Vitamin E-stabilised UHMWPE for orthopaedic implants:quantitative determination of vitamin E and characterisation of its transformation products

The fate of vitamin E and the formation and identification of its transformation products were investigated at different stages of the manufacturing process of commercially produced cross-linked (by γ-irradiation) UHMWPE stabilised with vitamin E (vitamin E infused-post irradiation) used for tibia-components (as articulating surfaces) in total knee arthroplasty (total knee replacement). Vitamin E (α-tocopherol) and its transformation products were extracted from microtomed Tibia films and the different products were separated, isolated, purified using high performance liquid chromatography (HPLC), and characterised by spectroscopic methods and LC-MS. The amount of vitamin E and that of the products formed in the different Tibia samples and in their extracts were also quantified using FTIR and HPLC analysis and calibration curves. Thorough analysis of the Tibia extracts has shown that a number of vitamin E transformation products were formed at different concentrations at two selected stages of the implant manufacturing process that is before and after sterilisation by γ-irradiation. The identified products were found to correspond mainly to different stereoisomeric forms of a small number of vitamin E transformation products. Most of the observed products were of dimeric and trimeric nature with their identity confirmed through a detailed study of their spectral and chromatographic characteristics. It was found that the products of vitamin E, prior to the sterilisation step but after the crosslinking and doping of vitamin E, were mainly the dihydroxydimers and trimers (Tibia samples at this stage are referred to as “Tibia-VEPE”). After sterilisation and completion of the manufacturing process, additional dimers of vitamin E were also formed (Tibia samples at this stage are referred to as ‘Tibia-VEPE-Sterile’), Furthermore, two tocopherol-derived aldehydes (aldehyde 5-formyl-γ-tocopherol and aldehyde 7-formyl-γ-tocopherol) were also formed but at very low concentrations especially in the Tibia-VEPE-Sterile samples. The question of whether vitamin E becomes chemically reacted (grafted) onto the polymer matrix during the manufacturing process of the Tibia is also addressed.

Decomposition of the B2-type matrix

The microstructural stability of aluminide diffusion coatings, prepared by means of a two-stage pack-aluminization treatment on single-crystal nickel-base superalloy substrates, is considered in this article. Edge-on specimens of coated superalloy are studied using transmission electron microscopy (TEM). The effects of coating thickness and post-coating heat treatment (duration, temperature, and atmosphere) on coating microstructure are examined. The article discusses the partial transformation of the matrix of the coating, from a B2-type phase (nominally NiAl) to a L12 phase (nominally Ni3(Al, Ti)), during exposure at temperatures of 850 °C and 950 °C in air and in vacuum for up to 138 hours. Three possible processes that can account for decom- position of the coating matrix are investigated, namely, interdiffusion between the coating and the substrate, oxidation of the coating surface, and aging of the coating. Of these processes, aging of the coating is shown to be the predominant factor in the coating transformation under the conditions considered. © 1992 The Minerals, Metals and Materials Society, and ASM International.