Heat transfer from molten materials to liquids

An apparatus was designed and constructed which enabled material to be melted and heated to a maximum temperature of 1000C and then flooded with a pre-heated liquid. A series of experiments to investigate the thermal interaction between molten metals (aluminium, lead and tin) and sub-cooled water were conducted. The cooling rates of the molten materials under conditions of flooding were measured with a high speed-thermocouple and recorded with a transient recorder. A simplified model for calculating heat fluxes and metal surface temperatures was developed and used. Experimental results yielded boiling heat transfer in the transition film and stable film regions of the classic boiling curve. Maximum and minimum heat fluxes were observed at nucleate boiling crisis and the Leidenfrost point respectively. Results indicate that heat transfer from molten metals to sub-cooled water is a function of temperature and coolant depth and not a direct function of the physical properties of the metals. Heat transfer in the unstable transition film boiling region suggests that boiling dynamics in this region where a stationary molten metal is under pool boiling conditions at atmospheric pressure would not initiate a fuel-coolant interaction. Low heat fluxes around the Leidenfrost point would provide efficient fuel-coolant decoupling by a stable vapour blanket to enable coarse mixing of the fuel and coolant to occur without appreciable loss of thermal energy from the fuel. The research was conducted by Gareph Boxley and was submitted for the degree of PhD at the University of Aston in Birmingham in 1980.

Fatigue crack growth behaviour in molten-metal processed SiC particle-reinforced aluminium alloys

Fatigue crack initiation and subsequent short crack growth behaviour of 2014-5wt%SiC aluminium alloy composites has been examined in 4-point bend loading using smooth bar specimens. The growth rates of long fatigue cracks have also been measured at different stress ratios using pre-cracked specimens. The distributions of SiC particles and of coarse constituent particles in the matrix (which arise as a result of the molten-metal processing and relatively slow cooling rate) have been investigated. Preferential crack initiation sites were found to be SiC-matrix interfaces, SiC particles associated with constituent particles and the coarse constituent particles themselves. For microstructurally short cracks the dispersed SiC particles also act as temporary crack arresters. In the long crack growth tests, higher fatigue crack growth rates were obtained than for monolithic alloys. This effect is attributed to the contribution of void formation, due to the decohesion of SiC particles, to the fatigue crack growth process in the composite. Above crack depths of about 200 μm 'short' crack growth rates were in good agreement with the long crack data, showing a Pris exponent, m = 4 in both cases. For the long crack and short crack growth tests little effect of specimen orientation and grain size was observed on fatigue crack growth rates, but, specimen orientation affected the toughness. No effect of stress ratio in the range R = 0.2-0.5 was seen for long crack data in the Paris region.