situ X-ray spectroscopies (XAS and XPS) reveal dynamic restructuring of dispersed Pd nanoparticles and Pd single-crystals in response to changing reaction environments, and thereby identify surface PdO as the active species responsible for palladium catalysed crotyl alcohol selox (Figure 1); on-stream reduction to palladium metal under oxygen-poor regimes thus appears the primary cause of catalyst deactivation. This insight has guided the subsequent application of surfactant-templating and inorganic nanocrystal methodologies to optimize the density of desired active PdO sites for the selective oxidation of natural products such as sesquiterpenoids.