Cu and Fe oxides dispersed on SBA-15:a Fenton type bimetallic catalyst for N,N-diethyl-p-phenyl diamine degradation

A bimetallic oxidation catalyst has been synthesized via wet impregnation of copper and iron over a mesoporous SBA-15 silica support. Physicochemical properties of the resulting material were characterized by XRD, N2 physisorption, DRUVS, FTIR, Raman, SEM and HRTEM, revealing the structural integrity of the parent SBA-15, and presence of highly dispersed Cu and Fe species present as CuO and Fe2O3. The CuFe/SBA-15 bimetallic catalyst was subsequently utilized for the oxidative degradation of N,N-diethyl-p-phenyl diamine (DPD) employing a H2O2 oxidant in aqueous solution.

Silica-clad neodymium-doped lanthanum phosphate fibers and fiber lasers

We have fabricated a neodymium-doped phosphate glass fiber with a silica cladding and used it to form a fiber laser. Phosphate and silicate glasses have considerably different glass transition temperatures and softening points making it hard to draw a fiber from these two glasses. A bulk phosphate glass of composition (Nd2O3)(0.011)(La2O3)(0.259)(P2O5)(0.725)(Al2O3)(0.005) was prepared and the resultant material was transparent, free from bubbles and visibly homogeneous. The bulk phosphate glass was drawn to a fiber while being jacketed with silica and the resultant structure was of good optical quality, free from air bubbles and major defects. The attenuation at a wavelength of 1.06 mu m was 0.05 dB/cm and the refractive index of the core and cladding at the pump wavelength of 488 nm was 1.56 and 1.46, respectively. The fibers were mechanically strong enough to allow for ease of handling and could be spliced to conventional silica fiber. The fibers were used to demonstrate lasing at the F-4(3/2) - I-4(11/2) (1.06 mu m) transition. Our work demonstrates the potential to form silica clad optical fibers with phosphate cores doped with very high levels of rare-earth ions (27-mol % rare-earth oxide).

An XPS study of the effect of ion bombardment on transition metal oxides

Thesis was water damaged in store, retrieved for use but may still show signs of damage. Unable to scan to make available online.